- MakaleAçık Erişim2024Scopus SJRQ2Effects of Ga, Nb, V, Zr, and Cr on the crystal structures and thermal behavior of CuAlMn shape memory alloys
Özkul, İskender; Karaduman, Oktay; Canbay, Canan Aksu
CuAlMn alloys are cheaper and more promising alloy types compared to NiTi alloys. In this study, based on CuAlMn shape memory alloy, thermodynamic and structural characteristics of some new alloys containing four elements were investigated in detail. In this study, five new quaternary shape memory alloys, each containing a CuAlMn base alloy and a different fourth additive element (Ga, Nb, V, Zr, and Cr), were produced. The properties of the obtained alloys were characterized using a series of analysis methods such as X-ray diffraction (XRD), optical microscopy, differential scanning calorimetry (DSC), and differential thermal analysis (DTA). The results showed the effects of different elements on the crystal structures of the alloys and how different elements could change the thermal behavior of the alloys.
AtıfScopus4WoS3OpenAlex6
İncele - MakaleAçık Erişim2024Scopus SJRQ2Hysteresis gap-shrinking and structural effects of minor Al and Ti modifications on binary CuAl-based high-temperature shape memory alloys
Karaduman, Oktay; Özkul, İskender; Aksu Canbay, Canan
Cu-based shape memory alloys (SMAs), except for exhibiting shape recovery, superelasticity, and high damping, are desirable because these smart materials have higher electrical and thermal conductivity and much lower prices than NiTi SMAs. However, they also have some downsides in mechanical strength and brittleness (mostly stemming from their coarse grain structure) and thermal instability. Therefore, adding some grain refining elements to these SMAs to improve their shape memory effect (SME), and thermal, structural, and mechanical properties is a widespread and simple way that significantly affects their martensitic phase transitions, structure, and mechanical properties. One of these grain-refining elements is titanium. Its thermal conductivity is lower than those of Cu and Al elements and has a low solubility in Cu-matrix. Besides the effects of small Al variations, the use of minor amounts of titanium in binary CuAl-base alloys can show impressive effects on all characteristics of these shape memory alloys, such as shape memory effect properties, martensitic transformation kinetics parameters, and microstructural features. In this research work, CuAlTi ternary high-temperature shape memory alloys (HTSMAs) with new compositions were produced by the arc melting method without a complicating use of Mn or Ni components in usual ternary CuAlMn and CuAlNi shape memory alloys. Thermal analyses of the prepared samples of the alloys were investigated by using differential scanning calorimetry (DSC) and differential thermal analysis (DTA) measurements. In contrast, x-ray diffraction (XRD) test results and optical micrographs were used for analyzing the structure of the alloy samples. The effect of different amounts of low soluble and grain refining Ti element on the binary CuAl alloy system was investigated.
AtıfScopus2WoS2OpenAlex2İncele - MakaleAçık Erişim2024Scopus SJRQ2High thermal stability effect of vanadium on the binary CuAl base alloy for a novel CuAlV high-temperature shape memory alloy
Karaduman, Oktay; Özkul, İskender; Güler, Seval Hale; Aksu Canbay, Canan
In this study, two high-temperature shape memory alloys (HTSMAs) of CuAlV with unprecedented chemical compositions were fabricated using the arc melting technique, followed by traditional ice-brine water quenching after the melting process. To characterize the shape memory properties and structure of the alloys, a series of tests including differential calorimetry (DSC and DTA), EDS, optical microscopy, and XRD were conducted. The DSC tests, performed at different heating and cooling rates, demonstrated highly stable reversible martensitic phase transformation peaks at high temperatures, which were also confirmed by the results of DTA tests. Microstructural XRD and optical microscopy tests were conducted at room temperature, revealing the martensitic structure of the alloys in both cases. Based on all the results, the effects of different minor amounts of vanadium additives directly on the CuAlV alloy were discussed.
AtıfScopus2WoS2OpenAlex3İncele - MakaleAçık Erişim2024Scopus SJRQ2Fabrication of CuAlVMg High-Temperature Shape Memory Alloy Containing Low-Soluble Vanadium Addition
Karaduman, Oktay; Boyrazli, Mustafa; Canbay, Canan Aksu; Özkul, İskender; Çelik, Emrah; Başbağ, Güneş
For the first time, CuAlVMg high-temperature shape memory alloy (HTSMA) with unprecedented alloy composition and with extended solubility of vanadium element was fabricated as-cast ingot by arc melting method, then homogenization of the alloy in high β-phase temperature region and quenching in iced-brine water were performed, respectively. The characteristic forward martensite to austenite martensitic transformation (MT) temperatures were detected at around 390 °C, which put the novel alloy in the category of HTSMAs. The thermal response of the alloy at high-temperatures was observed by DTA test as coherent with usual Cu-based HTSMAs. The residual sub-eutectoid precipitations emerging at around 500 °C hindered the direct martensitic transformation. The martensite structure of the alloy was revealed by XRD, SEM and optical microscopy tests.