- MakaleYayıncıda açık erişim2026Scopus SJRQ1Tailoring of Dy2O3-B4C hybrid-reinforcements in Fe-Co-Ni-Cr-W High-Entropy Alloy (HEA) matrix for correlating structural, mechanical, and experimental gamma-ray transmission behaviour
Özkul, İskender; Güler, Ömer; Camgoz, Berkay; ALMisned, Ghada; Yaprak, Gunseli; Tekin, H.O.; Durmus, Hasan
This study investigates the structural, mechanical, and experimental gamma-ray attenuation properties of Fe-Co-Ni-Cr-W high-entropy alloy (HEA) composites reinforced with varying concentrations of Dy2O3 and B4C. A series of samples (S0-S4) was synthesized via vacuum arc melting to evaluate the synergistic effects of rare-earth oxide and carbide additions on a stable multi-component matrix. Thermodynamic assessments confirmed that the base alloy aligns with solid-solution formation criteria (1.61R configurational entropy, Ω = 10.33), which was experimentally validated by XRD patterns revealing a consistent FCC crystal structure across all compositions. SEM-EDS mapping further verified the successful integration of reinforcements as discrete secondary phases within the HEA matrix. Mechanical characterization showed that ceramic incorporation significantly enhances the hardness of the monolithic HEA, with the hybrid-reinforced S3 sample achieving a peak value of 628 HV. This improvement is attributed to the combined effects of oxide dispersion strengthening and microstructural refinement induced by B4C. Experimental gamma-ray transmission tests, conducted using a high-purity germanium (HPGe) detector in the 276-383 keV energy range, demonstrated that the S3 configuration provides the most efficient shielding performance, characterized by the lowest transmission factors. Interestingly, the results suggest that beyond an optimal threshold, increased reinforcement loading, as seen in S4 sample, may lead to minor performance trade-offs due to phase distribution dynamics. The findings highlight that the development of multifunctional HEA-based shields requires a delicate balance between reinforcement volume fraction and microstructural homogeneity to maximize both structural and shielding efficiency.
AtıfOpenAlex1
İncele