- MakaleAçık Erişim2026Scopus SJRQ2Design of Fe–35Ni/PCL nanocomposites with coupled magnetic and shape memory properties
Kök, Mediha; Çirak, Z Deniz; Aydin, Handan; Coşkun, Meltem
In this study, poly(ϵ-caprolactone) (PCL)-based nanocomposite films reinforced with a Fe–35%Ni alloy, which possesses a low coefficient of thermal expansion and distinct magnetic properties, were produced. The composites were prepared using the solvent casting method, with the Fe–Ni alloy incorporated into the PCL matrix at different weight ratios (10%–50%). The structural, morphological, thermal, and magnetic properties of the resulting nanocomposites were comprehensively investigated using FTIR (Fourier transform infrared spectroscopy), XRD (X-ray diffraction), SEM (scanning electron microscopy/energy dispersive x-ray spectroscopy), differential scanning calorimetry, TGA (Thermogravimetric analysis) ve (vibrating sample Magnetometry). FTIR results indicated that the Fe–Ni addition does not form chemical bonds with the PCL matrix and that the composite structure is formed through physical interactions. XRD analyses confirmed that the semi-crystalline structure of PCL is preserved and that the Fe–Ni alloy exhibits a face-centered cubic (FCC) crystal structure. SEM images revealed that while a homogeneous distribution is achieved at low doping levels, partial agglomeration occurs at high levels. Thermal analyses showed that Fe–Ni particles increase the degree of crystallization through a nucleation effect and provide a significant increase in melting temperature and crystallinity values, particularly in the 10%–40% range. TGA results revealed that the thermal stability of the composites increased and their decomposition behavior became multi-stage. Magnetic measurements showed that the saturation magnetization increased significantly with increasing Fe–Ni content, and the composites acquired ferromagnetic character. Furthermore, it was determined that the developed composites exhibit distinct shape memory behavior and can return to their original form upon thermal stimulation. The findings indicate that Fe–35%Ni-doped PCL nanocomposites are a promising candidate for multifunctional applications due to their enhanced thermal, magnetic, and smart material properties.
- MakaleAçık Erişim2024Scopus SJRQ2Zr and V-doped effect on Martensitic transformations and magnetic properties of NiMnIn shape memory alloy
Taşgın, Yahya; Kanca, M. Sait; Kök, Mediha; Öner, Ecem Özen; Güler, Ömer
In this study, the elements vanadium (V) and zirconium (Zr) were doped separately as a fourth element to the ternary NiMnIn Heusler magnetic shape memory alloy and the alloys were produced as ingots by arc-melting method. The shape memory properties, microstructures, magnetic and microstructural changes of these new alloys were investigated in detail. The vanadium (V) and zirconium (Zr) elements doped into the alloy caused a decrease in the transformation temperature values of the alloy, but did not cause a significant change in its magnetic properties. The master sample, which has low hysteresis, undergoes a phase transition from the martensite phase to the austenite phase due to an increase in the nucleation of austenite phases at the twinning boundaries. Here, the vanadium and zirconium doping of the alloy caused an increase in the strength and ductility values of the alloy and this caused the formation of the second phase. Due to the increase of this phase formation in the alloy, it can be said that there is a slight decrease in the shape retention of the alloy.
AtıfScopus3WoS3OpenAlex3
İncele - MakaleAçık Erişim2024Scopus SJRQ2High thermal stability effect of vanadium on the binary CuAl base alloy for a novel CuAlV high-temperature shape memory alloy
Karaduman, Oktay; Özkul, İskender; Güler, Seval Hale; Aksu Canbay, Canan
In this study, two high-temperature shape memory alloys (HTSMAs) of CuAlV with unprecedented chemical compositions were fabricated using the arc melting technique, followed by traditional ice-brine water quenching after the melting process. To characterize the shape memory properties and structure of the alloys, a series of tests including differential calorimetry (DSC and DTA), EDS, optical microscopy, and XRD were conducted. The DSC tests, performed at different heating and cooling rates, demonstrated highly stable reversible martensitic phase transformation peaks at high temperatures, which were also confirmed by the results of DTA tests. Microstructural XRD and optical microscopy tests were conducted at room temperature, revealing the martensitic structure of the alloys in both cases. Based on all the results, the effects of different minor amounts of vanadium additives directly on the CuAlV alloy were discussed.
AtıfScopus2WoS2OpenAlex3İncele - MakaleAçık Erişim2024Scopus SJRQ2Fabrication of CuAlVMg High-Temperature Shape Memory Alloy Containing Low-Soluble Vanadium Addition
Karaduman, Oktay; Boyrazli, Mustafa; Canbay, Canan Aksu; Özkul, İskender; Çelik, Emrah; Başbağ, Güneş
For the first time, CuAlVMg high-temperature shape memory alloy (HTSMA) with unprecedented alloy composition and with extended solubility of vanadium element was fabricated as-cast ingot by arc melting method, then homogenization of the alloy in high β-phase temperature region and quenching in iced-brine water were performed, respectively. The characteristic forward martensite to austenite martensitic transformation (MT) temperatures were detected at around 390 °C, which put the novel alloy in the category of HTSMAs. The thermal response of the alloy at high-temperatures was observed by DTA test as coherent with usual Cu-based HTSMAs. The residual sub-eutectoid precipitations emerging at around 500 °C hindered the direct martensitic transformation. The martensite structure of the alloy was revealed by XRD, SEM and optical microscopy tests.
- MakaleAçık Erişim2023Scopus SJRQ3Effect of 5.31Ti (at.%) content used as ternary in quaternary Cu-rich high-temperature shape memory alloy cast via arc melting
Başbağ, Güneş; Karaduman, Oktay; Canbay, Canan Aksu; Özkul, İskender; Boyrazlı, Mustafa
In this work, the new quaternary CuAlTiMg high-temperature shape memory alloy (HTSMA) with an unprecedented composition and with extended solubility of Ti was produced by the arc melting method. The thermal shape memory effect characterization tests were done by performing a series of differential calorimetric (DSC and DTA) measurements. The obtained thermograms of the alloy displayed the martensitic phase transformation peaks. The forward (martensite to austenite) phase transformation was found to occur at above 350◦C, which qualifies the produced alloy as an HTSMA. The microstructural XRD measurement was performed to reveal the atomic planes of martensite structures formed in the alloy, which constitute the shape memory effect property of the fabricated alloy. The alloy surface was monitored by optical microscopy image taken at room temperature, and finely dispersed Ti-rich X-phases were observed.