Durmus, Hasan; Kilic, G.; Ilik, E.; Kavaz, E.; Güler, Ömer; Birdogan, Selcuk; ALMisned, Ghada; Tekin, H.O.

This study investigates the structural, physical, and radiation-shielding properties of nano-Gd2O3-reinforced lithium borotellurite glasses with the composition 50TeO2-30B2O3-(20-x)Li2O-xGd2O3 (x= 0-10 mol %). X-ray diffraction and transmission electron microscopy confirmed the fully amorphous nature of the glasses and the homogeneous distribution of nanoscale Gd clusters. Density increased from 4.03 to 4.77 g/cm3, accompanied by compositional shifts, decreasing boron and increasing oxygen and tellurium contents, indicating enhanced structural compactness and electron density. Gamma-ray attenuation measurements revealed a 74 % increase in the linear attenuation coefficient from 8.33 to 14.53 cm−1 at 81 keV and a nearly 27 % reduction in the half-value layer from 1.21 to 0.89 cm. Effective atomic number values remained highest for Gd(n)10 across the photon energy range investigated. Experimental neutron dose measurements showed absorption improvements from 37.66 % to 51.91 %, while the effective removal cross-section increased from 0.1066 to 0.1096 cm−1, outperforming water, B4C, and graphite. Compared with the Gd-doped zinc borotellurite glasses reported in the literature, the present lithium-based system exhibited higher densification and superior dual γ-neutron attenuation. These results demonstrate that controlled nano-Gd2O3 integration into the lithium borotellurite matrix yields a stable, lead-free amorphous material with outstanding radiation-shielding efficiency for advanced photonic and nuclear applications.

AtıfScopus3·OpenAlex3

İncele

Kilic, G.; Durmus, Hasan; Birdogan, Selçuk; Ilik, E.; Perişanoğlu, Esra Kavaz; Saltık, Sevda; Guler, Ömer; ALMisned, Ghada; Tekin, H.O.

In this study, a novel series of nano-Sm2O3-doped lithium borotellurite glasses was synthesized and systematically investigated in terms of their structural, physical, and radiation shielding characteristics. X-ray diffraction confirmed the amorphous nature of all samples, while transmission electron microscopy revealed progressive nanoarchitectural refinement and particle growth with increasing Sm2O3 content, from uniformly dispersed nanodomains to dense agglomerates exhibiting short-range crystalline ordering. Energy-dispersive X-ray spectroscopy and elemental mapping validated the homogeneous incorporation of boron, oxygen, tellurium, and samarium throughout the glass matrix without phase separation. Gamma-ray shielding evaluations showed enhanced mass attenuation coefficients and reduced half-value layers, particularly in the Sm(n)8 sample, with significant performance gains at lower photon energies. Neutron shielding assessments further indicated elevated macroscopic removal cross-section values and dose attenuation, affirming the compositional benefit of Sm2O3 for fast neutron mitigation. It can be concluded that nano-Sm2O3 incorporation would play a multifunctional role on structural and radioprotective properties in addition to morphostructural features of lithium borotellurite glasses.

AtıfScopus5·OpenAlex6

İncele

Kilic, G.; Güler, Ömer; Kavaz, E.; Ilik, E.; Guler, Seval Hale; ALMisned, Ghada; Tekin, H.O.

While numerous oxide additives have traditionally been employed to enhance the radiation shielding capabilities of glasses, the unique attributes of high-entropy oxides (HEOs), a group of materials acclaimed in contemporary material science for their distinctive properties have remained unexamined in this specific area. This novel study explores the enhancement of radiation shielding properties in zinc-tellurite glasses through the integration of TiNbWMoZrOx High Entropy Oxides (HEO). Utilizing advanced synthesis techniques, including mechanical alloying and oxidation, the research successfully incorporates HEOs into glass matrices, aiming to improve gamma-ray and neutron attenuation. Characterization through X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) confirms the uniform distribution and structural integrity of the HEOs within the glasses. The synthesis of glass samples with a base structure suitable for the molar composition of 25ZnO.75TeO2 (mol%) and glass samples doped with TiNbWMoZrOx (HEO) was carried out using the traditional high-temperature melting and annealing method. The outcomes demonstrate a concentration-dependent increase in shielding efficacy, particularly highlighting the superior performance of glasses doped with 4 mol% of TiNbWMoZrOx (HEC2–4), which exhibit significantly enhanced mass attenuation coefficients, lower half-value layers, and higher effective atomic numbers. This indicates the effective role of HEOs in boosting radiation protection capabilities. Comparative analysis with traditional shielding materials showcases the HEC2–4 glasses' competitive advantage, underlining their potential as a versatile shielding solution. It can be concluded that incorporating TiNbWMoZrOx high entropy oxides into zinc-tellurite glasses significantly augments their radiation shielding properties, offering a novel approach for enhancing protection against gamma-ray and neutron in various applications.

AtıfScopus6·OpenAlex5

İncele

Divina, R.; Sathiyapriya, G.; Marimuthu, K.; Askin, A.; Sayyed, M.I.

The effect of modifier ions in different basis have been analyzed through a new series of heavy metals incorporated borate based glasses 39H3BO3+30PbO+20MO+10Bi2O3 +1Dy2O3 (where M=Ca,Sr,Ba,Na and K) which are synthesized following melt quenching technique for radiation screening applications. The potentiality of glasses to withstand the penetration of fast moving neutrons is checked by various studies. Functional groups are identified through different stretching and bending modes of vibrations within the glass membrane through FTIR spectral analysis. In addition to that, other structural properties like Boron-Boron distance (dB−B), molar volume of oxygen (Vo), Oxygen Packing Density (OPD), optical basicity (Λth) and Bond density (nb) are calculated theoretically. The bonding nature (β) and nephelauxetic ratio (δ) values reveals that the glasses possess more of ionic linkages. The high density value exhibited by the Bismuth lead borate glasses indicates their capability to act as a good shielding material in reactors emitting hazardous radiation. Different moduli of elasticity (E, K, G, σ) values for the present glasses are calculated and the results reveal the enhancement in shielding performances when compared to other existing glasses and a comparative study is made on it. Optical studies are carried out and the absorption of Dy3+ions to different energy levels is observed and optical band gap (Eopt) values of the synthesized glasses are calculated along with the Urbach energy (ΔE) values. Radiation shielding properties of the produced glasses were investigated in terms of the mass attenuation coefficients (µm), transmission fraction (T), half value layer (HVL) and effective atomic number (Zeff) parameters. The results attained in the shielding study indicated that glass specimen with M = Ba exhibits enhanced shielding behavior as Ba owns high atomic number (Z) compared to other elements. Glass specimen with M = Na shows the poorest shielding characteristics due to the low Z of Na.

AtıfScopus117·OpenAlex107

İncele

Boonin, K.; Yasaka, P.; Limkitjaroenporn, P.; Rajaramakrishna, R.; Askin, A.; Sayyed, M.I.; Kothan, S.; Kaewkhao, J.

In this study, the zinc barium tellurite glasses (ZBaT) synthesized and inspected their radiation defensive mechanism and structural behavior. Glass composition (90-x) TeO2 - 10 ZnO - xBaO, where 25≤ x ≤ 35 (mol%) was prepared using the melt quenching technique and glass-forming pseudo-ternary diagram was discussed. Addition of BaO enhances the polarization in the present glasses there by it increases the bond length hence glass network expands resulting in volume. The mass attenuation coefficient (μm) of ZBaT glasses have been evaluated at various energies via Compton scattering technique. The results found that the μm, effective atomic number and effective electron density decrease with the increase in γ-ray energies which is in a good agreement with theoretical values attained using Geant4 and WinXCOM. At 25 mol% BaO content the glass samples show less mean free path (MFP) which were compared with other standard shield defensive materials. The obtained results reveal that the formation of non-bridging oxygens increased with higher concentration of BaO. The transmission spectra of the prepared glasses displayed optical light transparency thereby demonstrating their efficient role being transparent window when used as radiation defensive material without Pb component proving them as eco-friendly for environment.

AtıfScopus80·OpenAlex83

İncele

Aşkın, A.; Sayyed, M.I.; Sharma, Amandeep; Dal, M.; El-Mallawany, R.; Kaçal, M.R.

In the present work, the radiation shielding proeprties of lithium borophosphtellurite glass system with the composition of (100-x) [0.5Li2O-0.1B2O3–0.4P2O5]-xTeO2 (x = 0, 10, 20, 30 and 40 mol%) were reported. The mass attenuation coefficient (μ/ρ) of the selected glass system (LiBPTe0, LiBPTe10, LiBPTe20, LiBPTe30 and LiBPTe40) was calculated at 356 keV, 662 keV, 1173 keV and 1330 keV photon energies by using Geant4 and FLUKA codes and the results were compared to the values obtained theoretically using WinXcom software. The correlation theory has been used to calculate the correlation coefficients (R2) between the results from WinXcom and the both simulations codes (Geant4 and FLUKA) for each sample. Moreover, some other radiation shielding parameters such as effective atomic number, photon transmission, mean free path and half value layer were calculated. The gamma photon transmission results showed that the transmission values of the 356 keV photons are lower than those of energies 662, 1173 and 1330 keV. At 356 keV, the transmission value for LiBPTe0 (at 6 cm thickness) is found to be 0.245 while at the same energy and thickness the transmission value is 0.088 for LiBPTe40. Out of all the glasses considered in present work, LiBPTe40 possesses the highest values of effective atomic number (Zeff). The Zeff values for the present glasses are 8.02, 9.55, 11.16, 12.85 and 14.64 for LiBPTe0, LiBPTe10, LiBPTe20, LiBPTe30 and LiBPTe40 respectively at 356 keV. The mass attenuation coefficient and effetive atomic number results showed that utilization 40% mol of TeO2 significantly improves the gamma ray shielding properties of the selected glass system. The shielding effectiveness of the selected samples was compared with other reference materials namely two radiation shielding glasses and four concretes used in different shielding purposes in terms of the mean free path (MFP) at 356 keV. The results revealed that the MFP of RS-253-G18 is lower than LiBPTe0sample. Moreover, the MFP of ordinary concrete is higher than the MFP of all glasses under examination, thus the investigated tellurite glasses have better attenuation features than the ordinary concrete.

AtıfScopus106·OpenAlex107

İncele

Sathiyapriya, G.; Marimuthu, K.; Sayyed, M.I.; Askin, A.; Agar, O.

Structural, physical and gamma ray shielding properties of Dy3+ doped telluroborate glasses have been discussed. The molar volume of the glasses is proportional to the TeO2 content. The FTIR studies investigate the expansion of TeO2 content and the dynamic change of tetrahedral [BO4] units into trigonal [BO3] units. Using the absorption spectra, optical band gap (Eg) and Urbach's energy (ΔE) values are calculated. The molar volume of oxygen (VO) and boron‑boron separation (<dB–B>) values are increasing while there is a fall in oxygen packing density (OPD) from 0% to 40% of TeO2. The ionic nature of the present glasses is analyzed from the bonding parameter (δ), optical basicity (Λth), covalent and ionic characteristic factors. The gamma photon attenuation investigated employing GEANT4 code. The transmission factor (TF) shows that 0TBD sample (0 wt% of TeO2) has the highest TF, while the 4TBD sample (40 wt% of TeO2) has the lowest TF.

AtıfScopus42

İncele

Sayyed, M.I.; Aşkın, A.; Ali, Atif Mossad; Kumar, Ashok; Rashad, M.; Alshehri, Ali M.; Singh, Mandeep

Amorphous PbO – WO3 – BaO – Na2O – B2O3 glass system have fabricated using traditional melt quenching method. The XRD and FTIR spectra confirm the amorphous nature and the various structural properties of the glasses respectively. The various optical properties have been measured in the spectral range 400–4000 cm−1. Also, to understand the shielding ability of the fabricated glasses, we used the Geant4 model of a HPGe detector and WinXcom program to calculate the mass attenuation coefficient (MAC) at six energies between 356 and 2510 keV. In order to confirm the agreement between both methods, we used correlation theory and calculated the correlation coefficients (R2) for each sample. It is found that the R2 values are close to 1 for all samples. The MAC values at 356 keV for the prepared samples lies between 0.221 and 0.246 cm2/g. It is found that the usage of different concentration of PbO (from 50 to 70 mol%) affects the MAC values and thus the attenuation ability of the samples due to the heavier density of the PbO in comparison to B2O3. The effective atomic number results showed that Pb70B10 sample (contains 70 mol% of PbO) was higher than the other samples. Hence, Pb70B10 absorbs more photons than the rest of the prepared glasses.

AtıfScopus33·OpenAlex33