Yazarlar
Yayınlar
- MakaleAçık Erişim2026Scopus SJRQ1Change in phase stability and transformation kinetics of NiTiCuW alloy after heat treatment at 650–850 °C
Tatar, Cengiz; Kök, Mediha; Kanca, M. Sait
In this study, the effects of different heat treatment temperatures (650 °C, 750 °C, and 850 °C) on the phase transformation behavior, microstructure, thermodynamic parameters, and microhardness of the NiTiCuW alloy, produced by adding tungsten (W) to the NiTiCu shape memory alloy, were investigated. The crystal structure change was determined by X-ray diffraction (XRD), the transformation temperatures were determined by differential scanning calorimetry (DSC), the microstructure was examined by scanning electron microscopy (SEM), and the mechanical properties were evaluated by Vickers microhardness measurements. XRD results showed that the reference and 850 °C samples were predominantly in the B2 (austenite) phase at room temperature, while martensitic phases (B19/B19′) became prominent at 650 °C and 750 °C. DSC analyses revealed that the transformation peaks became sharper at 650 °C and the R-phase transformation could be observed; at 750 °C, the peaks broadened, indicating a decrease in transformation stability. The austenite finish temperature (Af) increased from 2.1 °C (reference) to 52.9 °C at 650 °C and 60.3 °C at 750 °C, while it remained low (4.5 °C) at 850 °C. Thermodynamic evaluations showed that ΔS increased at 650 °C (0.053 J/g K) and decreased at 750–850 °C (≈0.032 J/g K). Microhardness reached its maximum value at 650 °C (398 Hv), decreased at 750 °C (271 Hv), and showed an upward trend again at 850 °C (351 Hv), compared to the reference value (243 Hv). These results indicate that the heat treatment temperature critically determines the functional and mechanical performance of the NiTiCuW alloy.
- MakaleAçık Erişim2025Scopus SJRQ2Multifunctional properties and microstructural correlations of NiCoMnTi-Based high entropy alloys with focus on magnetic, thermodynamic, and radiation shielding characteristics
Özkul, İskender; Karaduman, Oktay; Şimşek, Tuncay; Şimşek, Telem; Canbay, Canan Aksu; Güler, Ömer; ALMisned, Ghada; Baykal, Duygu Sen; Tekin, Huseyin Ozan
High-entropy alloys (HEAs) are a novel class of materials known for their complex compositions and exceptional multifunctional properties. In this study, NiCoMnTi-based HEAs were modified with Fe, Cr, and Cu as fifth elements to systematically investigate their structural, magnetic, thermodynamic, and nuclear radiation shielding characteristics. The alloys were synthesized via arc melting and characterized using XRD, SEM-EDS, VSM, and theoretical modeling methods. The findings reveal that each additional element uniquely alters the alloy’s properties. The Fe-containing alloy exhibited a well-defined lamellar microstructure, the highest saturation magnetization (10.79 emu/g), and a Curie temperature near 450 K, along with strong gamma-ray shielding performance across both low and high energy ranges. The Cr-containing alloy demonstrated soft magnetic behavior, featuring the lowest coercivity (29.64 Oe) and the highest fast neutron removal cross-section. In contrast, the Cu-containing alloy enhanced low-energy photon attenuation due to its higher atomic number but exhibited limited magnetic homogeneity. Despite these differences, all samples displayed stable thermodynamic behavior and comparable buildup factor trends. Overall, the addition of Fe led to a synergistic improvement in both magnetic and radiation shielding capabilities of the NiCoMnTi-based HEA system.
AtıfScopus3OpenAlex3
İncele