Sürdürülebilir Kalkınma Amaçları
Yazarlar
Yayınlar
- MakaleYalnız künye2024Scopus SJRQ1Sustainable use of boron waste and volcanic scoria in slag-based self-compacting alkali-activated mortars: fresh, mechanical and durability properties
Yön, Merve Şahin; Yön, Burak; Karataş, Mehmet; Benli, Ahmet
Sustainable self-compacting alkali-activated concrete (SCAAC) manufacturing is an environmentally friendly concrete that has a reduced carbon footprint than ordinary concrete. Alkali-activated binders have been demonstrated in experiments to reduce concrete's energy consumption and carbon emissions by over 50%. This paper focuses on manufacturing boron waste (BW), volcanic scoria (VS) and ground blast furnace slag (GBFS) incorporated binary and ternary blends of self-compacting alkali-activated mortars (SCAAM). The main objective of this study is to investigate the fresh, mechanical, durability and microstructural properties of SCAAM based on binary and ternary mixtures of BW, VS, and GBFS. SCAAM samples were synthesized at 60 °C and 100 °C for 72 h then exposed to ambient cured at 3, 28 and 90 days. The compressive strength, flexural strength, physical, and sorptivity properties of the SCAAM mixtures, as well as flowability, were investigated. The performance of the produced blends at freeze-thaw exposure were also examined. SEM, and EDS was also used to examine the microstructures of the mixtures. The findings showed that 50% GBFS and 50%VS based SCAAM mixture heat cured at 100oC activated with NS/NH ratio of 3.0 produced a compressive strength of 40 MPa at 90 days. The findings indicated that inclusion of BW to the SCAAM mixtures decreased the compressive strength notably regardless of NS/NH ratio and curing temperature. Inclusion of BW also affected the durability performance negatively.
AtıfScopus38WoS36OpenAlex35
İncele - MakaleAçık Erişim2022Scopus SJRQ1Evaluation of the mechanical properties and durability of self-compacting alkali-activated mortar made from boron waste and granulated blast furnace slag
Yön, Merve Şahin; Karataş, Mehmet
The production of high-strength alkali-activated mortar and concrete by using waste materials instead of cement in order to reduce the amount of carbon dioxide released to nature in cement production is an important study that attracts the attention of researchers. In this study, self-compacting alkali-activated mortar samples were produced using boron waste (BW) and granulated blast furnace slag (GBFS). Prismatic samples of 40 × 40 × 160 mm and cubes of 50 × 50 × 50 mm were produced, in which 0%, 5%, 10%, 15%, 20%, 25% of BW were used. To achieve self-compacting alkali-activated mortar (SCAAM) slump-flow test method was conducted by per The European Federation of Specialist Construction Chemicals and Concrete Systems (EFNARC) guidelines. The samples prepared using Na2SiO3 (NS)/NaOH (NH) = 3.0 were exposed to oven curing at 60 °C and 100 °C for 3 days. The flexural and compressive strength (CS) values of 3, 28 and 90 days were obtained for the samples whose curing period was completed. According to the mechanical strength results, influence of capillary water absorption, porosity, water absorption and density and freeze-thaw from durability tests were carried out. After experimental tests, Scanning Electron Microscope (SEM) and Energy-dispersive X-ray Spectroscopy (EDS) images were utilized to determine microstructures of the samples. As a result of the study, it was determined that the highest strengths were obtained at the curing temperature of 60 °C. Also, it was seen that mechanical strengths and durability decreased with the increase in the BW ratio in the mixtures.
AtıfScopus31WoS28OpenAlex33İncele