Yazarlar
Yayınlar
- MakaleAçık Erişim2020Scopus SJRQ2Fabrication of a novel acrylate polymer bearing chalcone and amide groups and investigation of its thermal and isoconversional kinetic analysis
Biryan, Fatih; Pihtili, Güzin
The aim of the article was to examine the thermal degradation, thermal decomposition kinetics and dielectric behavior of novel poly(APHP-Am–Ac). For this purpose, the novel monomer, 4-(3-(4-acetamidophenyl)-3-oxoprop-1-en-1-yl)phenyl acrylate (APHP-Am–Ac), was synthesized from 1-(4-aminophenyl)-3-(4-hydroxyphenyl) prop-2-en-1-one (APHP) and acetic anhydride reaction. The homopolymer P(APHP-Am–Ac) was prepared by free radical polymerization within dimethylformamide at 80 °C. The presence of rigid and bulky chalcone units in polymer side chains significantly improved the solubility of polyamides, giving them an amorphous nature and good thermal stability. The structural characterization of homopolymer was accomplished using FT-IR and NMR techniques. The thermal stability and degradation features of homopolymer have been performed by using TG analysis and FT-IR during partial degradation at different temperatures. The glass transition temperature of homopolymer was determined by DSC analysis. For thermal decomposition kinetics of poly(APHP-Am–Ac), Flynn–Wall–Ozawa and Kissinger methods were applied to thermogravimetric curves and apparent activation energies (Ea) calculated from these two methods. According to FWO, the activation energy (Ea) of the first step and the second step was found as: 157.78 kJ mol−1 and 151.81 kJ mol−1, respectively. For Kissinger’s model, Ea was calculated as 154.3 kJ mol−1 and 142.83 kJ mol−1, respectively. The dielectric and conductivity measurements of homopolymer were investigated by impedance analyzer technique in a range of 10 Hz–20 kHz frequency at different temperatures (from 25 to 120 °C). The results have been plotted as a function of frequency and temperatures. The values increased significantly with temperature.
AtıfScopus18WoS17OpenAlex18
İncele - MakaleAçık Erişim2020Scopus SJRQ2Thermal studies and influence of the thermal decomposition on dielectric properties of a new coumarin copolymers
Biryan, Fatih; Pihtili, Güzin; Demirelli, Kadir
In this study, firstly 7-hydroxy-4-chloroethyl coumarin compound was synthesized in accordance with the literature (Peterson et al. in Macromol Chem Phys 202: 775–784, 2001). Then, this compound was reacted with acryloyl chloride to form the 4-(chloromethyl)-2-oxo-2H chromen-7-yl-acrylate) monomer. A series of copolymers were prepared using this monomer and n-butyl acrylate monomer. TGA analysis system was used to examine the thermal properties of homopolymers and copolymers. The activation energies were calculated for thermal decomposition of homopolymer and certain copolymers according to Flynn–Wall–Ozawa method. TGA measurements were taken at different heating rates and given comparatively. The glass transition temperatures of the copolymers were determined by DSC analysis and these results were given comparatively. For investigating the dielectric properties of copolymers, dielectric constant, dielectric loss factor, and ac conductivity values were calculated in the range of 100 Hz–20 kHz frequencies. The results were plotted as a function of frequency. In addition, dielectric behaviors of residues were determined after heating to the first decay temperature of the two-stage decay polymers and compared with the first states.
AtıfScopus6WoS6OpenAlex6İncele