  Characterization of the mechanical and thermal properties of rape short natural-fiber reinforced thermoplastic composites

  Kısmet, Yılmaz; Dogan, Akar

  In this study, the effects of filler amounts were studied on the mechanical and thermal properties of high-density polyethylene (HDPE), polystyrene (PS) and polyoxymethylene (POM) polymers reinforced with short rape fibers. HDPE-rape, POM-rape and PS-rape fiber composite materials were prepared with different fiber contents and their tensile, flexural, Izod impact and TGA/DTA properties were examined. When tensile and Izod impact properties were compared, it was observed that an increase in the amount of filling in HDPE-based composites did not cause any significant changes in these peoperties, while they were decreased for POM- and PS-based composites. On the contrary to tensile and impact strengths, when the three-point flexural properties were examined, it was observed that the strength values of all these materials increased with increasing the amount of fillers. However, a pronounced increase was observed in the three-point flexural strength of the HDPE-based composite materials. The flexural strength of 30 wt% rape-reinforced HDPE composite was found to be twice that of the pure HDPE. The results of TGA and DTA analyses revealed that the reinforcement element started to burn before the matrix material and therefore burning was delayed in these thermoplastics. As a result, the mechanical properties of HDPE composite materials improved with rape reinforcement. In this way, by using approximately 30 wt% natural filling material in a polymeric matrix, an environmentally friendly material, as well as, significant advantages in cost can be obtained. Graphic abstract: [Figure not available: see fulltext.].

  • 
  AtıfScopus25·WoS25·OpenAlex33

  İncele
• MakaleYalnız künye2019Scopus SJRQ2/r/munzur/3488
  The effect of hygrothermal aging and UV radiation on the low-velocity impact behavior of the glass fiber-reinforced epoxy composites

  Dogan, Akar; Arman, Yusuf

  The present work examines the effects of hygrothermal and UV radiation aging on the reinforced epoxy composites. The role of temperature in the hygrothermal aging process on tensile properties, impact behavior of composites and compression-after impact was investigated. Among four different chosen aging conditions, three of them were hygrothermal and last one was composed of both hygrothermal and UV radiation. Unidirectional e-glass fiber fabrics with an areal density 300 g/m2 as reinforcement and epoxy matrix were used. Composites were manufactured using vacuum-assisted resin infusion molding. The goal of this study was to investigate the effect of UV radiation and aging temperature with respect to the glass transition temperature. In this context, aging procedures were carried out in two different ways for 70 °C temperature with and without UV radiation. As a result of the test, the tensile strength, tensile modulus, absorbed energy, interlaminar shear strength (ILSS), and compression-after impact (CAI) strength of the glass reinforced composites decreased for all conditions. Despite being under the same ambient temperature and humidity, the samples which were exposed to UV radiation had lower mechanical properties. The reduction of tensile strength of specimens exposed to 70 °C and 70% humidity with and without UV radiation were 24% and 10%, respectively. The temperature of hygrothermal conditions significantly affected the perforation threshold. In low impact energies, delamination was the primary damage mode, while fiber breakage becomes more important in the composite at high impact energy levels.