- MakaleYalnız künye2026Scopus SJRQ1Effect of Ni–Co–Cr additions on the microstructural and magnetic field–induced radiation shielding behavior of Fe–Si–B alloys
Taşgın, Yahya; Taşar, Fatih
Fe–Si–B–based amorphous metallic glasses were synthesized via powder metallurgy and arc melting, followed by alloying with 10 wt% Ni, Co, or Cr. The alloys were examined in both as-cast and heat-treated conditions to assess the combined influence of composition, thermal relaxation, and magnetic processing on their mechanical and radiation-shielding properties. Microstructural characterizations (XRD, SEM, EDS) confirmed homogeneous alloying and the presence of Fe2B, Fe0.91Si0.09, and Ni/Co/Cr-boride phases. After alloying and heat treatment, the average Vickers hardness increased from 313 HV (base Fe-Si-B) to 480 HV. All synthesized samples were exposed to a 1 T magnetic field, and their gamma-ray attenuation behavior was subsequently evaluated using a Ba-133 source (80.99–383.85 keV). After magnetic exposure, the linear attenuation coefficient (LAC) increased by ≈ 3–4% for Co-doped alloys, ≈ 2% for Ni-doped and base Fe–Si–B alloys, and < 0.5% for Cr-doped alloys, accompanied by a corresponding reduction in half-value layer (HVL) from 1.86 cm to 1.79 cm. The fast-neutron removal cross-section (ΣR) also exhibited a modest rise (≈2%). These enhancements are attributed to field-induced microstructural relaxation, including domain alignment, internal-stress reduction, and partial free-volume collapse, which subtly modify the local electron-density distribution without altering the bulk composition. Overall, the findings demonstrate that Ni–Co–Cr alloying, combined with controlled magnetic-field exposure, offers an effective and non-destructive route to enhance both the mechanical durability and γ-ray/fast-neutron shielding performance of Fe-based amorphous alloys, highlighting their potential for magnetically tunable protective coatings and advanced smart-shielding applications. In some applications, both the magnetic properties and radiation shielding properties of the material used are important. This study investigates the effects of Ni, Co, and Cr on the magnetic properties of the Fe-Si-B alloy, while also demonstrating changes in radiation shielding properties.
AtıfScopus1WoS1OpenAlex1
İncele - MakaleAçık Erişim2026Scopus SJRQ2Investigation of the Mechanical and Metallographic Effects of Adding 2-3% Al-Ti-Mo Elements to High-Entropy CoCrFeNi Alloys
Dilek, İlhan; Taşgın, Yahya; Kanca, Muhammed Sait; Kök, Mediha; Güler, Ömer
Recently, high-entropy alloys (HEAs) have attracted significant attention due to their unique multicomponent composition and exceptional mechanical properties, such as high wear and corrosion resistance, making them superior to conventional alloys for advanced engineering applications. The effects of Al, Ti, and Mo addition on the microstructural and mechanical properties of CoCrFeNi-based HEAs were investigated. The alloys were produced via powder metallurgy and vacuum arc melting, with the addition of 2 and 3% Al, Ti, and Mo, respectively. Scanning electron microscopy (SEM), energy-dispersive x-ray spectroscopy (EDS), and x-ray diffraction (XRD) were used to perform microstructural characterization, while microhardness and wear tests were used to evaluate mechanical performance. The addition of Al and Ti enhanced the face-centered cubic phase stability and increased the hardness by improving the lattice structure. In contrast, the addition of Mo contributed to solid solution and precipitation hardening, resulting in a simpler microstructure and superior tribological performance. Among all compositions, the alloy with 3% Mo addition exhibited the highest hardness value (≈ 233.8 HV) and the lowest mass loss (4.3 mg) was observed, indicating a significant improvement in the wear resistance and mechanical strength. In conclusion, the addition of Ti and Mo to CoCrFeNi HEAs promotes solid solution, precipitation, and grain boundary hardening mechanisms, thereby enhancing microstructural integrity, hardness, and wear resistance. These findings suggest that such alloys are promising candidates for use as next-generation structural and tribological materials under demanding operational conditions.
- MakaleAçık Erişim2022Scopus SJRQ1High-temperature and abrasion resistance of self-compacting mortars incorporating binary and ternary blends of silica fume and slag
Yön, Merve Şahin; Arslan, Furkan; Karatas, Mehmet; Benli, Ahmet
Researchers from all over the world have recently developed an interest in the utilization of waste materials in the concrete industry. Using silica fume (SF) and ground granulated blast furnace slag (S) to manufacture self-compacting mortars (SCMs) could be a step toward sustainable waste management and produce the unique fresh qualities needed for SCMs. This research evaluates the abrasion and high-temperature resistance of SF and S based SCMs. A total of 14 mixtures were designed by partially replacing SF and S with Portland cement (PC) including control, binary and ternary mixtures. Binary mixtures were obtained by replacing cement by SF and S at replacement rates of 5, 10, 15 and 20 % and 10, 20, 30 % by weight respectively. Ternary mixtures were determined at the rates of 5, 10, 15 and 20 % SF and 10 and 20 % S respectively. The flexural strength and compressive strength of SF and S based binary and ternary water curing SCMs samples were determined at the age of 7, 28 and 90 days at room conditions. SCMs specimens were exposed to high temperatures after 90-day water curing. Water absorption, apparent porosity, sorptivity and abrasion resistance of 28-day water cured SCMs samples was also determined. The fresh and rheological properties of SCMs was evaluated by conducting mini-slump flow and viscosity tests. Cost analysis of the SCMs were also performed. The experimental results exhibited that the flowability of SCMs mixes containing SF was reduced with the increasing rate of SF compared to control while the workability of S incorporated SCMs mixes increased with the increase of S in comparison to control mixtures. Late- age of compressive strength above 70 MPa was achieved for 20 % SF incorporated binary mixture and 15 %SF and 10 % S incorporated ternary mixture. The ternary mixture with 15 % SF and 10 % S also exhibited the best abrasion resistance and the lowest sorptivity. Overall, it can be concluded from the mechanical characteristics and abrasion resistance that ternary combination of S with SF content of especially above 10 % and can be used to manufacture self-compacting mortar with a smaller carbon footprint.
AtıfScopus60WoS56OpenAlex62İncele