- MakaleYalnız künye2019Scopus SJRQ2The effect of hygrothermal aging and UV radiation on the low-velocity impact behavior of the glass fiber-reinforced epoxy composites
Dogan, Akar; Arman, Yusuf
The present work examines the effects of hygrothermal and UV radiation aging on the reinforced epoxy composites. The role of temperature in the hygrothermal aging process on tensile properties, impact behavior of composites and compression-after impact was investigated. Among four different chosen aging conditions, three of them were hygrothermal and last one was composed of both hygrothermal and UV radiation. Unidirectional e-glass fiber fabrics with an areal density 300 g/m2 as reinforcement and epoxy matrix were used. Composites were manufactured using vacuum-assisted resin infusion molding. The goal of this study was to investigate the effect of UV radiation and aging temperature with respect to the glass transition temperature. In this context, aging procedures were carried out in two different ways for 70 °C temperature with and without UV radiation. As a result of the test, the tensile strength, tensile modulus, absorbed energy, interlaminar shear strength (ILSS), and compression-after impact (CAI) strength of the glass reinforced composites decreased for all conditions. Despite being under the same ambient temperature and humidity, the samples which were exposed to UV radiation had lower mechanical properties. The reduction of tensile strength of specimens exposed to 70 °C and 70% humidity with and without UV radiation were 24% and 10%, respectively. The temperature of hygrothermal conditions significantly affected the perforation threshold. In low impact energies, delamination was the primary damage mode, while fiber breakage becomes more important in the composite at high impact energy levels.
AtıfScopus48WoS43OpenAlex48
İncele - MakaleYalnız künye2019Scopus SJRQ3Effects of temperature and impactor nose diameter on the impact behavior of PA6 and PP thermoplastic composites
Dogan, Akar; Arman, Yusuf
In this study, the effects of temperature and impactor nose diameter on the impact behavior of woven glass-reinforced polyamide 6 (PA6) and polypropylene (PP) thermoplastic composites were investigated experimentally. Impact energies are chosen as 10, 30, 50, 70, 90, 110, 130, and 170 J. The thickness of composite materials is 4 mm. Impact tests were performed using a drop weight impact testing machine, CEAST-Fractovis Plus, and the load capacity of test machine is 22 kN. Hemispherical impactor nose diameter of 12, 7, and 20 mm were used as an impactor. The tests are conducted at room temperature (20°C and 75°C). As a result, the PP composites of the same thickness absorbed more energy than PA6 composites. The amount of absorbed energy of PP and PA6 composites decreased with temperature.
AtıfScopus7WoS6OpenAlex6İncele - MakaleAçık Erişim2013EFFECT OF EMBEDDED DELAMINATIONS ON IMPACT BEHAVIOR OF LAMINATED COMPOSITES
Sabanci, Eray; Karakuzu, Ramazan
In this study, the influence of size and location of embedded delamination on impact behavior of laminated composite was investigated, experimentally. The specimens were produced as for with and without delamination by vacuum assisted resin infusion molding method (VARIM). CEAST-Fractovis plus impact test machine was used in the experiments. As a result of the experiments, the location of delamination on the impact behavior was seen to be more effective than the size of delamination.
AtıfWoS3OpenAlex5İncele