  Linking microstructural modifications of Ho2O3-doped borotellurite glasses to the enhancement of critical properties: Synthesis, structural, physical, and experimental Gamma-Ray and neutron transmissioncharacteristics

  Kilic, G.; Ilik, E.; Kavaz, E.; Durmus, Hasan; Güler, Ömer; Birdogan, Selcuk; ALMisned, Ghada; Tekin, H.O.

  This study investigates the effects of holmium oxide (Ho2O3) microparticle reinforcement on the structural, physical, and radiation shielding properties of borotellurite glasses with compositions ranging from 0 to 12 mol% Ho2O3. X-ray diffraction and TEM analyses confirmed the retention of amorphous structure across all samples, with localized short-range ordering observed at higher Ho contents. Glass density increased from 4.598 to 5.202 g/cm3 with increasing Ho2O3, while molar volume expanded from 27.94 to 30.61 cm3/mol, and oxygen packing density decreased from 0.605 to 0.551 g/cm3, indicating network expansion due to the substitution of lighter Li + ions by heavier Ho3+. Gamma-ray shielding properties significantly improved with Ho incorporation. At 81 keV, the linear attenuation coefficient increased from 8.33 to 13.70 cm−1, and the mass attenuation coefficient improved from 2.066 to 2.735 cm2/g. Moreover, effective atomic number rose from 44.9 to 52.5 and half-value layer decreased by 20.5% at 383 keV, and buildup factors dropped by up to 34% at 0.5 MeV. Neutron dose absorption improved, and the fast neutron removal cross-section increased from 0.1066 to 0.1113 cm−1. These results confirm that Ho2O3 contributes as a highly effective multifunctional dopant, significantly enhancing both gamma-ray and neutron shielding performance of borotellurite glasses, one of the most promising glass systems for advanced radiation protection applications.

  AtıfScopus1·OpenAlex1

  İncele
• MakaleYalnız künye2026Scopus SJRQ2/r/munzur/919
  Structural evolution and dual γ–neutron shielding performance of nano-Gd2O3 reinforced lithium borotellurite glasses

  Durmus, Hasan; Kilic, G.; Ilik, E.; Kavaz, E.; Güler, Ömer; Birdogan, Selcuk; ALMisned, Ghada; Tekin, H.O.

  This study investigates the structural, physical, and radiation-shielding properties of nano-Gd2O3-reinforced lithium borotellurite glasses with the composition 50TeO2-30B2O3-(20-x)Li2O-xGd2O3 (x= 0-10 mol %). X-ray diffraction and transmission electron microscopy confirmed the fully amorphous nature of the glasses and the homogeneous distribution of nanoscale Gd clusters. Density increased from 4.03 to 4.77 g/cm3, accompanied by compositional shifts, decreasing boron and increasing oxygen and tellurium contents, indicating enhanced structural compactness and electron density. Gamma-ray attenuation measurements revealed a 74 % increase in the linear attenuation coefficient from 8.33 to 14.53 cm−1 at 81 keV and a nearly 27 % reduction in the half-value layer from 1.21 to 0.89 cm. Effective atomic number values remained highest for Gd(n)10 across the photon energy range investigated. Experimental neutron dose measurements showed absorption improvements from 37.66 % to 51.91 %, while the effective removal cross-section increased from 0.1066 to 0.1096 cm−1, outperforming water, B4C, and graphite. Compared with the Gd-doped zinc borotellurite glasses reported in the literature, the present lithium-based system exhibited higher densification and superior dual γ-neutron attenuation. These results demonstrate that controlled nano-Gd2O3 integration into the lithium borotellurite matrix yields a stable, lead-free amorphous material with outstanding radiation-shielding efficiency for advanced photonic and nuclear applications.