- MakaleYalnız künye2023Scopus SJRQ2Effect of impactor nose form on the impact behavior of reinforced composite materials
Dogan, Sonay; Arman, Yusuf; Dogan, Akar
The goal of the present study is to investigate the influence of impactor shape on the low-velocity impact behavior of the composite panels manufactured with different reinforcement materials at the same thicknesses, experimentally. Kevlar, carbon, S-2 glass woven fabric and epoxy matrix have been used to manufacture thermoset composites with the vacuum-assisted resin infusion molding method. The Fractovis plus test machine with a 12.7 mm diameter hemispherical and two different conical impactor noses was used to perform impact tests. The effects of impactor shapes on the low-velocity impact behavior have been compared for 20 J, 40 J, and 60 J energy levels. Although at the same impact energy level, S-2 glass fiber-reinforced epoxy specimens have a higher perforation threshold than carbon and Kevlar fiber-reinforced epoxy. Because to achieve the same thickness, the number of S-2 glass layers was greater than the number of carbon and Kevlar layers. Additionally, the form of the impactor greatly influenced the perforation threshold.
AtıfScopus7WoS7OpenAlex6
İncele - MakaleAçık Erişim2021Scopus SJRQ1Thermoset powder coating wastes as filler in LDPE – Characterization of mechanical, thermal and morphological properties
Kismet, Yilmaz; Dogan, Akar; Wagner, Manfred H.
In this study, three different electrostatic powder coating wastes of thermoset structure were used as fillers for low-density polyethylene (LDPE). The mechanical, thermal, and morphological properties of these composites materials are reported. The thermoset powder coating wastes were hydrolyzed using water and alcohol, and then 10%, 20%, and 30% by weight of the deactivated wastes were mixed with LDPE, first in a mechanical dry mixer, and subsequently homogenized by melt compounding in an extruder at about 160 °C. Standard tensile test bars and plate-shaped samples were produced from these homogeneous compounds by injection molding. The effects of adding hydrolyzed powder coating wastes on the properties of LDPE were determined by mechanical, thermal, and morphological tests. Tensile strength and perforation threshold of the sample filled with powder coating wastes decreased to some extent compared to un-filled sample. However, an increase in izod impact and bending strengths has been observed. The results of this investigation demonstrate that powder coating wastes with thermoset structure can be used as fillers in LDPE.
AtıfScopus13WoS15OpenAlex16İncele