- MakaleAçık Erişim2023Experimental investigation of engineering properties of silica sand filled mortars containing high doses of SWCNT
Subaşı, Serkan; Dehghanpour, Heydar; Maraşlı, Muhammed; Doğan, Fatih
Recently, great efforts have been made by researchers on the mixture of electrically conductive concretes that have been developed for different purposes. In this study, an experimental research was carried out on electrically conductive mortar mixtures especially for shell elements produced for building facade cladding. Six different mixtures were produced, including the non-conductive reference mixture. Single-walled carbon nanotube (SWCNT) was used as nano-sized conductive additive material. SWCNT was added at 0.2% and 0.3% of cement weight. SF was added to the same mixtures as another group at the rate of 4% by total weight. 2, 14, 28, 90 and 180 days electrical resistivities of the obtained conductive mortar samples were measured. As a non-destructive method, dynamic resonance testing was performed and the 28-day damping rates of the samples were determined. Ultrasonic pulse velocity (UPV) and Leeb hardness tests were performed, respectively, by using other non-destructive testing methods to obtain information about the internal structure voids and surface hardness of the samples. SWCNT, which causes low machinability and therefore internal structure voids, caused a decrease in compressive strength and flexural strength, as well as a significant increase in electrical conductivity.
AtıfOpenAlex1
İncele - MakaleAçık Erişim2023Doğal Elyaf Takviyeli (Jüt-Keten-Kenevir) Kompozit Malzemelerin Mekanik ve Metalografik Olarak İncelenmesi
Taşgın, Yahya; Kandemir, Seçkin
Teknolojinin gelişmesiyle birlikte özellikle polimer esaslı saf haldeki malzemelerin yetersiz kalmasından dolayı kompozit malzemeler geliştirilmiş ve zamanla kullanım alanları çoğalmıştır. Son yıllarda artan çevre bilincinin getirdiği üretimde sürdürülebilirlik ve yenilenebilir, çevre dostu kompozitlerin kullanımını giderek yaygınlaşmaktadır. İçeriğindeki malzemelerden en az birisinin doğal olması ile tanımlanan biyokompozitlerin, alternatiflerine kıyasla çok daha çevre dostu olmalarına karşın, hidrofilik yapıda olmaları ve mekanik özelliklerinin zayıf olması sebebiyle sanayide kısıtlı alanda kullanılmaktadır. Bu çalışmada takviye malzemesi olarak kullanıla bilirliğini ortaya koymak için jüt, keten ve kenevir den oluşan doğal lif takviyeli epoksi kompozitlerin (NFRC) mekanik ve metalografik açıdan ortaya koyduğu farkındalıklar incelenmiştir. Üretim yöntemi olarak vakum destekli reçine transfer kalıplama (VDRTK) metodu kullanılmıştır. Metalografik olarak incelediğimizde; doğal liflerin yapı içerisinde yer alması ve epoksinin ara yüzeylere nüfuziyeti açısından problem oluşturmadığı görülmüştür. Çekme testleri, kompozitler arasında farklı mekanik davranışları ortaya çıkarmıştır; keten kompoziti en yüksek çekme mukavemetini (75,56 MPa) jüt ve kenevirin ise ketene kıyasla düşük çekme mukavetine sahip olduğu görülmektedir. Endüstriyel olarak üretilen yapay elyaflara (Cam elyafı) kıyasla mekanik ve mikro yapı açısından zayıf görünse de özellikle karmaşık yapılı parçaların üretiminde nüfuziyet ve ara bölgelere yerleşebilecek olmasından kaynaklı daha kullanışlı olduğu ortaya çıkmıştır.
AtıfOpenAlex1TR Dizin1İncele - MakaleAçık Erişim2022Viscometric Investigation of Compatibilizer Effect on Polyvinyl chloride/Polystyrene Blends
Yilmaz, Ersen; Boztuğ, Ali
In this study, polyvinyl chloride (PVC) and polystyrene (PS) polymers, which do not form a compatible blend with each other in certain concentration ranges and are widely used on an industrial scale, were used. The concentration range in which these two polymers do not form a compatible blend were determined viscometrically, and maleic anhydride-styrene (MAS) copolymer was added as a compatibilizing agent in this concentration range. The concentration range in which the polymer pair did not form a compatible blend was determined as 1.5 and 2.0 g dL-1. In this concentration range, 5.0 and 10.0 % MAS copolymer was added to the polymer couple and its compatibilizing effect was investigated. It was determined by viscometric method that the MAS copolymer was a good compatibilizer in the range where the polymer pair did not form a compatible blend.
AtıfOpenAlex1İncele - MakaleAçık Erişim2022Tane şeklinin galen cevherinin flotasyonuna ve topaklanmasına etkisi
Guven, Onur; Uysal, Turan
Farklı şekil faktörlerine sahip tanelerle yürütülen flotasyon çalışmalarında daha köşeli tanelerin yuvarlak tanelere nazaran daha yüksek verimle kazanıldığı bilinmektedir. Bu durum flotasyon işlemlerinde şekil faktörlerinin rolünü göstermekte olup, uygulamalarda uygun tane morfolojisi ile önemli kazanımlar sağlanılabilmektedir. Bu çalışmada ise galen flotasyonu üzerine tane şeklinin etkisi çalışılmıştır. Bu amaçla galen -74+38 µm boyutunda şekil faktörü analizi yapılmıştır. Farklı şekil faktörüne sahip numuneler farklı KAX konsantrasyonlarında mikro-flotasyon ve agregasyon işlemleri yapılmıştır. Mikro-flotasyon sonuçlarına göre KAX konsantrasyonu arttıkça şekil faktörünün etkisinin arttığı ancak yüksek konsantrasyonlarda bu etkinin tam olarak gözlenmediği saptanmıştır.
- MakaleAçık Erişim2019Production and Characterization of Carbon-Kevlar-Aramid Reinforced Layer Composites with VARTM Method
Taşgın, Yahya; Sahin, Engin Sahin
In this study, laminated composite materials are produced by Vacuum Assisted Resin Transfer Molding(VARTM) Method. Three different reinforcement materials (carbon, kevlar and aramid) are used in theproduction phase. Tensile test is applied to the samples after the production and in the light of SEM images;fractured surfaces of the samples and their results are evaluated.