- MakaleYalnız künye2016Scopus SJRQ3Characterization of hot pressed CuAl-TiC composites with different TiC grain sizes
Islak, S.; Çelik, E.; Kir, D.; Özorak, C.
In this study, the CuAl-TiC composite materials were produced using hot pressing process. Effect of TiC grain size (0.2, 4 and 20 mu m) on some properties of these materials was investigated experimentally. Production of CuAl-TiC composites was carried out under pressure of 35 MPa, at 700A degrees C, and for a sintering time of 5 minutes. SEM-MAP studies showed that the TiC grains were relatively homogeneously distributed in the CuAl matrix. Microstructure analysis revealed that the composite materials consist of Cu, Al, Cu9Al4, CuAl2 and TiC phases. With the decreasing of TiC grain size, the hardness, transverse rupture strength, relative density and sintered density of composites increased.
AtıfWoS7OpenAlex8
İncele - MakaleYalnız künye2014Scopus SJRQ3Preparation of cupric oxide by isothermal oxidation of metallic copper powder produced by electroless deposition
Demirkiran, Nizamettin; Tanaydin, Mehmet Kayra
In this study, cupric oxide powder was prepared from copper powder using a thermal oxidation method. The copper powder was produced by electroless deposition method using ascorbic acid as a chemical reducing agent. The oxide powder product was synthesized at 500A degrees C for 5 h. The metallic copper and oxide powder were characterized using X-ray diffraction and scanning electron microscopy. Based on results from these analytical techniques, it was determined that cupric oxide was successfully synthesized from the thermal treatment of copper powder and was in agglomerated state.