Sürdürülebilir Kalkınma Amaçları
Yayınlar
- MakaleYalnız künye2025Scopus SJRQ3Development of alternative carbon fibre powder and rare earth element-based filler for high density polyethylene; [Entwicklung von alternativen Kohlenstofffaserpulvern und Seltene Erden-basierten Füllstoffen für Polyethylen hoher Dichte]
Ayikurt, P.; Kısmet, Y.; Dogan, A.; Höchstötter, K.H.; Fiedler, B.
This study developed alternative fillers to enhance the flowability of high-density polyethylene (HDPE). Lanthanum and cerium oxide with over 90 % purity were used as binder interfacial elements in fillers developed using both carbon fiber powder wastes and powder coating wastes. Polyethylene gel was used to make the fillers thermoplastic and homogenous. A total of six different fillers were developed and melt flow index analyses were performed. As a result of these analyses, it was found that the fluidity of high-density polyethylene improved significantly, especially with fillers containing carbon fiber powder. As a result, high-density polyethylene mixtures containing 10 %, 20 %, 30 %, 40 %, and 50% by weight of carbon fiber powder-based fillers were pressed into molds by a plastic injection molding machine, and samples were produced. According to the mechanical analysis results of these specimens, tensile and flexural strengths decreased slightly depending on the filling ratio, while the impact strengths remained constant. Differential scanning calorimetry analysis was performed to determine the glass transition temperature and melting/crystallization temperatures of the obtained mixtures, while thermogravimetric analysis was performed to determine the mass losses. At the same time, electron microscope analysis of the cross sections of the samples were performed.
- MakaleYalnız künye2024Scopus SJRQ3Powder coating waste filler in high-density polyethylene – Variations in morphology, mechanical and thermal performance; [Variationen in Morphologie, mechanischer und thermischer Leistung von Pulverlackrecyclaten als Füllstoff in Polyethylen mit hoher Dichte]
Kısmet, Y.
In the present study, electrostatic powder coating waste was recycled and employed to reinforce high-density polyethylene. The hydrolysis method was preferred to modify the powder coating waste of various systems, and they were mixed with high-density polyethylene at various weight ratios. The mixtures were prepared in a mechanical mixer and then in an extruder to obtain a homogeneous mixture. This homogeneous structure was pressed into molds with a plastic injection device to obtain standard tensile samples. Mechanical and thermal tests were conducted on the samples. It was determined that the tensile stress of the sample decreased with the increase in filler content. The changes in sample tensile strength were investigated after the samples were aged. Three-point bending strength of the samples was also investigated and it was observed that they became more resistant to vertical loads as the filler content increased. The Izod impact strength of the samples differed based on the filler type and weight ratio. Furthermore, mass loss in the produced mixtures was determined with thermogravimetric analysis. The matrix and filler bonding mechanisms were observed under an electron microscope.
AtıfScopus1WoS1OpenAlex1
İncele