  Effect of mechanical activation on lithium and alkali cation release from dolomitic clay wastes of boron processing plant

  Boylu, Feridun; Teker, Gülsen Obuz; Angur, Gafure Ersever; Ozdemir, Orhan; Çelik, Mehmet Sabri

  With the significant increase in lithium demand and production, alternative resources such as lithium-bearing clays have increasingly attracted attention and have been considered as a potential source. In addition to conventional Li recovery methods such as acid treatment and roasting, more economical and environmentally friendly techniques such as mechanical activation followed by water leaching are also being considered. In Türkiye, wastes from boron processing plants, containing approximately 900 ppm of lithium and mainly of dolomitic clays and unrecovered boron minerals (~10-13% of waste), are considered as a potential lithium source. However, due to high dolomite and boron mineral contents, the waste material may release significant amounts of alkaline earth ions such as Na+, K+, Mg2+, Ca2+, and B2O3 during leaching, which may interfere with lithium extraction from the solution. In this study, the leaching behavior of lithium, alkali ions, and other possible elements (e.g., B2O3, Fe3+, and Al3+) from both raw clay waste and mechanically activated forms of this waste material was investigated in detail. The results showed that water leaching without sodium salt of activated waste samples achieves about 44.7–57.7% lithium recovery, yielding high lithium concentrations (80–115 ppm), low levels of alkali ions (4430 ppm Na+, 114 ppm K+, 20 ppm Ca2+, and 7 ppm Mg2+), and almost no detectable Fe3+ (<0.2 ppm) or Al3+ (0.07 ppm) ions. On the other hand, a single problem was encountered where 0.95 % of B2O3 concentrations did not decrease in water leaching at even room temperature.

  • 
  • 
  İncele
• MakaleYalnız künye2025Scopus SJRQ2/r/munzur/771
  Removal of Impurities from Sepiolite by Gravity/Sizing Methods for Better Viscosity Development

  Angur, G. Ersever; Çınar, M.; Çelik, M.S.

  Sepiolite, a natural strategic clay mineral within the phyllosilicate group, is utilized in numerous applications because of its physical, and rheological properties. In particular, outstanding rheological properties are utilized in areas including drilling mud, paint, cosmetics, adhesives, etc. Several studies have been performed for the purification of clays, such as air classification, calcination, hydrocyclone, and flotation, for different purposes. In this study, relatively easy physical upgrading methods involving hydroxyclone, Falcon, and shaking table have been tested with the aim of obtaining a high-viscosity sepiolite product for rheological applications. It is shown that dispersion time, particle size, and pH are the most critical parameters in the viscosity development of sepiolite. The results indicate that, depending on the dispersion time of the raw HS1 sepiolite sample used in this study, the highest quality rheological material remains in the size range of – 2 mm to + 1 mm. Below – 0.1 mm, the viscosity value of the sepiolite sample decreased to its lowest value of 6000 cP. The pH-dependent viscosity measurements of a raw HS1 sepiolite sample exhibited the highest viscosity value of 13,000 cP at its natural pH of 8.5. Polyacrylic acid sodium salt (PAA) is the most effective dispersing agent in the decantation process for the enrichment of HS1 sepiolite samples. Among the three gravity/sizing beneficiation techniques tested, the middlings product of the shaking table achieved the highest quality sepiolite product of 17,000 cP with 49.2 wt.% using the size range of – 2.83 mm to + 1 mm; this material is suitable for high-grade rheological applications.