Demirelli, Kadir; Dere, Ayşegül; Barım, Esra; Tuncer, Hülya; Yakuphanoğlu, Fahrettin

MXene based ternary composite photonic device was fabricated and characterized for the detection of different illuminations. The single chain polymer-cobalt phthallocyanine (SCP-CoPc) carrying metallised pthalocyanine macro ring was used as a polymer for the preparation of ternary composite. The Fourier Transform Infrared Spectroscopy (FT-IR), Transmission Electron Microscopy (TEM), Scanning electron microscopy with energy dispersive X-ray spectroscopy (SEM/EDX) were used to differentiate MXene/ZnO/SCP-CoPc composite prepared. The presence of Ti, C, O, Zn and Co elements in the structure of the composite was confirmed by EDX. The electrical properties of planar interdigital coated MXene/ZnO/SCP-CoPc (1:1:1 by wt) were investigated for photovoltaic application. The photo-generated carriers contribute to the current flow, and the linear photoconductivity behaviour in current measurements with different illuminations such as 20, 40, 60, 80 and 100 mW/cm2 indicates the possible photo device use of MXene/ZnO/SCP-CoPc nanocomposite. The photocurrent increased from 20 mA/cm2 to 100 mA/cm2 with the light intensity at 0.5 V was tuned from 28 to 280 μA. The forbidden energy gap (Eg) value of the MXene/ZnO/SCP-CoPc ternary composite from optical measurements was found to be 2.36 eV. Experimental results showed that the presence of SCP-CoPc and ZnO (zinc oxide) in the ternary nanocomposite increased the ε' and ε" values of MXene. The ε′ and ε″ of the ternary composite is 13.0, 26217 at 1 kHz and room temperature, respectively. The current-time results suggest that MXene based ternary composite photonic device is a self driven photodevice as the device can detect light without any external voltage bias.

AtıfScopus6·OpenAlex6

İncele

Aydin, Handan; Gündüz, Bayram; Aydin, Cihat

In this work, we synthesized the graphene oxide by Hummers method and prepared poly-N-vinylcarbazole (PVK)/graphene oxide (GO) nanocomposites. We investigated the SEM images, FTIR and UV spectroscopy and ac conductivity properties of PVK:wt% (0, 1, 5, 10, 15%) GO nanocomposites thin films. The PVK and PVK/GO nanocomposites are dominant in near ultraviolet region. The absorption band edge of the films of the PVK/GO nanocomposites varies from 3.077 to 3.175 eV, while the allowed optical band gap of the 0, 1, 5, 10 and 15% wt. GO + PVK nanocomposites varies from 2.97 to 3.30 eV. The optical band gap and refractive indices of the PVK can be changed with increasing the percentage by weight of graphene oxide. The single oscillator energy varies from 3.358 to 3.670 eV, while the dispersion energy varies from 6.404 to 6.970 eV. The graphene oxide has an important effect on the ac conductivity of the PVK. Obtained results show that the PVK material modified with graphene oxide is promising for electronic, optical and optoelectronic technology.

AtıfScopus20·WoS20·OpenAlex22

İncele