Sürdürülebilir Kalkınma Amaçları
Yayınlar
- MakaleAçık Erişim2017Scopus SJRQ2Synthesis, thermal degradation and dielectric properties of poly[2-hydroxy,3-(1-naphthyloxy)propyl methacrylate]
Biryan, Fatih; Demirelli, Kadir; Torgut, Gulben; Pihtili, Guzin
2-Hydroxy-3-(1-naphthyloxy)propyl methacrylate (NOPMA) monomer was synthesized from reaction of 2-[(2-naphthyloxy)methyl]oxirane with methacrylic acid in the presence of pyridine. The polymerization of NOPMA was carried out by free radical polymerization method in the presence of AIBN at 60 A degrees C. The structure of monomer and polymer was characterized by H-1-NMR, C-13-NMR and FT-IR spectroscopy techniques. The glass transition temperature and average-molecular weights of poly(NOPMA) were measured using differential scanning calorimetry and gel permeation chromatography, respectively. The thermal degradation behavior of poly(NOPMA) has been investigated by FT-IR studies of the partially degraded polymer and thermogravimetry. The cold ring fractions (CRFs) were collected at two different temperatures, initially fraction-1 (CRF1) is from room temperature to 320 A degrees C, and the other fraction-2 (CRF2) is from 320 to 500 A degrees C. The volatile products of the degradation were trapped at -195 A degrees C (in liquid nitrogen). All the fractions were characterized by FT-IR, H-1 and C-13-NMR spectroscopic techniques, and the cold ring fractions (CRFs) were also characterized by GC-MS. For the degradation of polymer, the major compound between products of CRFs is alpha-naphthol. The GC-MS, FT-IR and NMR data showed that depolymerization corresponding to monomer was not prominent below 320 A degrees C in the thermal degradation of poly(NOPMA). The mode of thermal degradation containing formation of the major products was identified. The dielectric permittivity (epsilon'), the loss factor (epsilon aEuro(3)) and conductivity (sigma(ac)) were measured using a dielectric analyzer in the frequency range of 50 Hz to 20 kHz.
AtıfWoS17OpenAlex22
İncele - MakaleAçık Erişim2017Scopus SJRQ1Application of response surface methodology for optimization of Remazol Brilliant Blue R removal onto a novel polymeric adsorbent
Torgut, Gulben; Tanyol, Mehtap; Biryan, Fatih; Pihtili, Guzin; Demirelli, Kadir
The poly[2-hydroxy-3-(1-naphthyloxy)propyl] methacrylate [poly(NOPMA)] was used as a novel adsorbent for the removal of Remazol Brilliant Blue R (RBBR) known as a reactive dye. Physico-chemical properties of polymer were analyzed by FT-IR and SEM before and after dye adsorption. The Langmuir and Freundlich isotherms were used to explain the adsorption equilibrium, and when it was compared with each other it was seen that the adsorption process was well explained by the Langmuir isotherm model and showing a monolayer adsorption capacity for RBBR of 238.10 mg/g. Kinetic models known as pseudo-first-order, pseudo-second-order and intra-particle diffusion model were utilized to analyze the mechanism of adsorption, and results indicated that was an adsorption kinetic suitable with the pseudo-second-order. The thermodynamic parameters (∆Ho, ∆So, ∆Go) indicated that the adsorption process was spontaneous and endothermic. To optimize the study conditions, the effects of the concentration of RBBR, adsorbent amount and contact time on the adsorption were investigated by response surface methodology (RSM). According to RSM results, maximum RBBR removal was reached at the optimum initial dye concentration of 60.85 mg/L, adsorbent dosage of 0.04 g/50 mL and contact time of 59.91 min.
AtıfScopus40WoS37OpenAlex43
İncele