Sürdürülebilir Kalkınma Amaçları
Yazarlar
Yayınlar
- MakaleYalnız künye2021Scopus SJRQ2Recovery of Cu(II) by Acorga M5640 After Leaching of Malachite Ore in Perchloric Acid Solutions
Demirkıran, Nizamettin; Tanaydın, Mehmet Kayra
Abstract: In the present study, the recovery of Cu2+ from the resulting actual leach solution after the leaching of malachite ore in perchloric acid solutions was examined by applying the solvent extraction method. The organic phase was prepared using Acorga M5640 and kerosene. The effects of the initial pH of solution, extractant concentration, Cu2+ concentration, temperature, and stirring speed on the extraction process were investigated. It was determined that the extraction yield increased with an increase in the extractant concentration, initial pH of aqueous solution, stirring speed, and temperature, and with a decrease in the concentration of Cu2+. To prevent or minimize Zn2+ transfer to the organic phase and to ensure maximum Cu2+ extraction from the aqueous phase, the optimal values for the initial pH of the aqueous phase, initial concentration of Cu2+, extractant concentration, temperature, and stirring speed were selected to be 1, 0.152 g/L, 4% (v/v), 25 °C, and 400 rpm, respectively. The stoichiometry and mechanism of the extraction process were determined applying the equilibrium slope method. The changes in the Gibbs free energy, enthalpy, and entropy were determined. The changes in these thermodynamic parameters were calculated to be − 3.87 kJ/mol, 64.67 kJ/mol, and 0.23 kJ/(mol K), respectively. Graphical Abstract: The extraction percentage of Cu2+ increases substantially when the initial pH of the leach solution increases from 0.1 to 1. The further increase in the initial pH above 1 does not create an increase in the extraction extent of Cu2+. When the initial pH of the leach solution is higher than 1, the amount of Zn2+ transferred from the aqueous phase to the organic phase increases significantly.[Figure not available: see fulltext.].
AtıfScopus7WoS5OpenAlex9
İncele - MakaleYalnız künye2020Scopus SJRQ3Kinetic models for the extraction of copper by Acorga M5640 after leaching of malachite ore in perchloric acid solutions and the stripping of copper from loaded organic phase
Tanaydın, Mehmet Kayra; Demirkıran, Nizamettin
In the present work, the extraction kinetics of copper using the resulting actual leach solution obtained from the leaching of malachite ore in perchloric acid solutions and the stripping kinetics of copper from the loaded organic phase were examined. The organic phase was prepared by using Acorga M5640 and kerosene. In the extraction process, the effects of the initial pH of aqueous solution, initial concentration of copper, extractant concentration, temperature, and stirring speed on the extraction rate were investigated. In the stripping process, the effects of the concentration of perchloric acid, temperature, stirring speed, and extractant concentration on the stripping rate were examined. It was determined that the extraction rate increased with increasing the initial pH of aqueous solution, stirring speed, extractant concentration and temperature, and with decreasing the initial concentration of copper ions. In the stripping process, it was observed that the stripping rate increased with increasing the concentration of perchloric acid, temperature and stirring speed, and with decreasing the extractant concentration. It was determined that both the solvent extraction and stripping processes could be described by the first order pseudo homogenous reaction model. The activation energy for the extraction and stripping processes was calculated to be 50.04 kJ/mol and 32.42 kJ/mol, respectively.
AtıfScopus8WoS7OpenAlex10İncele