- MakaleAçık Erişim2023Scopus SJRQ3Evaluation of waste polyethylene terephalate in polyol and polyurethane production
Fırat, Tülay; Kar, Filiz
As technology advances and human population grows, we must meet our diverse needs while minimising harm to the environment. One solution is to prioritise recycling and using second-hand consumer goods. In this study, PET flakes were depolymerised by glycolysis using different molar ratios of glycol such as propylene glycol(PG), triethylene glycol(TEG) and polyethylene glycol(PEG 400) in the presence of two different catalysts: zinc acetate- zinc sulphate. As a result, glycated products (polyols-PO) were obtained. The obtained polyols were then used to synthesise polyurethane films (PU) via acetone process. The thermal and chemical characterisations of the polyurethane films (PU) were analysed. In similar studies, zinc acetate was used as a transesterification catalyst for the glycolysis process. In this study, the same process was carried out using zinc sulphate and zinc acetate. Zinc sulphate was found to be a cheaper and eco-friendlier catalyst alternative to zinc acetate for the glycolysis process.
AtıfOpenAlex1
İncele - MakaleAçık Erişim2021Scopus SJRQ1Investigation on the properties of new palm-oil-based polyurethane modified bitumen
Vural Kök, Baha; Aydoğmuş, Ercan; Yilmaz, Mehmet; Akpolat, Mustafa
Polyurethane-derived polymer synthesized by the reaction of 4.4′-diphenylmethane diisocyanate (MDI) with the new modified palm-oil-based polyol was used as an alternative additive to thermoplastic-elastomers, such as styrene–butadienestyrene (SBS), the most commonly used additive. The study aimed to investigate the effect of polyurethane (PU) modification on the rheological and chemical structure of base bitumen. The softening point, rotational viscosity, dynamic shear rheometer (DSR), multi-stress creep recovery (MSCR), bending beam rheometer (BBR), and Fourier transform infrared (FTIR) tests were conducted on the binders. The effects of curing time and temperature, isocyanate/hydroxyl (NCO/OH) molar ratio, and PU content were examined and the best modification conditions were determined. It was found that 24 h curing conditions at 85 °C were sufficient for the formation of PU bonds and these processes increased the rutting parameter of the binder by 256% compared to 1 h curing. At 50 °C and a frequency of 5 Hz, the binder with a 4:1 NCO/OH ratio had 63% more complex modulus than the binder with a 10:1 NCO/OH ratio. The 7 wt% PU modified binder had the same performance level as 4% SBS modification and 10 wt% PU modified binder was one degree higher. Moreover, above 60 °C, all the PU modified binders gave lower phase angles compared to the 4% SBS modified binder. 7 wt% PU modified binder showed similar elastic properties against cracks at low temperatures compared to the 4% SBS modified binder. The use of palm oil in the synthesis of PU presents an environmentally friendly and cost-effective solution compared to the use of petrochemical derivatives.
AtıfScopus56WoS53OpenAlex60İncele