Simsek, Tuncay; Simsek, Telem; Chattopadhyay, Arun K.; Avar, Barış; Yakin, Alican; Guler, Seval Hale; Almisned, Ghada; Sen Baykal, Duygu; Tekin, H.O.

In this study, mechanically alloyed Fe70Nb10V10B10, Co70Nb10V10B10, Ni70Nb10V10B10, and (FeCoNi) 70Nb10V10B10 high-entropy alloys were successfully synthesized, and their structural, magnetic, and radiation shielding properties were systematically investigated. Structural analysis revealed that Fe favored bcc phase formation, while Co and Ni stabilized fcc structures; the equiatomic alloy resulted in a single-phase fcc solid solution with the smallest crystallite size (2.1 nm). All samples exhibited soft ferromagnetic behavior, with the Fe-based alloy achieving the highest saturation magnetization (120 emu/g), and the (FeCoNi) 70Nb10V10B10 alloy displaying the lowest coercivity. Among all compositions, Co70Nb10V10B10 demonstrated the best gamma and neutron shielding performance, showing the highest linear attenuation coefficient and fast neutron removal cross-section. The equiatomic alloy also exhibited well-balanced and stable shielding behavior. These findings position Co70Nb10V10B10 as a promising candidate for multifunctional applications requiring both efficient radiation protection and favorable magnetic properties.

AtıfScopus1

İncele

Guler, Seval Hale; Yakin, Alican; Guler, Omer; Chattopadhyay, Arun K.; Simsek, Tuncay

In this study, the traits, production methods, and applications of refractory high-entropy materials—including refractory high-entropy alloys (RHEAs), refractory high-entropy composites (RHE-Cs), and refractory high-entropy ceramics (RHE-Ce)—which are part of the broader category of refractory high-entropy materials with a wide range of applications, have been thoroughly examined and discussed. RHEAs have emerged as materials that exhibit superior properties, such as high melting temperatures, excellent temperature resistance, and high wear and corrosion resilience, in addition to high mechanical and fatigue strength. These attributes have made them extensively studied materials in recent times. The properties of RHEAs suggest their safe operation in challenging environments such as nuclear reactors, gas turbines, aerospace, and energy production. Among refractory materials, RHE-Cs stand out for their high strength and low density, showing significant potential for use in the automotive, aerospace, and space industries. Another group with a wide range of applications, RHE-Ce materials, is distinguished by their high-temperature resilience, high hardness, and low thermal conductivity, making them suitable for high-temperature environments. Refractory materials are generally fabricated using traditional techniques such as arc melting, powder metallurgy, and magnetron sputtering. In this study, along with traditional production methods, additive manufacturing techniques which have revolutionized the manufacturing field are discussed concerning their applications in refractory material production. Additive manufacturing methods enable the achievement of high temperatures and the production of homogeneous, single-phase solid solutions, making them suitable for fabricating refractory materials with high melting points.

AtıfScopus37·WoS35·OpenAlex41

İncele

Simsek, Tuncay; Kurtulus, Altug; Avar, Baris; Güler, Seval Hale; Dag, İlker Emin; Chattopadhyay, Arun K.

This study focuses on synthesizing and characterizing mechanically alloyed refractory high entropy alloys (RHEA) containing TiMoNb, Cr, W, and Cr + W. Analytical techniques including XRD, SEM, EDX, DTA, and TGA were employed to explore the influence of Cr and W on the alloys' structure, morphology, and thermal stability towards oxidation. XRD analysis confirmed the formation of a single-phase bcc solid solution in TiMoNbCr, TiMoNbW, and TiMoNbCrW alloys. Crystallite size decreased as milling progressed, yielding average sizes of approximately 7.2 nm, 7.4 nm, and 9.7 nm, with lattice strains of 1.143%, 1.148%, and 1.15%, respectively. Both experimental and calculated values of lattice parameters converged to around 3.1685 ± 0.002 and 3.1791 ± 0.010 Å for all three alloys. The synergy of Cr and W in TiMoNb was observed for the first time, impacting dislocation density, hardness, and oxidation stability. TiMoNbCrW exhibited reduced dislocation density and the highest hardness (502 HV). TGA indicated enhanced oxidation resistance up to 400 °C for TiMoNbCrW compared to the most vulnerable TiMoNbCr alloy.

AtıfScopus2·OpenAlex2

İncele

Şimşek, Telem; Özkul, İskender; Canbay, Canan Aksu; Avar, Barış; Şimşek, Tuncay; Güler, Seval Hale; Özcan, Sadan; Güler, Ömer; Chattopadhyay, Arun K.

In this study structural, morphological, thermal and magnetic properties of equiatomic CoNiMnGaSi (base), CoNiMnGaSiCu, CoNiMnGaSiSn and CoNiMnGaSiSb alloys are discussed. The formation of solid-solution nanocrystalline bcc structure of the alloys was determined by XRD and DTA techniques. SEM–EDS analyses also revealed the homogeneous distribution of the elements. The room temperature magnetic hysteresis loops showed that as-casted alloys reached saturation easily with coercivity less than or equal to 35 Oe. As the Cu and Sn were added to the alloy, the saturation magnetization was decreased from 112 emu/g to 50 emu/g, which was mainly due to the substitution of non-magnetic atoms to the magnetic Co in the base CoNiMnGaSi alloy, whereas the addition of Sb to the base alloy did not have a significant effect on the Ms. The CoNiMnGaSiSb was found to have the highest Curie Temperature of 670 K, which makes the alloy a promising candidate for power industry-related applications.

AtıfScopus3·OpenAlex4