  Optimizing the thermoelectric performance of Bi-Sb-Te thin films through compositional engineering

  Yüzüak, Gizem Durak; Çetin, Mehmet; Yüzüak, Ercüment

  The objective of the present investigation was to systematically investigate the structural and thermoelectric (TE) properties of BixSb2-xTe3 thin films with varying content of Bi. We investigated the impact of different atomic percentages of Bi (4, 6, 8 at. %) on the properties of carrier transport and TE performance. In general, the Seebeck coefficient remained consistent across the thin films. For the 8 at. % Bi thin film, the Seebeck coefficient and electrical conductivity were measured at 230 μV/K and 730 S/cm, respectively, at room temperature. These values were more than 20 times greater than the electrical conductivity observed in the thin films with compositions of 6 and 4 at. % Bi. As a result, the Bi-Sb-Te compound exhibited a TE power factor (PF) of 38x10−4 W/mK2 at 40 °C, surpassing the PFs observed in previous compositions. The analysis of surface microstructure, combined with atomic force microscopy and Kelvin probe microscopy images, revealed that the transport of carriers in films with high Bi content was impeded by the size of particles and scattering sites. On the other hand, an augmentation in Bi content promoted the transfer of charge through crystalline regions, hence improving the mobility of carriers and the total electrical conductivity. The aforementioned results emphasize the significant influence of Bi content on the electrical properties of semiconductors and demonstrate the effectiveness of compositional engineering based on Bi content in the development of TE materials with superior performance. The present study investigates the influence of Bi content on the electrical properties of Bi-Sb-Te thin films, demonstrating that compositional adjustments based on Bi content can impact the performance of TE materials. These findings contribute to the understanding of material optimization in the field of TE.

  • 
  AtıfScopus4·WoS5·OpenAlex5

  İncele
• MakaleAçık Erişim2024Scopus SJRQ2/r/munzur/1755
  Photodetector performance analysis of a hybrid MnPc/DLC device with high photoresponsivity, sensitivity, and On/Off ratio

  Unal, Fatih; Aktas, Sitki; Kurt, Mustafa Sukru; Koc, Mumin Mehmet; Coskun, Burhan; Aslan, Naim; Arslan, Tayfun; Gur, Mahmut

  The fabrication and characterization of high-performance devices for optoelectronic applications, particularly their response to incident light, are crucial. In this study, a MnPc/DLC device was fabricated using thermal evaporation and magnetron sputtering techniques, and its fundamental optoelectronic properties were characterised. Key diode parameters including barrier height, ideality factor, reverse saturation current, series resistance, and shunt resistance were determined using several methods, such as TE, Ohm's Law, the modified Norde method, and the Mikhelashvili method. The results from these methods were found to be consistent with varying light intensities. Additionally, photodetector parameters of the MnPc/DLC device were measured at ±1 V under light intensities of 20, 40, 60, 80, and 100 mW/cm2, and the findings were compared with the literature. The maximum values for photocurrent, photoresponsivity, photosensitivity, specific detectivity, and on/off ratio were 6.41 × 10−2 A, 2.49 A/W, 2.02 × 105, 5.8 × 109 Jones and 2.06 × 103, respectively. Notably, the photocurrent, photoresponsivity, photosensitivity, and on/off ratio values were found to be significantly higher and more promising compared to those reported in the literature.