Ayday, Aysun; Duru, Erhan; Kırsever, Derya; Doğan, Fatih

This study investigates the influence of Y2O3 addition on the microstructure, growth kinetics, and mechanical properties of TiO2-based ceramic coatings formed on Ti–6Al–4V alloy through the Micro Arc Oxidation (MAO) process. The experiments were carried out using Ti–6Al–4V plates coated in silicate-based electrolytes, with and without 1 g/L Y2O3, under a constant current density of 5 A/dm2 and a voltage of 360 ± 20 V for different treatment times (1, 3, 7, and 10 min). The coatings were evaluated by weight gain measurements, SEM/EDS analyses, X-ray diffraction (XRD), and constant load scratch testing supported by profilometry. Results revealed that Y2O3 significantly accelerated coating growth during the initial stages, leading to higher weight gains and denser, less porous morphologies compared to Y2O3-free coatings. XRD analysis indicated amorphous TiO2 and anatase phases at short durations, while rutile formation became dominant with longer treatments. Kinetic modeling demonstrated that both coatings initially followed a linear reaction-controlled mechanism (n ≈ 1), with calculated growth constants of 3.44 × 10⁻4 mg/mm2·s for Ti-MAO and 7.45 × 10⁻4 mg/mm2 s for Ti–Y2O3–MAO. However, after approximately 420 s, the Y2O3 coatings exhibited a marked reduction in growth rate due to electrical insulation effects of the thickened ceramic layer, resulting in multi-stage kinetics. Constant load scratch testing showed that Y2O3 incorporation reduced groove depth and width by nearly 45%, improving adhesion strength and mechanical durability. These findings confirm that rare-earth oxide addition is an effective strategy for enhancing the performance of MAO coatings on titanium alloys.

AtıfScopus2·WoS1·OpenAlex2

İncele

Ayday, Aysun; Durmaz, Mustafa; Duru, Erhan; Kırsever, Derya; Doğan, Fatih

In this study, CeO2-doped ceramic coatings were produced on Al 1050 alloy by micro-arc oxidation (MAO) using a silicate-alkaline electrolyte containing 0, 0.5, 1, and 2% CeO2. The aim was to investigate the effect of CeO2 addition on the microstructure, phase composition, corrosion behavior, and constant-load scratch adhesion performance of the coatings. Surface characterization was carried out by SEM, EDS, XRD, and 3D profilometry, while corrosion performance was evaluated by potentiodynamic polarization and electrochemical impedance spectroscopy in 3.5 wt% NaCl solution. Scratch tests were also performed to assess the mechanical integrity of the coatings. The results showed that increasing CeO2 content improved coating uniformity, reduced surface roughness and porosity, and promoted the formation of a denser oxide structure. XRD analysis confirmed that γ-Al2O3 was the predominant alumina phase in all coatings, while Ce-containing species were incorporated into the oxide layer without forming additional detectable phases. Electrochemical results revealed that CeO2 addition significantly improved corrosion resistance by lowering the corrosion current density and increasing the polarization resistance. Scratch test results further showed improved adhesion-related behavior with reduced crack formation and surface damage. Overall, CeO2 addition effectively enhanced both the corrosion protection and mechanical performance of MAO coatings on Al 1050 alloy.

AtıfScopus1·OpenAlex1

İncele