Sürdürülebilir Kalkınma Amaçları
Yayınlar
- MakaleAçık Erişim2026Scopus SJRQ2Radiation shielding performance of CeO2-reinforced ternary nanocomposites based on biodegradable polymers and waste-derived polystyrene
Pekdemir, Mustafa Ersin; Yilmaz, Demet; Selçuk Pekdemir, Sibel; Gülhan, Aleyna; Yalçin Kuzu, Serpil; Altun, Sedanur; Taşgin, Yahya
The development of sustainable polymer-based materials for radiation shielding has attracted increasing interest, particularly for lightweight and flexible applications. In this study, ternary nanocomposites based on poly (hydroxyalkanoate) (PHA), poly (ε-caprolactone) (PCL), and polystyrene (PS) were prepared and reinforced with cerium oxide (CeO2) nanoparticles (5–15 wt%) to enhance radiation shielding performance. Structural characterization confirmed the preservation of polymer chemical structures and the successful incorporation of crystalline CeO2, while SEM observations revealed a relatively homogeneous nanoparticle dispersion within the ternary matrix, particularly at intermediate filler loadings. Thermal analysis demonstrated enhanced thermal stability with increasing CeO2 content, as evidenced by an increase in residual mass from 0.42% for the neat blend to 11.21% for the nanocomposite containing 15 wt% CeO2, along with a shift of degradation onset temperatures toward higher values. Photon shielding performance was experimentally evaluated in the energy range of 13.37–59.54 keV. The incorporation of 15 wt% CeO2 increased the mass attenuation coefficient (MAC) from 1.277 to 12.366 cm2 g−1 at 13.37 keV, corresponding to an approximately ninefold enhancement, while significantly reducing the half-value layer (HVL) and mean free path (MFP). Neutron shielding analysis showed a slight decrease in thermal neutron attenuation due to hydrogen dilution within the polymer matrix, whereas fast neutron attenuation and neutron removal cross sections exhibited only minor variations; the fast neutron removal cross section increased modestly from 0.1014 to 0.1047 cm−1 with 15 wt% CeO2 addition. Overall, the results highlight clear structure–property–performance relationships in CeO2-reinforced PHA/PCL/PS nanocomposites, demonstrating their potential as lightweight radiation shielding materials for low energy protection with improved thermal stability and shielding efficiency.
AtıfScopus2OpenAlex1
İncele - MakaleYalnız künye2024Scopus SJRQ1Influence of praseodymium oxide on the structural, mechanical and photon, charged particles, and neutron shielding properties of alumina borate glass
Acikgoz, Abuzer; Izguden, Ilyas; Tasgin, Yahya; Yilmaz, Demet; Demircan, Gokhan; Kalecik, Sedanur; Aktas, Bulent
The structural, mechanical and radiation shielding properties of (69-x)B2O3-20TeO2-10Al2O3-1HfO2-xPr6O11 (where x = 0, 0.25, 0.5, 0.75, 1 mol %) glass system were investigated. This study introduces a novel approach by incorporating Pr6O11 into glass composition, highlighting its unique contributions to enhancing elastic properties, fracture toughness, hardness, and radiation shielding abilities. Experimental measurements were conducted within the energy range of 59.54–661.62 keV and theoretical calculations are made for MAC values. The presence of Pr6O11 was noted to positively influence the gamma shielding capabilities. At 59.54 keV, the addition of 0.25 mol% Pr6O11 increased the mass attenuation coefficient of the glass by 2.9 %, and the addition of 1 mol% Pr6O11 increased it by 29.8 %. The addition of 0.25 mol% Pr6O11 increased the fast neutron removal cross section of the glass by 4.4 %. Also, it is observed that the glass with 1 mol% Pr6O11 is the best shielding material against alpha and proton particles. A significant enhancement of 24.36 % in the fracture toughness value was observed, increasing from 1.059 to 1.317 MPa m1/2 at 1 mol% Pr6O11. Experimental hardness values increased from 3.374 to 3.985 GPa, resulting in an improvement of 18.11 % at 1 mol% Pr6O11. The thermal stability (ΔT, °C) value demonstrated a notable increase from 85 to 106, indicating a significant 24.7 % improvement at 0.25 mol% Pr6O11.
AtıfScopus58WoS57OpenAlex60İncele