Ozkaya, Serdar; Çelebi, Müslim; Yanar, Harun; Karabacak, Abdullah Hasan; Çelik, Ertuğrul; Güler, Onur; Coskun, Abdulkadir; Sekban, Dursun Murat

Cu-based hybrid composites reinforced with AlCrFeCuNi high-entropy alloy (HEA) particles and graphene were successfully fabricated by spark plasma sintering (SPS) to investigate the combined effects of microstructure, mechanical properties, and tribological performance under electrical current. Microstructural observations revealed a dense and homogeneous distribution of HEA particles within the Cu matrix, while the addition of 2.0 wt.% graphene promoted noticeable grain refinement due to its grain boundary pinning effect. Although graphene addition provided beneficial effects in terms of grain refinement and electrical conductivity, it also increased the porosity from 2.49% to 5.08%. Consequently, the beneficial contribution of graphene to mechanical strengthening was substantially offset by the adverse effect of increased porosity, resulting in only a marginal increase in hardness from 127 HB to 129 HB. The addition of 2.0 wt.% graphene led to a pronounced change in the tribological behavior of the composites. The Cu–HEA exhibited relatively stable friction behavior but experienced a higher wear rate under all test conditions. In comparison, the Cu–HEA–2.0 Gr composite demonstrated a lower coefficient of friction and wear rate at 0–10 A, which is consistent with the possible formation of a graphene-rich lubricating surface layer. A clear transition occurred at 30 A, where the coefficient of friction and wear rate began to increase, while at 50 A, further increases in both parameters were observed, suggesting progressive disruption of the proposed protective surface layer under the investigated current-carrying sliding conditions.

İncele

Güler, Ömer; Boyrazlı, Mustafa; Albayrak, Muhammet Gökhan; Güler, Seval Hale; Ishihara, Tatsumi; Edalati, Kaveh

One of the most promising solutions to slow down CO2 emissions is the use of photocatalysis to produce hydrogen as a clean fuel. However, the efficiency of the photocatalysts is not at the desired level, and they usually need precious metal co-catalysts for reactions. In this study, to achieve efficient photocatalytic hydrogen production, a high-entropy oxide was synthesized by a mechano-thermal method. The synthesized high-entropy oxide had a bandgap of 2.45 eV, which coincided with both UV and visible light regions. The material could successfully produce hydrogen from water under light, but the main difference to conventional photocatalysts was that the photocatalysis proceeded without a co-catalyst addition. Hydrogen production increased with increasing time, and at the end of the 3 h period, 134.76 µmol/m2 h of hydrogen was produced. These findings not only introduce a new method for producing high-entropy photocatalysts but also confirm the high potential of high-entropy photocatalysts for hydrogen production without the need for precious metal co-catalysts.

AtıfScopus33·WoS30