Sürdürülebilir Kalkınma Amaçları
Yazarlar
Yayınlar
- MakaleAçık Erişim2025Scopus SJRQ4Adsorption of RB-5 Dyestuff onto Boric Acid-Zinc Nanoalloys: Isotherm, Kinetic, and Thermodynamic Investigations
İlhan, Hasan; Güler, Ömer; Şi̇mşek, Tuncay; Alkan, Salih
In this study, boric acid-zinc (BA-Zn) nanoalloys were employed as an adsorbent for the removal of RB-5 dyestuff from aqueous solutions. The investigation focused on analyzing the impact of the initial dyestuff concentration, solution pH, temperature, and equilibrium contact time on the adsorption process of RB-5. The adsorption behavior of RB-5 onto the surface of BA-Zn-nanoalloys was explored, with a particular emphasis on the influence of initial dyestuff concentration and solution pH. The adsorption equilibrium data were subjected to analysis using Langmuir, Freundlich, DRK, and Temkin isotherm models. The results revealed a consistent alignment of RB-5 adsorption with both Langmuir and Temkin isotherms. Notably, the Langmuir adsorption capacity of BA-Zn-nanoparticles for RB-5 adsorption was determined to be 11.77mg / g at a temperature of 25°C. In the Temkin isotherm model, an adsorption constant (AT) of 1.003 was obtained. The calculated adsorption energy from the DR adsorption model was 1.09kJ / mol, implying a physical interaction-driven adsorption process. The empirical data further exhibited conformity with the pseudo-second order kinetic model, reflecting the rate-limiting step and overall kinetics of the adsorption process. Complementary to this, thermodynamic parameters such as enthalpy (ΔH0), Gibbs free energy (ΔG0), and entropy (ΔS0) were evaluated to discern the energetics of BA-Zn-nanoparticle RB-5 adsorption. This study not only underscores the effectiveness of BA-Zn nanoalloys as a potential adsorbent for RB-5 dyestuff removal but also contributes to the understanding of the underlying adsorption mechanisms and energetics. The insights gained hold implications for the development of sustainable and efficient strategies for wastewater treatment and environmental protection.
- MakaleYalnız künye2024Scopus SJRQ2Effects of Cr and W in TiMoNb Refractory High Entropy Alloys
Simsek, Tuncay; Kurtulus, Altug; Avar, Baris; Güler, Seval Hale; Dag, İlker Emin; Chattopadhyay, Arun K.
This study focuses on synthesizing and characterizing mechanically alloyed refractory high entropy alloys (RHEA) containing TiMoNb, Cr, W, and Cr + W. Analytical techniques including XRD, SEM, EDX, DTA, and TGA were employed to explore the influence of Cr and W on the alloys' structure, morphology, and thermal stability towards oxidation. XRD analysis confirmed the formation of a single-phase bcc solid solution in TiMoNbCr, TiMoNbW, and TiMoNbCrW alloys. Crystallite size decreased as milling progressed, yielding average sizes of approximately 7.2 nm, 7.4 nm, and 9.7 nm, with lattice strains of 1.143%, 1.148%, and 1.15%, respectively. Both experimental and calculated values of lattice parameters converged to around 3.1685 ± 0.002 and 3.1791 ± 0.010 Å for all three alloys. The synergy of Cr and W in TiMoNb was observed for the first time, impacting dislocation density, hardness, and oxidation stability. TiMoNbCrW exhibited reduced dislocation density and the highest hardness (502 HV). TGA indicated enhanced oxidation resistance up to 400 °C for TiMoNbCrW compared to the most vulnerable TiMoNbCr alloy.
AtıfScopus2OpenAlex2
İncele