  Preparation of carbon dot/polyaniline composites as voltage based dielectric material for capacitor applications

  Coğalmış, Fatma Tuba; Demirelli, Kadir; Barım, Esra; Ük, Nida; Ünlü, Caner; Şenkal, Bahire Filiz; Dere, Ayşegül; Tuncer, Hülya; Yakuphanoğlu, Fahrettin

  Polyaniline-carbon dot (CD/PANI) composites were prepared via in-situ oxidative polymerization of aniline in the presence of carbon dots, with specific concentrations carefully controlled during synthesis. The composite was characterized using spectroscopic (FT-IR), morphological (TEM, SEM) and electrical methods. Impedance analysis was employed to investigate the transport behavior of charge carriers in the frequency range of 500 Hz to 10 MHz at 25 °C. This study provides a comprehensive analysis of the dielectric properties of the CD/PANI composite, including dielectric constant, dielectric loss, loss factor, AC conductivity, admittance, impedance, and Cole–Cole plots. The dielectric constant of the CD/PANI composite was 6.97 for 1 kHz at 0.5 V and 12.87 for 1 kHz at 5 V. The values indicate that the increase in the dielectric constant of nanocomposite with increasing voltage. This suggests that CD/PANI composite is a dielectric material whose dielectric constants are controlled by applied voltage. Notably, the dielectric constant increased with rising applied voltage and decreased with increasing frequency. Current-voltage (I-V) measurements revealed that the composite's dielectric parameters could be tuned by varying the applied DC voltage, suggesting its potential as a voltage-dependent dielectric (VDD) material for capacitor applications. Furthermore, the enhanced electrical conductivity indicates that the CD/PANI composite is a promising candidate for next-generation dielectric devices.

  AtıfScopus7·OpenAlex7

  İncele
• MakaleYalnız künye2020Scopus SJRQ1/r/munzur/3497
  A thermodynamic and kinetic approach to adsorption of methyl orange from aqueous solution using a low cost activated carbon prepared from Vitis vinifera L.

  Yönten, Vahap; Sanyürek, Nesrin Karaca; Kivanç, Mehmet Rıza

  In this paper, thermodynamic and kinetic parameters of the Methyl Orange adsorption process on active carbon prepared from endemic Vitis vinifera L. grape seeds (AC-VVL) grown in the Tunceli-Elazığ region and % removal of dye from aqueous solutions were evaluated by using a batch system. Experiments were performed as a function of pH (2, 5, 8 and 11), temperature (15 °C, 30 °C and 45 °C) and initial concentration (100, 150, 300 and 1000 mg L−1). The mechanism and characterization of adsorption of dye was analyzed pre-adsorption (AC-VVL) and post-adsorption (AC-VVL+dye) using FTIR (Fourier Transform Infrared Spectroscopy), SEM (Scanning Electron Microscope) and Brauner Emmet and Teller (BET) analyzer. The activation energy (Ea) was determined as 24.80, 39.15, −22.40 and 61.73 kJ/mol for 100, 150, 300 and 1000 mg L−1, respectively. The Langmuir, Freundlich, Temkin and Harkins Jura isotherms were used to describe the adsorption equilibrium studies at different temperatures. The Freundlich isotherm shows better fit than other isotherms in the temperature range studied. Maximum adsorption occurred at pH 2 and was approximately 79.7 mg/g. The % Recycling Yield was found to be 20% and 9 mg/g with acetone. Thermodynamic parameters like the change in enthalpy (ΔH o), entropy (ΔS o) and Gibbs free energy (ΔG o) were evaluated and the adsorption process was found to be endothermic and spontaneous. The results show that this AC-VVL biomass is an appropriate biosorbent and has specific affinity for removal of Methyl Orange from aqueous solutions.

  • 
  • 