  Development of alternative carbon fibre powder and rare earth element-based filler for high density polyethylene; [Entwicklung von alternativen Kohlenstofffaserpulvern und Seltene Erden-basierten Füllstoffen für Polyethylen hoher Dichte]

  Ayikurt, P.; Kısmet, Y.; Dogan, A.; Höchstötter, K.H.; Fiedler, B.

  This study developed alternative fillers to enhance the flowability of high-density polyethylene (HDPE). Lanthanum and cerium oxide with over 90 % purity were used as binder interfacial elements in fillers developed using both carbon fiber powder wastes and powder coating wastes. Polyethylene gel was used to make the fillers thermoplastic and homogenous. A total of six different fillers were developed and melt flow index analyses were performed. As a result of these analyses, it was found that the fluidity of high-density polyethylene improved significantly, especially with fillers containing carbon fiber powder. As a result, high-density polyethylene mixtures containing 10 %, 20 %, 30 %, 40 %, and 50% by weight of carbon fiber powder-based fillers were pressed into molds by a plastic injection molding machine, and samples were produced. According to the mechanical analysis results of these specimens, tensile and flexural strengths decreased slightly depending on the filling ratio, while the impact strengths remained constant. Differential scanning calorimetry analysis was performed to determine the glass transition temperature and melting/crystallization temperatures of the obtained mixtures, while thermogravimetric analysis was performed to determine the mass losses. At the same time, electron microscope analysis of the cross sections of the samples were performed.

  • 
  • 
  İncele
• MakaleYalnız künye2024Scopus SJRQ3/r/munzur/2126
  Powder coating waste filler in high-density polyethylene – Variations in morphology, mechanical and thermal performance; [Variationen in Morphologie, mechanischer und thermischer Leistung von Pulverlackrecyclaten als Füllstoff in Polyethylen mit hoher Dichte]

  Kısmet, Y.

  In the present study, electrostatic powder coating waste was recycled and employed to reinforce high-density polyethylene. The hydrolysis method was preferred to modify the powder coating waste of various systems, and they were mixed with high-density polyethylene at various weight ratios. The mixtures were prepared in a mechanical mixer and then in an extruder to obtain a homogeneous mixture. This homogeneous structure was pressed into molds with a plastic injection device to obtain standard tensile samples. Mechanical and thermal tests were conducted on the samples. It was determined that the tensile stress of the sample decreased with the increase in filler content. The changes in sample tensile strength were investigated after the samples were aged. Three-point bending strength of the samples was also investigated and it was observed that they became more resistant to vertical loads as the filler content increased. The Izod impact strength of the samples differed based on the filler type and weight ratio. Furthermore, mass loss in the produced mixtures was determined with thermogravimetric analysis. The matrix and filler bonding mechanisms were observed under an electron microscope.

  • 
  • 
  AtıfScopus1·WoS1·OpenAlex1

  İncele
• MakaleAçık Erişim2024Scopus SJRQ3/r/munzur/1736
  Synthesis process, thermal and electrical behaviors of Ti3C2Tx MXene; [Syntheseprozess, thermisches und elektrisches Verhalten von Ti3C2Tx MXene]

  Demirelli, K.; Çelik, A.; Aksoy, Y.; Yegin, M.; Barım, E.; Hanay, Ö.; Hasar, H.

  Synthesis of two-dimensional (2D) titanium carbide (Ti3C2Tx), with the name of MXene, by etching Ti3AlC2 (MAX) for different times 20 (v/v) % hydrofluoric acid (HF) at 40 °C was carried out. The influences of time, temperature and source of MAX on the synthesis of MXene were researched. The MXenes produced were characterized by fourier-transform ınfrared (FT-IR) spectroscopy technique, energy dispersive x-ray spectroscopy (EDX), scanning electron microscopy (SEM), x-ray diffraction (XRD) and thermogravimetry (TG) instruments. Above 390 °C, MXene layers were considerably oxidizing and forming anatase and rutile phases of TiO2 under air atmosphere. The resistance of MAX and MXene was 3.6 Ω and 116 Ω, respectively. However, the resistance of the residual part of MXene heated to 620 °C considerably increased to 17850 Ω. This behavior is another important piece of evidence showing that the MXene crystal structure has changed significantly and transformed into a new chemical structure containing anatase and rutil titanium oxide (TiO2). The dielectric loss (ϵ’’) and alternating conductivity (δac) of the MAX and MXenes were determined from their impedance measurements. The ϵ’’ and δac values of MXene were compared with those of MAX. Direct curent conductivities of MAX and MXene produced for 24 h were found to be 0.016 S/cm and 0.0023 S/cm, respectively.

  AtıfScopus12·OpenAlex11

  İncele
• MakaleYalnız künye2019Scopus SJRQ3/r/munzur/3636
  Utilizing hydrolyzed powder recyclates as filler in polystyrene; [Verwendung von hydrolisierten Pulverlackrecyclaten als Füllstoff in Polystyrol]

  Kismet, Y.; Wagner, M.H.

  In the present study, hydrolyzed powder coating wastes were used as filler materials in polystyrene compounds, and the effect on the mechanical properties, melt flow index and density of polystyrene compounds were investigated. Epoxy/polyester, epoxy and polyurethane systems with thermoset structure were used as powder coating recyclates. After separately hydrolyzing these wastes, 5 %, 10 %, 20 % and 30 % by weight were homogeneously mixed with polystyrene, initially mechanically and subsequently with an extruder in the melt at 180 °C. The resulting compounds were cooled and granulated, and by use of an injection molding machine at 180 °C to 200 °C, standard tensile test bars were produced. Tensile strength, bending strength and izod impact strength of the test bars were measured and the variations of the mechanical properties of the polystyrene compounds as a function of the type and amount of filler were examined. In addition, melt flow index and density of the compounds were determined. Furthermore, the bonding mechanism of filler and matrix material was examined by electron microscopy.

  • 