- MakaleAçık Erişim2024Scopus SJRQ3ENHANCING MILLING PERFORMANCE OF 6061 ALUMINUM ALLOY WITH NANOCUTTING FLUID AND MQL
Tosun, Nihat; Rasul, Sleman Yahya; Mahmat, Aybars; Tosun, Gul
During the machining of aluminum alloys, the adhesion of chips to the tool affects the performance characteristics. Today, different cooling systems are used to eliminate these negativities. In this study, the effects of end milling using HSS and carbide cutting tools of 6061-T6 aluminum alloy on surface roughness, chip thickness ratio and tool wear were examined using different cooling techniques (dry, minimum quantity lubrication (MQL) and nanocutting fluid). Different cutting speeds (180, 200, 220 m/min) and different feed rates (0.05, 0.06, 0.07 mm/rev) were used in the experiments. According to experimental findings, tool wear and surface roughness decreased at low cutting speed and feed rate by using nanocutting fluid with carbide cutting tools. It has been observed that the chip thickness ratio increases with high cutting speeds using nanocutting fluid and decreases with dry machining and high feed rates. The best milling performance of the aluminum alloy was achieved in experiments using carbide cutting tools and nanocutting fluid.
AtıfScopus4WoS4OpenAlex4
İncele - MakaleYalnız künye2023Scopus SJRQ2Aluminum Recovery by Acid Leaching of Variously Enriched Pyrophyllite Ore: Effects of Pre-treatment Methods for Activation
Aydoğmuş, Ramazan; Erdemoğlu, Murat; Uysal, Turan
Effects of pre-treatment methods such as calcination for thermal activation and intensive milling for mechanical activation on the aluminum (Al) recovery by acid leaching of preliminarily enriched pyrophyllite ore via attrition scrubbing and froth flotation were investigated. XRD patterns of the calcined and the intensively milled samples were compared to determine the changes during the pre-treatment processes. Hot HCl solution was used for dissolution of aluminum to determine the Al recoveries from variously enriched and variously pre-treated pyrophyllite ore samples. Specific thermal and milling energies consumed per unit amount of ore were calculated, and the ideal activation method was suggested by comparing the activation methods in terms of energy consumption. Mechanical activation of the pyrophyllite concentrate obtained by attrition scrubbing rather than froth flotation was suggested for higher recoveries of aluminum from by acidic leaching. It was determined that operating cost (in terms of energy) of the mechanical activation is lower and aluminum recovery is higher than thermal activation. It was concluded that mechanical activation instead of thermal activation is more economical and environmentally friendly method.
AtıfScopus5WoS4OpenAlex5İncele