Sürdürülebilir Kalkınma Amaçları
Yayınlar
- MakaleYalnız künye2026Scopus SJRQ1Enhancing durability of slag-based alkali-activated composites with dunite sand and carbon fiber: Sulfate, freeze–thaw, and thermal resistance optimization
Benli, Ahmet; Bürlükkara, Sadullah; Öz, Ali; Karataş, Mehmet; Kaplan, Gökhan
The replacement of natural river sand with sustainable alternatives is essential to reduce environmental degradation associated with aggregate extraction. In this context, dunite sand (DS), a magnesium-rich ultramafic mineral, was investigated as an eco-efficient fine aggregate in thermally cured slag-based alkali-activated composites (AACs), in combination with carbon fiber (CF) reinforcement. The study aims to clarify how aggregate substitution and fiber addition interact to control matrix densification, crack-bridging efficiency, and durability under aggressive conditions. Sixteen mixtures incorporating varying DS (0–100%) and CF (0–1.00%) contents were prepared and cured at 80°C to promote rapid slag activation and microstructural development. Mechanical performance, high-temperature resistance, sulfate durability, and freeze–thaw behavior were systematically evaluated. The results demonstrate that moderate DS substitution (~25%) significantly improves matrix compactness and interfacial quality through a micro-filler effect, leading to enhanced strength and durability. CF effectively bridge micro cracks and improve flexural and thermal performance; however, excessive fiber contents impair workability and increase porosity due to fiber clustering. Durability results confirm that optimized DS–CF combinations reduce thermal degradation, limit sulfate-induced deterioration, and enhance resistance to cyclic freezing. Overall, 25% DS replacement combined with limited CF content (≤0.50%) provides the best balance between mechanical performance and durability. The findings highlight the importance of controlling aggregate–fiber synergy and curing strategy to develop durable, thermally stable, and sustainable alkali-activated composites for harsh service environments.
AtıfScopus5WoS4OpenAlex4
İncele - MakaleYalnız künye2025Scopus SJRQ1Dunite powder as a green precursor in one-part alkali-activated composites: Effects on mechanical and durability properties
Benli, Ahmet; Bayraktar, Oğuzhan Yavuz; Karataş, Mehmet; Bodur, Burak; Yılmazoğlu, Mehmet Uğur; Kaplan, Gökhan
Natural pozzolans are a sustainable alternative to Portland cement, offering abundant alumina and reactive silica for geopolymer production. Due to their simple extraction methods, they are cost-effective and environmentally friendly. This study explores the utilization of dunite powder (DP) as a sustainable precursor in one-part alkali-activated slag-based composites (AAC), aiming to evaluate its potential to partially replace granulated blast furnace slag (GBFS). The mechanical, fresh, and durability properties of the composites were investigated by varying DP replacement levels (0%, 15%, 30%, and 60%) under an activator dosage of sodium metasilicate, with the mixtures cured at 80 °C for 24 h and subsequently exposed to ambient conditions. The compressive and flexural strengths were evaluated at 7, 28, and 91 days, while the fresh properties (flowability and setting time), durability under sulfate attack, high-temperature resistance, freeze-thaw resistance, dry shrinkage, sorptivity and microstructural characteristics (SEM, XRD, and FT-IR) were also examined. The compressive strength decreased with higher DP content, with the 60% DP mixture showing a 43% strength reduction at 28 days compared to the reference mixture. However, the 30% DP mixture achieved a favorable balance between strength and sustainability, demonstrating a compressive strength decrease of only 11% at 91 days. The mixture containing 15% DP demonstrated the best performance under high-temperature conditions and freeze-thaw cycles. The 60% DP mixture exhibited the highest mass and strength loss when exposed to temperatures above 400 °C and a 15% compressive strength reduction after 120 days of immersion in a 10% MgSO4 solution.
AtıfScopus29OpenAlex22İncele