Çelik, E.; Aslan, A. K.

In this study, the powder mixture which consists of Cu-Fe-Co was produced by using the method of hot pressing technique. In addition, effect of heat treatment process on microstructure and mechanical properties of this alloy was investigated. Following the hot pressing process applied on the samples, heat treatment was carried out at 950 degrees C for two different dwelling times (90 and 180 minutes). Measured density values were considered as physical characteristics, while hardness and fracture strength values were considered as mechanical characteristics. It was observed that porosity rates of hot pressed samples were decreased by increasing of temperature and pressing parameters. In this study it was observed that Cu was spread in matrix and filled the micro porosities. Hardness values were determined to be decreased as a result of grain growth after heat treatment process. That 4 fold increased elongation % values which were achieved by TRS experiments were observed as well.

AtıfWoS3·OpenAlex2

İncele

Islak, S.; Çelik, E.; Kir, D.; Özorak, C.

In this study, the CuAl-TiC composite materials were produced using hot pressing process. Effect of TiC grain size (0.2, 4 and 20 mu m) on some properties of these materials was investigated experimentally. Production of CuAl-TiC composites was carried out under pressure of 35 MPa, at 700A degrees C, and for a sintering time of 5 minutes. SEM-MAP studies showed that the TiC grains were relatively homogeneously distributed in the CuAl matrix. Microstructure analysis revealed that the composite materials consist of Cu, Al, Cu9Al4, CuAl2 and TiC phases. With the decreasing of TiC grain size, the hardness, transverse rupture strength, relative density and sintered density of composites increased.

AtıfWoS7·OpenAlex8

İncele