- MakaleYalnız künye2025Scopus SJRQ1Mechanical, durability and microstructure properties of eco-friendly self-compacting mortars with addition of volcanic scoria, silica fume and boron waste as cement replacement
Şahin Yön, Merve
The objective of this experimental study is to investigate the mechanical and durability performances of self-compacting mortars containing industrial waste and natural stone to develop an environmentally friendly mortar. Binary series of boron waste (B), silica fume (S) and volcanic scoria (V) were formed by substituting up to 95 % by weight with Portland cement, and ternary series were formed by substituting up to 80 % by weight with Portland cement. A total of 14 mixtures and one reference mixture (R) were improved for the purpose of investigating the workability, mechanical strength and durability properties of self-compacting mortar with different binder compositions. Samples of 40x40x160 mm were produced to evaluate mechanical properties and freeze-thaw effect, 100x100x100 mm for abrasion testing and 50x50x50 mm to determine physical properties. Additionally, SEM/EDS and XRD analyses were performed to determine the microstructural characteristics of the mixtures formed. The test results demonstrated that the sole replacement of boron waste with Portland cement resulted in enhanced fluidity. Nonetheless, the 90-day compressive strengths of the S10V20 and B5S10V5 mixtures exhibited increases of 7.47 % and 5.57 %, respectively, relative to the reference, whilst the B15 series saw a 52.5 % reduction, marking the lowest 90-day compressive strength compared to the reference sample. When the freeze-thaw effect was assessed after 136 cycles, the compressive strength diminished by 8.57 %, 13.1 %, 4.13 %, 7.28 %, 6.22 %, 24.77 %, and 48.1 % in the R, B5, V5, V10, V15, B5S10V5, B5S10V10, and B5S10V15 samples, respectively. Among the samples subjected to abrasion tests, a loss of 6.5 per thousand occurred in the mass of the reference sample at the end of 6 minutes, while a loss of 11 per thousand occurred in the binary mixture containing 5 % B, which had the highest abrasion.
AtıfScopus16WoS14OpenAlex16
İncele - MakaleYalnız künye2024Scopus SJRQ1Resistance to magnesium sulphate attack of binary and ternary cementless self-compacting alkali-activated mortar
Şahin Yön, Merve; Karataş, Mehmet
The aim of this study is to investigate the effect of sulphate on self-compacting alkali-activated mortars (SCAAMs) produced using volcanic scoria (V), boron waste (B) and granulated blast furnace slag (G) together with alkali activators. Thus, the production of cement-free alkali-active mortar by recycling waste and reducing the CO2 effect increases the importance of this study. The fact that the waste material is provided free of charge and that V is readily available from nature provides economic advantages in the production of these mortars. In this experimental study, magnesium sulphate solution was utilized to define the sulphate resistance of SCAAMs. In binary SCAAMs, B was used with G in a ratio of NS:NH = 3.0, with an increase from 5 % to 15 %; in ternary mixtures, B was used together with G and V in the same proportions, in a ratio of NS:NH = 1.0. The tests involved immersion in 5 % magnesium sulphate solution for 1, 3 and 6 months. Mass development, compressive strength, visual inspection and microstructural changes were investigated. In general, the binary SCAAMs performed better in magnesium sulphate solution than the ternary SCAAMs, except in the 6th month. Considering the samples with the highest B content, a 100 % loss of compressive strength occurred in the B15G85 sample under the influence of sulphate for 6 months, while a loss of compressive strength of about 15 % occurred in the B15G40V45 sample. The results showed that the increase in B content caused a severe deterioration of the sulphate effect in the samples over time and that the V additive had a positive effect on the sulphate resistance.
AtıfScopus26WoS23OpenAlex19İncele - MakaleYalnız künye2024Scopus SJRQ1Sustainable use of boron waste and volcanic scoria in slag-based self-compacting alkali-activated mortars: fresh, mechanical and durability properties
Yön, Merve Şahin; Yön, Burak; Karataş, Mehmet; Benli, Ahmet
Sustainable self-compacting alkali-activated concrete (SCAAC) manufacturing is an environmentally friendly concrete that has a reduced carbon footprint than ordinary concrete. Alkali-activated binders have been demonstrated in experiments to reduce concrete's energy consumption and carbon emissions by over 50%. This paper focuses on manufacturing boron waste (BW), volcanic scoria (VS) and ground blast furnace slag (GBFS) incorporated binary and ternary blends of self-compacting alkali-activated mortars (SCAAM). The main objective of this study is to investigate the fresh, mechanical, durability and microstructural properties of SCAAM based on binary and ternary mixtures of BW, VS, and GBFS. SCAAM samples were synthesized at 60 °C and 100 °C for 72 h then exposed to ambient cured at 3, 28 and 90 days. The compressive strength, flexural strength, physical, and sorptivity properties of the SCAAM mixtures, as well as flowability, were investigated. The performance of the produced blends at freeze-thaw exposure were also examined. SEM, and EDS was also used to examine the microstructures of the mixtures. The findings showed that 50% GBFS and 50%VS based SCAAM mixture heat cured at 100oC activated with NS/NH ratio of 3.0 produced a compressive strength of 40 MPa at 90 days. The findings indicated that inclusion of BW to the SCAAM mixtures decreased the compressive strength notably regardless of NS/NH ratio and curing temperature. Inclusion of BW also affected the durability performance negatively.
AtıfScopus38WoS36OpenAlex35İncele - MakaleAçık Erişim2022Scopus SJRQ1Evaluation of the mechanical properties and durability of self-compacting alkali-activated mortar made from boron waste and granulated blast furnace slag
Yön, Merve Şahin; Karataş, Mehmet
The production of high-strength alkali-activated mortar and concrete by using waste materials instead of cement in order to reduce the amount of carbon dioxide released to nature in cement production is an important study that attracts the attention of researchers. In this study, self-compacting alkali-activated mortar samples were produced using boron waste (BW) and granulated blast furnace slag (GBFS). Prismatic samples of 40 × 40 × 160 mm and cubes of 50 × 50 × 50 mm were produced, in which 0%, 5%, 10%, 15%, 20%, 25% of BW were used. To achieve self-compacting alkali-activated mortar (SCAAM) slump-flow test method was conducted by per The European Federation of Specialist Construction Chemicals and Concrete Systems (EFNARC) guidelines. The samples prepared using Na2SiO3 (NS)/NaOH (NH) = 3.0 were exposed to oven curing at 60 °C and 100 °C for 3 days. The flexural and compressive strength (CS) values of 3, 28 and 90 days were obtained for the samples whose curing period was completed. According to the mechanical strength results, influence of capillary water absorption, porosity, water absorption and density and freeze-thaw from durability tests were carried out. After experimental tests, Scanning Electron Microscope (SEM) and Energy-dispersive X-ray Spectroscopy (EDS) images were utilized to determine microstructures of the samples. As a result of the study, it was determined that the highest strengths were obtained at the curing temperature of 60 °C. Also, it was seen that mechanical strengths and durability decreased with the increase in the BW ratio in the mixtures.
AtıfScopus31WoS28OpenAlex33İncele