  Improvement of mechanical, dynamic mechanical, and thermal properties of almond shell powder reinforced acrylonitrile butadiene styrene composites by addition of cerium oxide

  Doğan, Akar; Güneş, Çağdaş

  Currently, natural materials are gradually replacing synthetic materials in polymer composites due to factors including cost-effectiveness, sustainability, and the availability of raw materials. This study examined the variations in thermal, mechanical, and dynamic mechanical properties of acrylonitrile butadiene styrene (ABS) thermoplastic composite materials incorporating varying ratios of almond shell powder (ASP) and Cerium Oxide (CeO2). Tensile tests, three-point bending tests, dynamic mechanical analyses, and thermogravimetric analyses were conducted. Scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) analyses were employed to assess pure ABS and nine distinct composite materials. The tensile strength, elastic modulus, and three-point bending strength of the composite material exhibited increases of 6%, 7%, and 7.5%, respectively, compared to pure ABS, with various ratios of almond shell powder and CeO2 reinforcement. Moreover, composite materials exhibit elevated glass-transition temperatures and storage moduli compared to pure ABS. Microstructure images obtained through SEM and EDS element mapping illustrate the distribution of ASP and CeO2 in ABS, influencing its mechanical and thermal properties. Highlights: Almond shell powder and cerium oxide were used as filler materials in ABS. Mechanical, morphological, and dynamic mechanical properties were investigated. Almond shell powder enhanced the mechanical properties of the ABS composite. Low cerium oxide supplementation improved the mechanical properties.

  • 
  AtıfScopus4·WoS4·OpenAlex5

  İncele
• MakaleYalnız künye2024Scopus SJRQ2/r/munzur/2277
  Mechanical and thermal properties of short banana fiber reinforced polyoxymethylene composite materials dependent on alkali treatment

  Doğan, Akar; Güneş, Çağdaş

  The present study aimed to develop a recyclable composite material based on a natural product, namely banana fiber, instead of synthetic reinforcement elements such as glass fiber or carbon fiber in thermoplastic matrix composites employed in many aspects of daily life. Polyoxymethylene (POM) thermoplastic was used as the matrix material. 3 %, 6 %, and 9 % by weight short natural banana fiber was used as reinforcement. Furthermore, the study improved the mechanical and thermal properties of the composite material with chemical improvements based on alkali treatment of banana fiber. Banana fiber and POM was initially mixed mechanically and then extruded at temperatures between 170 and 190 °C to obtain a homogeneous mixture. The mixture obtained by extrusion was initially cooled in the cooling pool and then passed through the crusher to obtain granules. These granules were pressed in plastic injection molds to obtain standard test samples. The ratio of reinforcement material and the variations in mechanical and thermal properties of the composites induced by the alkali treatment are presented in figures and tables. Furthermore, the changes in cross-sectional material images were examined with electron microscopy scans. The tensile and flexural strength of the material improved with alkali treatment.

  • 
  AtıfScopus21·WoS19·OpenAlex20

  İncele
• MakaleAçık Erişim2022/r/munzur/6547
  Sıcak Presleme Yöntemi İle Üretilen Fe Esaslı Matriste Ni Esaslı Süper Alaşımların Katkı Oranlarının Etkisi

  Somunkıran, İlyas; Çelık, Ertugrul; Tunç, Büşra; Güneş, Çağdaş

  Doğal taş kesme işlemlerinde kullanılan elmaslı kesici takımlar da matris dizaynı; takımların kesme performansı açısından oldukça önem arz etmektedir. Bu çalışmada toz metalurjisi yöntemiyle Fe-Ni-Cu metal tozlarına ağırlıkça farklı oranlarda (%10-20-30) 9062 ve 9045 ticari kodlu nikel esaslı süper alaşımlar ilave edildi. Üretilen numunelerin mikro yapı ve bazı mekanik özellikleri incelendi. Deney numuneleri 920ºC sıcaklıkta 35 MPa basınç altında dört dakika süre boyunca sıcak preslendi. Elde edilen numunelerin sertlik, yoğunluk, üç noktalı eğilme testleri yapıldı. Mikroyapı incelemeleri için SEM (taramalı elektron mikroskobu), ve XRD kullanıldı. Numunelerin SEM görüntülerinde 9045 ve 9062 ticari kodlu Ni esaslı alaşım ile takviyelendirilmiş düzgün küresel tozların yapı içerisinde homojen dağıldığı ve en yüksek sertlik değeri 9062 grubu numunelerde olduğu gözlenmiştir.

  AtıfOpenAlex1·TR Dizin1

  İncele
• MakaleAçık Erişim2022/r/munzur/5852
  Toz Metalurjisi Yöntemiyle Üretilen Fe Esaslı Fe-Ni-Cu Elmas Kesici Takımında Co’ın Etkisi

  Somunkıran, İlyas; Çelık, Ertugrul; Tunç, Büşra; Güneş, Çağdaş

  Bu çalışmada toz metalürjisi (TM) tekniğiyle Fe esaslı Fe-Ni-Cu matrisine ağırlıkça farklı oranlarda (%10-20-30) kobalt (Co) ilave edilerek üretilen numunelerin mikroyapı ve bazı mekanik özellikleri incelendi. Sinterleme; 920 ºC’ de, 35 MPa basınç altında, 4 dk süreyle argon gazı atmosferinde yapıldı. Numunelerin mikroyapısal karakterizasyonu X-ışınları analizi (XRD), taramalı elektron mikroskobu (SEM), enerji dağılım spektrometresi (EDS) ile incelendi. Yoğunluk ölçümleri yapılan numuneler, sertlik ve üç noktalı eğme deneylerine tabi tutuldu. Sonuç olarak; takviye oranının artması ile porozitede azalma meydana geldi. En yüksek sertlik ve yoğunluk değerinin %20 Co ilaveli numunede olduğu görüldü. Co oranı ilavesiyle başlangıçta eğme gerilmesi ve yüzde uzamanın arttığı ve artan Co oranıyla birlikte eğme gerilmesi ve yüzde uzamanın azaldığı gözlendi.

  AtıfOpenAlex2·TR Dizin1