- MakaleAçık Erişim2025Scopus SJRQ2Comprehensive evaluation of thermal, structural, magnetic, and radiation shielding properties of CuAlNi and CuAlNi-X (X = Co, CoFe, CoFeMn, CoFeMnCr) high-temperature shape memory alloys
Özkul, İskender; Karaduman, Oktay; Şimşek, Telem; Şimşek, Tuncay; Canbay, Canan Aksu; Güler, Ömer; Şan, Mert Hüseyin; ALMisned, Ghada; Tekin, H.O.
This study investigates the thermal, structural, magnetic, and radiation shielding properties of CuAlNi-based high-temperature shape memory alloys (HTSMAs) enhanced through sequential alloying with Co, Fe, Mn, and Cr. Five different variants were produced, designated as CRef (reference CuAlNi alloy), CCo (CuAlNiCo), CFe (CuAlNiCoFe), CMn (CuAlNiCoFeMn), and CCr (CuAlNiCoFeMnCr). Differential scanning calorimetry (DSC) confirmed the presence of reversible martensitic transformations in all alloys, with Co and Mn additions significantly enhancing thermal stability. Structural analyses using X-ray diffraction (XRD) and microscopy showed significant grain refinement and phase transitions, while magnetic measurements highlighted the strong ferromagnetic response of CCo (CuAlNiCo) and the increased coercivity of CMn (CuAlNiCoFeMn) due to domain-pinning effects. Moreover, radiation shielding analyses demonstrated the critical influence of density and elemental composition, with CRef exhibiting superior linear attenuation coefficients (LAC), effective atomic number (Zeff), and energy absorption buildup factor (EBF) performance, attributed to its optimized Cu fraction and high density (7.1296 g/cm3). In contrast, CMn (CuAlNiCoFeMn) showed the weakest shielding properties due to reduced density and Mn content. Among the samples, CRef emerged as the superior alloy, demonstrating exceptional multifunctionality across all evaluated parameters, while CCr (CuAlNiCoFeMnCr) displayed synergistic properties, combining shape memory behavior with competitive shielding efficiency. It can be concluded that CuAlNi-based HTSMAs hold significant potential as multifunctional materials, particularly for nuclear safety and aerospace engineering applications, where adaptive functionality and radiation protection are critical.
AtıfScopus2OpenAlex2
İncele - MakaleAçık Erişim2025Scopus SJRQ2A Novel CuAlMnFe/CeO2 Composite Alloy: Investigating the Wear and Corrosion Features
Doğan, Fatih; Duru, Erhan
Shape memory alloys (SMAs) are known for their exceptional mechanical properties, particularly their superior wear resistance compared to conventional alloys with similar surface hardness. Rare earth oxides are often used as additives to further improve these characteristics. This study investigates the effects of different CeO2 (cerium dioxide) concentrations (0.01 wt.%, 0.1 wt.%, 0.5 wt.%, and 1.0 wt.%) on the properties of CuAlMnFe alloys produced via powder metallurgy (PM). Various analyses were performed, including scanning electron microscopy (SEM), Energy Dispersive Spectroscopy (EDS), X-ray diffraction (XRD), as well as hardness, wear, and corrosion tests. The increase in wear rate is closely related to the formation of precipitates from CeO2 addition. Improvements in wear resistance and hardness are attributed to the effects of grain refinement and solid solution strengthening due to CeO2. Specifically, the wear rate increased from 1.5 × 10−3 mm3/(Nm) to 3.4 × 10−3 mm3/(Nm) with higher CeO2 content. Additionally, the friction coefficient of the CuAlMnFe alloy was reduced with CeO2 addition, indicating enhanced frictional properties. The optimal CeO2 concentration of 0.5% was found to improve grain uniformity, resulting in better wear resistance. Incorporating CeO2 particles into CuAlMnFe alloy enhances hardness and reduces wear rate when used in appropriate amounts. Additionally, it exhibits superior corrosion resistance, as evidenced by a positive shift in corrosion potential in Tafel measurements in solutions and a decrease in corrosion current density. The C0.5 specimen showed the highest corrosion potential (Ecorr, −588 V) and the lowest corrosion current density (icorr, 6.17 μA/cm2) during electrochemical corrosion in 3.5 wt.% NaCl solution.
AtıfScopus2WoS2OpenAlex2İncele - MakaleYalnız künye2024Scopus SJRQ2Investigation of thermal, crystal and magnetic behavior of addition of Nd rare earth element effect on CuAlMn shape memory alloy
Kanca, Muhammed Sait
In this study, CuAlMn alloys, a popular Cu-based shape memory alloy, were chosen because they exhibit superior shape memory properties and improved ductility compared to other Cu-based SMAs. The rare earth element Nd (neodymium) was added to CuAlMn alloy at the specified atomic percentages in the composition Cu70-xAl24Mn6Ndx(x = 0,2,4,8) and their thermal behavior, crystal structure, surface morphology and magnetic properties were investigated after fabrication. As a result of the thermal analysis measurements, it was observed that for low Nd ratios, the austenite phase transformation initial temperature of the CuAlMn alloy was increased, while at high Nd ratios, a decrease in the shape memory property was detected. Martensitic phase and precipitate phase α phase were observed in the crystal structure properties of CuAlMn alloys without and with Nd doping. These results were also detected in surface morphology observations. In addition, the crystal size decreased from 135 to 105 nm with Nd doping. As a result of magnetic measurements, CuAlMn ternary shape memory alloy was found to be paramagnetic at room temperature. Magnetic susceptibility values of the alloys showing paramagnetic magnetic properties were calculated as 11.5 × 10–6, 12.5 × 10–6, 9.15 × 10–6 and 6.15 × 10–6 emu.Oe−1.g−1, respectively. According to these results, the magnetic susceptibility value decreased with increasing Nd ratio.
AtıfScopus3WoS3OpenAlex3İncele