Karaduman, Oktay; Boyrazli, Mustafa; Canbay, Canan Aksu; Özkul, İskender; Çelik, Emrah; Başbağ, Güneş

For the first time, CuAlVMg high-temperature shape memory alloy (HTSMA) with unprecedented alloy composition and with extended solubility of vanadium element was fabricated as-cast ingot by arc melting method, then homogenization of the alloy in high β-phase temperature region and quenching in iced-brine water were performed, respectively. The characteristic forward martensite to austenite martensitic transformation (MT) temperatures were detected at around 390 °C, which put the novel alloy in the category of HTSMAs. The thermal response of the alloy at high-temperatures was observed by DTA test as coherent with usual Cu-based HTSMAs. The residual sub-eutectoid precipitations emerging at around 500 °C hindered the direct martensitic transformation. The martensite structure of the alloy was revealed by XRD, SEM and optical microscopy tests.

İncele

Özkul, İskender; Boyrazli, Mustafa; Aksu Canbay, Canan; Başbağ, Güneş; Karaduman, Oktay

Shape memory alloys (SMAs) constitute the second largest commercial smart material class after piezoelectric materials. Different SMA alloy systems or SMAs with miscellaneous functionalities and characteristic properties have been designed for using in different applications until today. High temperature shape memory alloys (HTSMAs) are also widely desired to be used in various smart materials applications. HTSMAs with different functional and characteristic properties are muchly demanded for different tasks to be done by these alloys or devices designed by these alloys. A common and practical way to fabricate SMAs or HTSMAs with different shape memory effect (SME) and other properties is to fabricate them with different alloying compositions and add different additive elements. In this work, a quaternary CuAlZnMg HTSMA with an unprecedented composition consisting minor amount of zinc and magnesium additives was produced by arc melting method. As a result of applying post-homogenization in high β–phase temperature region and immediate quenching, the microstructural mechanism of a SME property was formed in the produced alloy. After then, to examine SME characteristics of the CuAlZnMg alloy some differential thermal analysis (DTA), microstructural (XRD) and magnetization (VSM) characterization tests were carried out. The DTA results showed that the alloy is a HTSMA exhibiting reverse martensitic transformations at temperature range between 167 °C and 489 °C. The XRD pattern obtained at room temperature revealed the martensite phases formed in the alloy, which phases are the base mechanism of the reversible martensitic transformation (the SME property) of the alloy. The VSM test showed that the alloy exhibit a diamagnetic property with a weak ferromagnetic coercivity contribution.

İncele

Başbağ, Güneş; Karaduman, Oktay; Canbay, Canan Aksu; Özkul, İskender; Boyrazlı, Mustafa

In this work, the new quaternary CuAlTiMg high-temperature shape memory alloy (HTSMA) with an unprecedented composition and with extended solubility of Ti was produced by the arc melting method. The thermal shape memory effect characterization tests were done by performing a series of differential calorimetric (DSC and DTA) measurements. The obtained thermograms of the alloy displayed the martensitic phase transformation peaks. The forward (martensite to austenite) phase transformation was found to occur at above 350◦C, which qualifies the produced alloy as an HTSMA. The microstructural XRD measurement was performed to reveal the atomic planes of martensite structures formed in the alloy, which constitute the shape memory effect property of the fabricated alloy. The alloy surface was monitored by optical microscopy image taken at room temperature, and finely dispersed Ti-rich X-phases were observed.

İncele