Simsek, Tuncay; Simsek, Telem; Chattopadhyay, Arun K.; Avar, Barış; Yakin, Alican; Guler, Seval Hale; Almisned, Ghada; Sen Baykal, Duygu; Tekin, H.O.

In this study, mechanically alloyed Fe70Nb10V10B10, Co70Nb10V10B10, Ni70Nb10V10B10, and (FeCoNi) 70Nb10V10B10 high-entropy alloys were successfully synthesized, and their structural, magnetic, and radiation shielding properties were systematically investigated. Structural analysis revealed that Fe favored bcc phase formation, while Co and Ni stabilized fcc structures; the equiatomic alloy resulted in a single-phase fcc solid solution with the smallest crystallite size (2.1 nm). All samples exhibited soft ferromagnetic behavior, with the Fe-based alloy achieving the highest saturation magnetization (120 emu/g), and the (FeCoNi) 70Nb10V10B10 alloy displaying the lowest coercivity. Among all compositions, Co70Nb10V10B10 demonstrated the best gamma and neutron shielding performance, showing the highest linear attenuation coefficient and fast neutron removal cross-section. The equiatomic alloy also exhibited well-balanced and stable shielding behavior. These findings position Co70Nb10V10B10 as a promising candidate for multifunctional applications requiring both efficient radiation protection and favorable magnetic properties.

AtıfScopus1

İncele

Şimşek, Telem; Kavaz, Esra; Güler, Ömer; Şimşek, Tuncay; Avar, Barış; Aslan, Naim; Almisned, Ghada; Zakaly, Hesham M.H.; Tekin, H.O.

We report the synthesis and structural, magnetic and Radiation shielding properties of High Entropy Alloy (HEA) produced through mechanical alloying method. Using an X-Ray Diffractometer (PanalyticalEmpryan) with CuK radiation at 45 kV and 40 mA, the phase identification starting elements and as-milled powders are identified. Scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDX), morphological and microstructural investigations were conducted (FEI Quanta FEG 450). EDX and elemental mapping analyses are conducted to assess the purity and elemental distributions of the synthesized alloys. Using the Quantum Design Physical Characteristics Measurement System (PPMS) with vibrating sample magnetometer (VSM) and a magnetic field of 30 kOe at room temperature, magnetic properties are examined. Using 137Cs radioisotope and mathematical methods, gamma-ray and neutron shielding properties of HEA are investigated in a conventional transmission setup using experimental and theoretical approaches. In the presence of a 3 T applied field, the sample exhibits a low magnetization of 5.30 emu/g at 300 K. Moreover, Ms is raised to 22 emu/g at 10 K owing to decreased thermal effects. The temperature dependence of the magnetization is recorded in the presence of a 1 T applied field. HEA exhibits superior neutron attenuation properties than conventional absorption materials such as B4C, graphite, and water. Our results showed that the synthesized HEA has superiority over other alloys and conventional neutron absorption materials. It can be concluded that the proposed novel HEA might be investigated further in terms of broadening its characterization and clarifying its other crucial properties to extend the scope of the current investigation.

AtıfScopus42·OpenAlex47

İncele

Şimşek, Telem; Özkul, İskender; Canbay, Canan Aksu; Avar, Barış; Şimşek, Tuncay; Güler, Seval Hale; Özcan, Sadan; Güler, Ömer; Chattopadhyay, Arun K.

In this study structural, morphological, thermal and magnetic properties of equiatomic CoNiMnGaSi (base), CoNiMnGaSiCu, CoNiMnGaSiSn and CoNiMnGaSiSb alloys are discussed. The formation of solid-solution nanocrystalline bcc structure of the alloys was determined by XRD and DTA techniques. SEM–EDS analyses also revealed the homogeneous distribution of the elements. The room temperature magnetic hysteresis loops showed that as-casted alloys reached saturation easily with coercivity less than or equal to 35 Oe. As the Cu and Sn were added to the alloy, the saturation magnetization was decreased from 112 emu/g to 50 emu/g, which was mainly due to the substitution of non-magnetic atoms to the magnetic Co in the base CoNiMnGaSi alloy, whereas the addition of Sb to the base alloy did not have a significant effect on the Ms. The CoNiMnGaSiSb was found to have the highest Curie Temperature of 670 K, which makes the alloy a promising candidate for power industry-related applications.

AtıfScopus3·OpenAlex4