  Solvent extraction of rare earth elements and α-alumina production from pregnant leaching solution obtained from Turkish bauxite-related ore

  Erust, Ceren; Uysal, Turan

  The use of bauxite-related shales as a secondary source for the extraction of rare earth elements (REEs) is very important to meet the raw material supply, which is the keystone of advanced technology applications. This study presents the investigation into the recovery of REEs from Kızıldağ shale ore and the potential utilization of its leach residue as a silica source. Mineralogical analysis revealed that the ore predominantly consists of paragonite, muscovite, quartz, pyrophyllite, and calcite. Calcined ore was subjected to acid leaching, and the resulting pregnant solution was purified using solvent extraction to separate from aluminum the ∑REEs with a content of 1887.35 ppm. Optimal solvent extraction conditions 1.5 M D2EHPA, 50% O/A ratio, pH 1.5, and 15-minute mixing time achieved 95% total REE extraction, with efficiency in the order Pr > La > Nd > Ce > Dy > Y > Sc. To purify Al from the Fe- and K-rich solution post-SX, electrolysis was performed, resulting in 97.16% precipitation efficiency of Al as Al(OH)3 at pH 5. The precipitate was subsequently roasted at 1100°C to produce α-alumina with 75.2% Al2O3 content. These findings confirm the technical feasibility of recovering REEs and producing coarse-purity alumina from Kızıldağ shale ore.

  • 
  AtıfScopus1·WoS3·OpenAlex1

  İncele
• MakaleYalnız künye2019Scopus SJRQ2/r/munzur/3708
  Investigation of selective leaching and kinetics of copper from malachite ore in aqueous perchloric acid solutions

  Tanaydın, Mehmet Kayra; Demirkıran, Nizamettin

  In this study, the leaching kinetics of malachite in perchloric acid solutions was investigated. The dissolution behaviors of copper, zinc, and iron in the ore matrix were determined at different acid concentrations and reaction temperatures. It was observed that the concentration of perchloric acid had a major effect on the dissolution of copper, zinc, and iron. It was determined that the effect of temperature on the dissolution of these species was not as significant as concentration impact. The results obtained shown that copper in the ore matrix was completely leached while zinc and iron were partially dissolved in perchloric acid solutions. In addition, the effects of the acid concentration, reaction temperature, stirring speed, particle size, and solid-to-liquid ratio on the leaching of malachite were researched. In these experiments, it was observed that the leaching rate of copper increased with increasing solution concentration, stirring speed, and reaction temperature, and with decreasing solid-to-liquid ratio and particle size. A kinetic analysis was performed, and it was found that the rate of leaching reaction obeyed the mixed kinetic control model in the unsteady state. The activation energy of the leaching process was calculated to be 34.69 kJ/mol.

  • 