Doğan, Fatih

The coatings were prepared by blending different concentrations of SWCNTs and CeO2 particles with an epoxy resin by hydrothermal method, which was then applied to the substrate through the doctor blade technique. The mixtures were transferred into a 1-L capacity autoclave with a teflon-lined flange type and subjected to hydrothermal treatment at 100°C for 3 h. The surface coatings were applied using a doctor blade. Subsequently, the coated materials were placed in an oven and dried for 12 h at 50°C under vacuum conditions. The samples' structural analysis was examined through x-ray diffraction (XRD). XRD analysis verified the CeO2/SWCNT composite coating, and Fourier transform infrared spectroscopy (FTIR) was utilized to assess the presence of functional groups. Thermodynamic properties and thermal stability of composite coatings that were modified with SWCNTs and CeO2 particles were studied by thermogravimetric analysis (TGA). The impact of the CeO2/SWCNT composite on the anticorrosion capabilities of the epoxy coating was examined through electrochemical impedance spectroscopy (EIS), Nyquist curve, and Tafel slope characterization. Corrosion tests were conducted on the CeO2/SWCNT composite coatings in a 3.5 wt% sodium chloride (NaCl) solution at 25°C to improve corrosion resistance. The concentration of 0.4 wt% CeO2 was found to be optimal for achieving effective corrosion resistance. The composite coating CNT0.6-C0.4 exhibited significantly higher Ecorr (−426 V) and lower Icorr (2.96 × 10−6 A cm−2) values compared to samples from the CNT0, CNT0.2, and CNT0.6 groups. The paper presents a viable solution with CeO2/SWCNT composite coating for the engineering application of corrosive-inhibiting coatings.

AtıfScopus1·WoS1

İncele

Pekdemir, Mustafa Ersin; Kök, Mediha; Kanca, Muhammed Sait; Özen Öner, Ecem; Pekdemir, Sibel; Inci, Şule; Kirbağ, Sevda; Tatar, Beyhan

Recently, there has been a great demand for boron-containing compounds (BCCs) with unique biological properties. The demand for the use of these compounds not alone but as additives in composite materials is increasing day by day. In this study, the effect of adding B2O3 compound to the blend of PLA and PEG polymers, which is an important biocompatible shape memory polymer, was investigated. In order to examine the effect of increasing B2O3 additive on the thermal properties of PLA-PEG blend, it was determined by using a Differential Scanning Calorimetry (DSC) and thermogravimetric analyzer (TGA), and it was seen that while the melting temperature of PEG decreased, the melting temperature of PLA increased. In addition, when the thermal stability of the composites was examined, increasing of thermal stability was observed with the addition of B2O3 and a three-step degradation occurred. It was determined that the B2O3/PLA-PEG composite was homogeneous by taking X-ray measurements and SEM measurements. The antimicrobial property of the PLA-PEG blend improved with the increasing B2O3 contribution were observed from the antimicrobial activity measurements of the composite against 4 different bacteria. However, it was determined that the PLA-PEG blend preserved its shape memory effect with increasing diboron trioxide contribution.

AtıfScopus13·OpenAlex16

İncele