  Design, structural characterization, and simulated radiation-transport assessment of high-entropy (GdErSmEuYb)2X2O7 (X = Hf, Zr, Ce, Si) rare-earth oxides

  Güler, Ömer; Güler, Seval Hale; Yayla, Nihal; Baykal, Duygu Sen; Durmus, Hasan; Tekin, Huseyin Ozan; ALMisned, Ghada

  This study investigates the structural, microstructural, surface-chemical, and radiation attenuation behaviour of high-entropy rare-earth oxide (HEO) powder compositions synthesized as TBC-related candidate coating materials, whose radiation attenuation potential was assessed within a computational Inconel-718-based sandwich model. Four compositions, namely (GdErSmEuYb)2Hf2O7, (GdErSmEuYb)2Ce2O7, (GdErSmEuYb)2Zr2O7, and (GdErSmEuYb)2Si2O7, were synthesized via high-energy ball milling followed by calcination at 1200 °C. X-ray diffraction results revealed the formation of distinct crystal structures depending on B-site chemistry, including defective fluorite and silicate-type phases. SEM-EDS mapping confirmed homogeneous elemental distribution, while XPS analysis demonstrated mixed valence states and different oxygen vacancy concentrations across the compositions. To evaluate radiation attenuation performance, a sandwich-type geometry consisting of a 10 mm Inconel-718 core with symmetrically defined simulated HEO layers was modelled using Monte Carlo simulations. Gamma-ray transmission was analyzed over an energy range of 0.276-1.332 MeV, and fast neutron attenuation was assessed at 4.5 MeV. The results showed that transmission factors decreased with increasing coating thickness, with the effect being more pronounced at lower photon energies. Among the investigated compositions, the Hf-based system exhibited the most favorable predicted attenuation response for both gamma rays and fast neutrons under the defined simulation conditions. Theoretical half-value layer calculations also showed good agreement with the simulation results. Overall, the findings indicate that high-entropy rare-earth oxide coatings may provide an additional radiation attenuation contribution when incorporated as layers in Inconel-718-based systems. However, since direct thermal-barrier properties such as thermal conductivity, thermal diffusivity, thermal cycling resistance, and thermal-stress behavior were not evaluated in the present work, the present study should be interpreted as a structural and radiation-transport assessment of TBC-related coating candidates rather than a direct demonstration of thermal-barrier performance.

  İncele
• MakaleAçık Erişim2026Scopus SJRQ2/r/munzur/1433
  Design and Characterization of Y2O3/Pr2O3–Enriched Inconel-718 Alloys for Nuclear Applications

  Albayrak, Muhammet Gökhan; Güler, Ömer; Güler, Seval Hale; Evin, Ertan; ALMisned, Ghada; Sen Baykal, Duygu; Alkarrani, Hessa; Susoy, Gulfem; Kilic, Gokhan; Tekin, Hüseyin Ozan

  This study explores the physical, structural, and radiation shielding enhancements in Inconel 718 superalloys reinforced with 1 wt% Y2O3 and varying Pr2O3 contents from 0 to 10 wt%, respectively. X-ray diffraction analysis confirmed preservation of the face-centered cubic structure, with increasing Pr2O3 inducing peak broadening and partial amorphization. The scanning electron microscopy/energy-dispersive X-ray spectroscopy results verified the homogeneous dispersion of oxides without agglomeration. Gamma-ray shielding parameters, including the mass attenuation coefficient (MAC), half-value layer, and effective atomic number, significantly improved with higher Pr2O3 content, particularly at low to mid photon energies. The 718Y-10PO sample exhibited the lowest transmission factors and the highest MAC values across all the tested energies. Buildup factors decreased in the Pr-rich samples, confirming reduced photon scattering. Notably, the fast neutron removal cross section for 718Y-10PO as 0.15521 cm−1 exceeded the benchmark materials like graphite and B4C. These findings establish the 718Y-10PO alloy as a promising candidate for advanced nuclear shielding applications, combining structural integrity with promising gamma and neutron attenuation capabilities.

  İncele
• MakaleYalnız künye2026Scopus SJRQ2/r/munzur/1432
  Synthesis, structural characterization, and radiation interaction behaviour of (ErSmGdYPr)2Hf2O7 high-entropy oxide powder: A preliminary investigation for potential applications in nuclear environments

  Güler, Ömer; Güler, Seval Hale; Özkul, İskender; ALMisned, Ghada; Baykal, Duygu Sen; Tekin, Huseyin Ozan

  This study represents an initial investigation toward exploring the multifunctional potential of the (ErSmGdYPr)2Hf2O7 high-entropy oxide as a thermal barrier coating (TBC) material in radiation environments. Therefore, the evaluated parameters should be considered as a preliminary step rather than a complete representation of the material’s overall performance in such complex applications. In this context, (ErSmGdYPr)₂Hf2O7 powders were synthesized through high-energy ball milling of commercial rare-earth oxide precursors followed by calcination at different temperatures. Structural evolution during synthesis was investigated using X-ray diffraction, scanning electron microscopy with energy-dispersive spectroscopy, and thermal analysis techniques. The results confirmed the formation of a defective fluorite-type high-entropy oxide structure after calcination at elevated temperatures, accompanied by homogeneous elemental distribution and stable ceramic microstructures. In addition to structural characterization, the radiation interaction behaviour of the synthesized material was evaluated through gamma-ray attenuation parameters and fast neutron removal cross-section analysis. The obtained results indicate that the presence of multiple rare-earth elements provides favorable interaction characteristics with both photons and fast neutrons. These findings highlight the potential of this high-entropy oxide as a precursor for multifunctional coating materials. However, it should be noted that this work represents a preliminary powder-level investigation, and further research on actual coating deposition and thermal testing is required to validate its service performance.

  İncele
• MakaleYalnız künye2026Scopus SJRQ2/r/munzur/1422
  Compositional control of structural, magnetic, and gamma-ray attenuation properties in rare-earth substituted Ho-based double perovskite oxides synthesized via mechanical alloying and oxidation

  Özkul, İskender; Kalay, Ece; Güler, Seval Hale; Karaduman, Oktay; Şimşek, Telem; Bülbül, Zeynel Abidin; Aksu Canbay, Canan; Sen Baykal, Duygu; ALMisned, Ghada; Tekin, H.O.

  Rare-earth substitution provides a route for tailoring the structural, magnetic, and gamma-ray attenuation behaviour of Ho-based Co-Mn double perovskites; however, the combined effects of rare-earth ionic size, magnetic character, and substitution level remain insufficiently understood. In this study, Ho1.5La0.5CoMnO6, Ho1.2Er0.8CoMnO6, Ho1.3Sm0.7CoMnO6, and Ho2CoMnO6 were synthesized through a two-step route involving mechanical alloying to obtain precursor powders, followed by annealing at 1000 °C in air to promote oxidation and double-perovskite phase formation. Their structural, thermal, surface-chemical, magnetic, and gamma-ray attenuation properties were examined by X-ray diffraction, thermal analysis, X-ray photoelectron spectroscopy, SEM-EDS, vibrating-sample magnetometry, and theoretical shielding calculations based on half-value layer (HVL) and transmission factor (TF) parameters. The XRD patterns were consistent with predominantly monoclinic P21/n type double-perovskite structures, while weak additional reflections suggested possible minor secondary phases. SEM-EDS showed homogeneous elemental distributions, and XPS analysis indicated Co2+ dominated and mixed Mn-valence characteristics in the spectra where reliable component analysis was possible. All compositions exhibited a low-temperature ferromagnetic-like field response but did not reach magnetic saturation at 3 T. Ho2CoMnO6 and Ho1.3Sm0.7CoMnO6 showed the highest field-dependent magnetization values at 10 K, whereas Ho1.2Er0.8CoMnO6 displayed the lowest response. The theoretical gamma-ray attenuation calculations showed clear composition-dependent differences. At 0.662 MeV, the HVL values were 1.0650, 0.9972, 1.0438, and 0.9967 cm for Ho1.5La0.5CoMnO6, Ho1.2Er0.8CoMnO6, Ho1.3Sm0.7CoMnO6, and Ho2CoMnO6, respectively. At the same photon energy and a thickness of 1.0 cm, the corresponding TF values were 0.0896, 0.0858, 0.0882, and 0.0860. Thus, Ho1.2Er0.8CoMnO6 and Ho2CoMnO6 exhibited the lowest HVL and TF values among the investigated compositions. The shielding calculations identified Ho1.2Er0.8CoMnO6 and Ho2CoMnO6 as the most effective attenuators, with lower HVL and TF values across the investigated energy range. These results show that rare-earth substitution enables compositional tuning of magnetic and theoretical gamma-ray attenuation behaviour, with the observed trends reflecting the combined influence of rare-earth ionic size, magnetic character, substitution level, and valence-state complexity.

  İncele
• MakaleYalnız künye2026Scopus SJRQ1/r/munzur/1321
  Engineering Ti-Zr-Hf high-entropy alloys (HEA) with rare-earth and boron additives for microstructure-controlled mixed-field radiation shielding: Fabrication, physical, structural and experimental γ-ray & fast-n shielding properties

  Özkul, İskender; Güler, Ömer; Kavaz, E.; Kalay, Ece; Güler, Seval Hale; ALMisned, Ghada; Tekin, H.O.

  This study investigates three newly designed Ti-Zr-Hf-based high-entropy alloys such as TiZrHfGdSm (N1), TiZrHfEr (N2), and TiZrHfGdEuB (N3), with the aim of understanding how selected rare-earth and boron additions influence microstructural evolution and dual γ-ray/fast-neutron shielding performance. All alloys were synthesized by arc melting and evaluated through thermodynamic modelling, X-ray diffraction, scanning electron microscopy with elemental mapping, and mixed-field attenuation measurements. The results show that each composition forms an HCP-type solid-solution matrix with composition-dependent lattice distortion and secondary phase formation. Among the studied systems, the Er-modified alloy N2 develops the most spatially uniform elemental distribution and demonstrates the most balanced combination of γ-ray attenuation, effective atomic number, buildup behaviour, and fast-neutron removal efficiency. N1 and N3, containing multiple rare-earth elements and, in the case of N3, boron-induced borides, exhibit distinct grain features and provide valuable insights into how multi-element additions shape photon and neutron interaction pathways. Comparative examination confirms that shielding performance in these HEAs is governed by the interplay of elemental cross sections, density, and microstructural uniformity. The findings highlight Ti-Zr-Hf-RE(B) alloys as promising platforms for multifunctional radiation-shielding materials and provide a compositional framework for future optimization in nuclear, medical, and aerospace applications.

  AtıfScopus2·OpenAlex2

  İncele
• MakaleYalnız künye2026Scopus SJRQ2/r/munzur/967
  Manufacturing, Structural Characterization, and Radiation Interaction Evaluation of Lightweight 6061-Al/Ytterbium(III) Oxide Composites with Emphasis on Gamma-Ray Shielding and Fast Neutron Removal Potential

  Guler, Seval Hale; Yayla, Nihal; Guler, Omer; ALMisned, Ghada; Sen Baykal, Duygu; Kilic, Gokhan; Tekin, Huseyin Ozan

  In this study, 6061-aluminum metal matrix composites doped with varying concentrations of ytterbium(III) oxide were synthesized using high-energy mechanical alloying to evaluate their structural, physical, and radiation shielding properties. X-ray diffraction confirmed the retention of the aluminum crystal structure with no secondary phase formation, while scanning electron microscopy and energy-dispersive X-ray spectroscopy revealed homogenous dispersion of Yb2O3 particles within the matrix. With increasing Yb2O3 content, particle densification and structural integrity were significantly enhanced. Gamma-ray and neutron shielding performance was assessed through theoretical modeling and Monte Carlo simulations. At low photon energy, the 20 wt% Yb2O3 composites showed a remarkable increase in linear attenuation coefficients compared to the undoped 6061-aluminum matrix. Neutron removal efficiency also increased by 32% at the highest Yb2O3 content. It can be concluded that Yb2O3 incorporation significantly improves both the photon and neutron shielding performance of the 6061-aluminum metal matrix.

  İncele
• MakaleAçık Erişim2026Scopus SJRQ1/r/munzur/909
  Comparative and systematically analysis of the effects of single and high-entropy rare earth oxide additives on the some physical properties and radiation shielding properties of copper composites

  Kanca, Muhammed Sait; Yılmaz, Demet; Tasgın, Yahya; Kök, Mediha; Güler, Seval Hale

  In this study, the effects of rare earth oxides (Gd₂O₃, La₂O₃, Eu₂O₃, Pr₂O₃, Dy₂O₃, and Y₂O₃) and high-entropy oxide (GdLaEuPrDyY)₂O₃ additives on the structural, mechanical, and radiation shielding properties of copper matrix composites were investigated. XRD and SEM-EDS analyses showed that the high-entropy oxide successfully formed in a single-phase bixbyite structure after mechanical alloying and was homogeneously distributed within the copper matrix. The rare earth oxide additive significantly reduced the crystal grain size of the Cu matrix and improved its mechanical properties. Specifically, the microhardness value reached 68.3 Hv in the composite with 20% high-entropy oxide additive, representing an increase of approximately 111% compared to pure copper (32.3 Hv). Gamma shielding results showed that the rare earth oxide additive significantly increased the photon attenuation capacity. Specifically, at 242 keV energy, the Dy₂O₃ additive increased the MAC value from 0.141 cm²/g to 0.246 cm²/g, providing a 74.5% improvement. The most important result is that the composite with 20% high-entropy oxide additive showed the highest shielding performance, achieving a MAC value of 0.278 cm²/g, which is significantly superior to pure copper. Furthermore, this composite exhibited the lowest HVL and MFP values, demonstrating the highest photon shielding efficiency. Neutron shielding analyses revealed that Gd₂O₃ and high-entropy oxide additives, in particular, increased thermal neutron attenuation performance to approximately 100%. These results demonstrate that high-entropy oxide additives provide a stronger impact compared to single oxide additives, offering superior performance in both gamma and neutron shielding. Consequently, copper composites doped with (GdLaEuPrDyY)₂O₃ stand out as promising alternative shielding materials for nuclear facilities, radiation protection systems, and advanced engineering applications due to their high shielding efficiency, improved mechanical properties, and non-toxic composition.

  AtıfScopus1·OpenAlex1

  İncele
• MakaleAçık Erişim2026Scopus SJRQ2/r/munzur/875
  Physical and gamma-ray shielding characteristics of Copper Matrix Refractory High Entropy Alloy Reinforced Composite: an extensive experimental and computational approach

  Kuluöztürk, Zehra Nur; Kuluöztürk, Muhammed Fatih; Güler, Seval Hale; Doğru, Mahmut; Güler, Ömer

  Refractory High Entropy Alloys (RHEAs) have become an attractive alternative for radiation shielding applications due to their high mechanical strength, thermal resistance, structural stability, and compositional diversity. In this study, Cu-based composites containing 0–20 wt% RHEAs were prepared, and the crystal structure, morphological properties, and radiation shielding performance of the synthesized Cu-RHEA were investigated experimentally and theoretically. Measurements were performed using a NaI(Tl) detector system with point sources of 133Ba, 137Cs, 22Na and 60Co emitting gamma energies in the range of 0.356–1.333 MeV. In addition, theoretical calculations were carried out using the FLUKA and Phy-X/PSD, showing good agreement with the experimental data. Linear attenuation coefficient (LAC) values were found to decrease with increasing photon energy and to increase with increasing RHEA content. In the 0.356–1.333 MeV energy range, the experimental LAC values ranged from 0.7599 to 0.3818 cm−1 for Cu-RHEA0 and from 0.9594 to 0.4221 cm−1 for Cu-RHEA20. At 0.662 MeV, the LAC value increased from 0.5426 cm−1 for Cu-RHEA0 to 0.6183 cm−1 for Cu-RHEA20. In terms of half-value layer (HVL), the Cu-RHEA20 sample exhibited a value of 0.729 cm at 0.356 MeV, approximately 20% lower than the 0.912 cm value of Cu-RHEA0. Compared with conventional shielding materials reported in the literature, the Cu-RHEA20 sample reached a maximum mass attenuation coefficient (MAC) of 76.279 cm2⋅g−1 at 0.015 MeV, demonstrating clear superiority over ordinary concrete with a value of 7.079 cm2⋅g−1. These findings demonstrate that increasing RHEA content improves gamma-ray attenuation performance, highlighting Cu-RHEA20 as a promising next-generation shielding material.

  İncele
• MakaleYalnız künye2026Scopus SJRQ2/r/munzur/861
  Correlative Investigation on physical, microstructure, magnetism, and gamma-neutron attenuation properties of mechanically alloyed multifunctional (Fe/Co/Ni)Nb10V10B10 soft magnetic alloy systems

  Simsek, Tuncay; Simsek, Telem; Chattopadhyay, Arun K.; Avar, Barış; Yakin, Alican; Guler, Seval Hale; Almisned, Ghada; Sen Baykal, Duygu; Tekin, H.O.

  In this study, mechanically alloyed Fe70Nb10V10B10, Co70Nb10V10B10, Ni70Nb10V10B10, and (FeCoNi) 70Nb10V10B10 high-entropy alloys were successfully synthesized, and their structural, magnetic, and radiation shielding properties were systematically investigated. Structural analysis revealed that Fe favored bcc phase formation, while Co and Ni stabilized fcc structures; the equiatomic alloy resulted in a single-phase fcc solid solution with the smallest crystallite size (2.1 nm). All samples exhibited soft ferromagnetic behavior, with the Fe-based alloy achieving the highest saturation magnetization (120 emu/g), and the (FeCoNi) 70Nb10V10B10 alloy displaying the lowest coercivity. Among all compositions, Co70Nb10V10B10 demonstrated the best gamma and neutron shielding performance, showing the highest linear attenuation coefficient and fast neutron removal cross-section. The equiatomic alloy also exhibited well-balanced and stable shielding behavior. These findings position Co70Nb10V10B10 as a promising candidate for multifunctional applications requiring both efficient radiation protection and favorable magnetic properties.

  AtıfScopus1

  İncele
• MakaleYalnız künye2026Scopus SJRQ1/r/munzur/818
  Thermodynamic assessment of an equiatomic FeNiCoCrMn precursor for a spinel high-entropy oxide produced via mechano-oxidation with structure–radiation interaction correlation

  Güler, Ömer; Güler, Seval Hale; Özkul, İskender; ALMisned, Ghada; Sen Baykal, Duygu; Tekin, H.O.

  Spinel high-entropy oxides (HEOs) can stabilize multiple transition-metal cations within a single lattice, yet their radiation-interaction behavior is scarcely explored. Here, a (FeNiCoCrMn)3O4 spinel HEO was produced via an alloy-to-oxide route: 40 h mechanical alloying of equiatomic FeNiCoCrMn powders followed by mechano-oxidation (1000 °C/3 h) and high-energy grinding. HEA-derived thermodynamic metrics were used to rationalize the stability of the equiatomic metallic precursor prior to mechano-oxidation, rather than to directly predict the formation of the final oxide phase. XRD evidenced progressive amorphization of the HEA and its conversion to a crystalline spinel oxide, while SEM–EDS confirmed homogeneous elemental distribution. XPS indicated a defect-rich, multivalent surface (Co2+/Co3+, Cr3+/Cr6+, Fe3+, mixed Mn states, Ni2+) with lattice oxygen and vacancy-related components. Moreover, the spinel oxide showed higher linear attenuation coefficients than 316L stainless steel, Inconel-718, and several lightweight Al-based entropy alloys, yielding lower HVL values, especially at low energies. Zeff exhibited the expected energy dependence and exceeded Al-dominant alloys across the spectrum. EBF/EABF at 1 and 40 mfp displayed Compton-region peaks and strong depth effects, consistent with attenuation behavior. It can be concluded that a (FeNiCoCrMn)3O4 spinel high-entropy oxide, produced via an alloy-to-oxide transformation route, exhibits structurally stable and compositionally homogeneous characteristics together with favorable gamma-ray attenuation behavior.