  Microstructure and Dry-Sliding Tribology of HVOF-Sprayed NiCrBSi/WC-Co Coatings on AZ91D

  Gürgenç, Turan; Macit, Cevher Kürşat; Sömer, Medeni; Aksakal, Bünyamin; Ayık, Merve; Say, Yakup

  High-velocity oxy-fuel (HVOF)-sprayed NiCrBSi coatings containing 0, 10, 30, and 50 wt.% WC-Co were evaluated on AZ91D magnesium alloy to determine how the discrete reinforcement level affects surface topography, phase constitution, Vickers microhardness, dry-sliding friction, mass loss, and wear-track microchemistry. As-sprayed surfaces were characterized by three-dimensional profilometry; coating cross-sections and worn surfaces by optical microscopy and SEM/EDS; phase constitution by XRD; and mechanical response by HV0.1 indentation. Dry-sliding tests were performed at 10, 30, and 50 N over 100–1000 m. Increasing WC-Co content raised Sa from 8.8 ± 0.3 to 13.0 ± 0.5 µm and Vickers microhardness from 776 ± 4 to 959 ± 5 HV0.1. XRD indicated a γ-Ni-based matrix containing boride/carbide constituents, while WC, W2C, and Co became increasingly prominent in the reinforced coatings. Boride assignments are based on diffraction evidence, whereas B and C EDS signals were treated semi-quantitatively. The 50 wt.% WC-Co coating exhibited the lowest mass loss and mean coefficient of friction at every load. Its mean friction coefficients were 0.31, 0.35, and 0.41 at 10, 30, and 50 N, corresponding to reductions of 40.1%, 38.9%, and 36.2% relative to AZ91D. At 1000 m, its mass-normalized wear rate indices were 9.0 × 10−4, 4.0 × 10−4, and 5.3 × 10−4 mg N−1 m−1, respectively. Post-wear mapping showed the largest field-scale W-Co-rich fraction in the 50 wt.% coating; however, isolated spectra containing more than 94 wt.% Mg are compatible with local coating penetration/substrate exposure and/or Mg-rich debris. The 50 wt.% composition therefore provided the best combined response among the four tested levels, while intermediate compositions are required to identify a continuous-composition optimum.

  İncele
• MakaleAçık Erişim2026Scopus SJRQ2/r/munzur/1502
  Which implant for Pauwels type 2 femoral neck fractures: a biomechanical study

  Aydın, Oğuz; Kazez, Muhammed; Say, Yakup; Belhan, Oktay

  Objective: Femoral neck fractures (FNF) in young patients are relatively rare but can lead to severe complications if not treated appro-priately. Pauwels type 2 fractures, characterized by moderate inclination, require surgical stabilization. However, no consensus exists regarding the optimal implant that provides superior biomechanical stability. This study aims to compare the biomechanical properties of 3 different fixation systems for the surgical treatment of Pauwels type 2 FNF. Methods: A total of 21 bovine femurs of similar age and size were selected and divided into 3 fixation groups: dynamic hip screw (DHS), cannulated screws (CS), and major plate (MP). Each specimen underwent axial compression testing to assess the maximum load-bearing capacity, shear force resistance, and deformation characteristics of the fixation methods. Results: The results showed that the CS group exhibited the highest shear stress resistance, followed by the DHS group, while the MP group showed significantly lower mechanical strength and elongation (P <.05). Although DHS provided substantial stability, CS demon-strated superior overall mechanical performance. In contrast, the MP system showed significantly lower resistance compared to the other 2 fixation methods. Conclusion: This biomechanical study highlights the importance of implant selection in the management of Pauwels type 2 FNF. Although previous investigations have questioned the adequacy of CS fixation in highly unstable Pauwels type 3 fractures, the results suggest that CS may be a reliable and effective option for the relatively more stable Pauwels type 2 pattern. Because the tests were performed on bovine femur models, which do not fully reflect the structural characteristics of human bone, these findings should be interpreted with caution. Further biomechanical studies using human cadaveric specimens are required to confirm the applicability of these results to clinical practice.

  • 
  İncele
• MakaleAçık Erişim2026Scopus SJRQ2/r/munzur/1340
  Effects of Magnetic Abrasive Finishing Process Parameters on the Inner Surface Machining of AISI 304 Austenitic Stainless Steel Pipes

  Sarıçiçek, İzel; Çaydaş, Alparslan Ulaş; Cihangir, Salih; Say, Yakup

  In this study, the effects of SiC abrasive ratio, size of magnetic Fe particles and the machining time parameters on the surface roughness, material removal rate, roundness of the holes and corrosion resistance in magnetic abrasive inner surface finishing (MAF) of the AISI 304 austenitic stainless steel pipes were experimentally investigated. A Taguchi L9 orthogonal array was used for the experiments. The surface roughness and the characteristics of the machined surfaces were examined by using the3D surface topography method. The characteristics of the abrasive and magnetic powders before and after machining operations were investigated under scanning electron microscope (SEM) and x-ray diffraction analysis (XRD) techniques. The electrochemical corrosion measurements were performed in 3.5 wt.% NaCl solutions in a typical three-electrode electrochemical cell. An analysis of variance (ANOVA) method was also applied to the study in order to determine the statistical effects of each factor on the measured responses. Consequently, AISI 304 samples machined with MAF technique revealed better results for corrosion performance, surface quality, material removal rate and the hole dimensional tolerances.

  AtıfScopus1·WoS1·OpenAlex1

  İncele
• MakaleAçık Erişim2025/r/munzur/6014
  Investigation of the Bioactivity Properties of TiZrCrNb0.3Ta0.07 Medium Entropy Alloy Produced from TNTZ Waste

  Say, Yakup; Yayla, Nihal; Güler, Ömer; Güzel, Harun

  High entropy alloys (HEAs) and medium entropy alloys (MEAs) have garnered significant attention as alternative materials in various fields due to their superior physical and chemical properties compared to conventional alloys. One of the most promising applications of this innovative material class is in biomaterials. In this study, a bio-medium entropy alloy (BioMEA), TiZrCrNb0.25Ta0.05, was successfully synthesized using non-toxic elements (Ti, Zr, Cr, Nb and Ta) through arc melting of TNTZ alloy waste. The produced BioMEA was comprehensively characterized using scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD) to analyze its structural and chemical properties. Additionally, the in-vitro degradation, ion release, and bioactivity properties of the alloy were evaluated and compared with those of the conventional TNTZ alloy, with a focus on the effects of heat treatment. The results demonstrated that heat treatment did not cause significant changes in the microstructure of the TiZrCrNb0.25Ta0.05 alloy but led to the formation of intermetallic compounds such as Cr2Zr and Cr2Ta on the surface. Degradation tests revealed an unexpected mass gain across all sample groups after a four-week immersion period due to surface precipitation, surpassing the expected mass loss from degradation. Ion release analyses showed similar behavior between the TiZrCrNb0.25Ta0.05 and TNTZ alloys, with ion release levels in the ppb range, confirming that Ti was released at non-toxic levels. Bioactivity tests identified low lesvels of Ca-P-O deposition on all sample surfaces, with the highest bioactivity observed in the heat-treated TiZrCrNb0.25Ta0.05 sample. Overall, the findings suggest that the TiZrCrNb0.25Ta0.05 alloy has the potential to serve as an alternative biomaterial to the TNTZ alloy, with its bioactivity properties being further enhanced through heat treatment. Further studies are recommended to optimize its bioactivity and evaluate its in-vivo performance for biomedical applications.

  • 
  • 
  İncele
• MakaleAçık Erişim2025Scopus SJRQ1/r/munzur/1546
  Y2O3-Doped BioGlass Coatings for Ti-6Al-4V Alloy: Insights into Degradation, Bioactivity, Ion Release, Adhesion, and Corrosion Behavior

  Say, Yakup; Aslan, Naim; Cihangir, Salih; Murat, Oğuzkağan; Çaydaş, Ulaş

  The Ti-6Al-4V alloy is particularly favored for orthopedic applications. However, important issues such as corrosion resistance, biocompatibility, and ion release need to be addressed. Therefore, this study aims to enhance the corrosion resistance and biocompatibility and reduce the ion release of the Ti-6Al-4V alloy by applying Y2O3-doped bioglass bioceramic coatings. The coatings were synthesized using the sol-gel method, including pure BioGlass and BioGlass with 1, 5, and 10 wt pct Y2O3. These coatings were then evaluated for their corrosion resistance, adhesion strength, degradation behavior, bioactivity, and ion release. The results showed that all coatings exhibited homogeneous, crack-free, and porous morphologies, which are favorable for osteointegration. The addition of 10 wt pct Y2O3 to the BioGlass coating resulted in a 52 pct increment in adhesion strength, which increased from 13.72 ± 2.80 MPa for single BioGlass coatings to 20.81 ± 2.53 MPa. All samples showed degradation values lower than 1 wt pct. Single BioGlass coatings significantly enhanced the bioactivity of Ti-6Al-4V alloy. However, the addition of Y2O3 negatively impacted BioGlass bioactivity, leading to a noticeable decrease as the Y2O3 content increased. Conversely, the presence of Y2O3 negatively impacted bioactivity and corrosion resistance while increasing the release of Ti ions. Specifically, the release of Ti ions increased from 79.5 ± 0.8 ppb in uncoated samples to 253.7 ± 15.3 ppb in BG-coated samples. For 1, 5, and 10 pct Y2O3-added samples, Ti releases were measured as 192.2 ± 33.6 ppb, 168.5 ± 62.4 ppb, and 194.3 ± 54.4 ppb, respectively. This research highlights the potential of tailored BioGlass coatings to improve the performance of Ti-6Al-4V alloys in orthopedic implant applications, particularly for enhancing bone integration and reducing implant failure.

  • 
  AtıfScopus4·WoS3·OpenAlex5

  İncele
• MakaleAçık Erişim2025Scopus SJRQ1/r/munzur/1363
  One-pot synthesis of quercetin-functionalized silver and copper nanoparticles for enhanced optical, antimicrobial, and computational properties

  Aziz, Dara Muhammed; Amin, Alla Ahmed Muhammed; Hassan, Sangar Ali; Özmen, Habibe; INCILI, Gökhan Kursad; Say, Yakup

  The emergence of multidrug-resistant bacterial strains has intensified the need for novel antimicrobial agents. Herein, we report a facile one-pot green synthesis of quercetin-stabilized silver (Qn@AgNPs) and copper (Qn@CuNPs) nanoparticles using quercetin as both reductant and capping ligand. The resulting nanocomposites were fully characterized by UV–Vis spectroscopy (surface plasmon resonance peaks at 420 nm for Ag and 580 nm for Cu), FTIR (confirming quercetin–metal coordination), SEM/EDX (spherical particles, and XRD (face-centered cubic Ag and Cu phases). Density functional theory (B3LYP/3-21G) calculations yielded frontier molecular orbital gaps of 0.164 eV for Qn@AgNPs and 0.245 eV for Qn@CuNPs, with corresponding high softness values (12.20 and 8.16 eV⁻¹), indicating enhanced electron-transfer propensity. Molecular electrostatic potential maps revealed increased charge polarization around the metal centers. Antibacterial assays against Escherichia coli and Staphylococcus aureus demonstrated minimum inhibitory concentrations of 2.11 ± 1.22 µg/mL and 4.69 ± 2.68 µg/mL for Qn@AgNPs, and 7.50 ± 0.00 µg/mL and 6.25 ± 0.17 µg/mL for Qn@CuNPs, significantly outperforming free quercetin (188 and 375 µg/mL). In silico docking against the S. epidermidis TcaR regulator (PDB: 1KZN) and E. coli DNA gyrase B (PDB: 1HSK) revealed strong binding affinities (–7.54 to − 10.15 kcal·mol⁻¹), consistent with the observed antimicrobial potency. This integrated experimental–computational study elucidates the mechanistic underpinnings of quercetin-mediated nanoparticle bioactivity and provides a rational framework for designing next-generation flavonoid-functionalized metal nanotherapeutics.

  • 
  AtıfScopus12·WoS11·OpenAlex14

  İncele
• MakaleYalnız künye2024Scopus SJRQ2/r/munzur/2304
  Synthesis and characterization of TiNbZrMo medium-entropy bio-composites: Microstructure, mechanical properties, and in vitro degradation

  Say, Yakup

  This study reports the synthesis and characterization of hydroxyapatite (HA)-based bio-composites reinforced with varying amounts (by weight, 1–15 wt.%) of bio-medium entropy alloy (BioMEA) for load-bearing implant applications. BioMEA powders consisting of Ti, Nb, Zr, and Mo were mechanically alloyed for 100 h and subsequently added to HA using powder metallurgy techniques. To show the effect of BioMEA, the microstructure, density, and mechanical tests have been conducted and the synthesized BioMEA was characterized by scanning electron microscope (SEM), x-ray diffractometer (XRD), and Fourier-transform infrared spectroscopy (FTIR) analysis. In addition, in vitro degradation behavior and bioactivity analyses of bio-composites have been conducted. XRD analysis revealed the formation of BioMEA after 20 h of mechanical alloying. The highest density value of 2.47 g/cm3 was found in 15 wt.% BioMEA-reinforced bio-composite. The addition of BioMEA reinforcement led to a significant increase in hardness and tensile strength values, with the highest values observed at 15 wt.% reinforcement. Compression tests demonstrated a significant increase in compressive strength and deformation capability of the bio-composites with the highest values observed at 15 wt.% BioMEA addition. The highest toughness of 7.68 kJ/m2 was measured in 10 wt.% MEA-reinforced bio-composites. The produced bio-composite materials have an elastic modulus between 3.5–5.5 GPa, which may provide a solution to the stress shielding problems caused by the high elastic modulus of metallic implant materials. The most severe degradation occurred in 15 wt.% MEA-reinforced bio-composites, and the effect of degradation caused a decrease in Ca and an increase in Ti-Ni-Zr-Mo in all bio-composites. These findings suggest that HA/BioMEA bio-composites have the potential to be developed as advanced biomaterials with moderate mechanical and biological properties for load-bearing implant applications.

  • 
  AtıfScopus2·WoS1·OpenAlex3

  İncele
• MakaleYayıncıda açık erişim2024Scopus SJRQ2/r/munzur/2202
  Selenium Inhibitor Coating on NiTi Shape Memory Alloys by Using Thermal Evaporation System

  Kök, Mediha; Kanca, Muhammed Sait; Say, Yakup; Saydam, Sinan; Dağdelen, Fethi; Qader, Ibrahim Nazem

  NiTi-based memory alloys are often used as intracorporeal implant materials because of their superelasticity and shape memory properties. However, over time, the release of nickel from the NiTi alloy into the body becomes unfavorable; therefore, studies should be conducted to reduce the negative impact of nickel leakage. In this study, the biocompatible selenium element was used to coat NiTi alloys with different thicknesses. The coating process was performed using the thermal evaporation technique. Scanning electron microscopy-Energy Dispersive X-ray Analysis measurements revealed that the surfaces of the samples were well covered. Also, the atomic force microscope device determined the surface roughness of the alloys. The roughness of the surface increased after the coating process. The Tafel test was accomplished to determine the biocompatibility of the coated and uncoated alloys in an artificial body fluid. The corrosion test reveals that Se-coated NiTi alloys have high corrosion resistance.

  İncele
• MakaleYalnız künye2024Scopus SJRQ2/r/munzur/2128
  Recycling Ti1.0Nb0.3Ta0.07Zr0.05 Conventional Alloys: Production of Non-equimolar TiZrCrNb0.3Ta0.07 Medium Entropy Alloys with the Addition of Cr for Improved In Vitro Corrosion Resistance

  Guler, Omer; Say, Yakup; Dikici, Burak; Ozkul, Iskender; Niinomi, Mitsuo

  A non-equimolar TiZrCrNb0.3Ta0.07 medium entropy alloy (MEA) was successfully designed as theoretical and produced by arc-melting method from Ti1.0Nb0.3Ta0.07Zr0.05 (TNTZ) scraps for possible usage in biomedical applications in this study. The main aim of this study is to find an alternative way to recycle with a reduced carbon footprint the available TNTZ conventional alloy and convert it to a value-added product during this recycling such as medium entropy alloys (MEAs) via using less energy. To examine the microstructural changes induced by the annealing process, scanning electron microscopy was employed. The chemical composition of the HEAs was assessed using energy-dispersive spectroscopy and x-ray photoelectron spectroscopy. Additionally, x-ray diffraction analysis was used to determine the crystallographic structure and phase composition of HEAs. Furthermore, in order to evaluate the electrochemical corrosion performance of the alloys, comprehensive in vitro corrosion tests were conducted in a simulated body fluid solution, specifically Hanks's Balanced Salt Solution. Some elemental segregation has been observed after the annealing process. A big migration of Zr and Cr elements was observed in the samples from the interdendritic region to the dendritic area during the annealing process. This segregation resulted in approximately 1.4 times increase in the hardness of the MEA. The electrochemical corrosion results showed that the in vitro resistance of the MEAs was higher than that of its conventional scraps.

  • 
  AtıfScopus5·OpenAlex5

  İncele
• MakaleYayıncıda açık erişim2024Scopus SJRQ1/r/munzur/1865
  Investigation of in-vitro bioactivity, electrochemical corrosion, wettability and adhesion properties of bioglass-based coatings modified with Y2O3 and Zr on novel β-type Ti-30Zr-5Mo alloys

  Dikici, B.; Say, Y.; Zhao, X.; Niinomi, M.; Szechyńska-Hebda, M.

  In this study, the in-vitro bioactivity, electrochemical corrosion resistance, wettability, and adhesion properties of bioglass-based coatings modified with Y2O3 and ZrO2 on Ti-30Zr-5Mo alloy were investigated. The coatings were prepared using the sol-gel method and applied to the alloy substrates through dip-coating. The surface morphology and elemental composition of the coatings were analyzed using SEM/EDS and XRD techniques. Potentiodynamic polarization (PDS) and electrochemical impedance spectroscopy (EIS) were employed to assess the electrochemical behavior of the coatings under in-vitro conditions. Contact angle measurements were conducted to evaluate the wettability of the surfaces. Adhesion strength was measured using tensile testing in accordance with ISO 13779-2 standards. Bioactivity tests were performed by immersing the samples in simulated body fluid (SBF). The results demonstrate that the addition of Y2O3 and ZrO2 improves adhesion strength and corrosion potential, but introducing localized galvanic effects that increase the corrosion current density. Besides, the coatings maintained their structural integrity after the bioactivity tests, and promoted new apatite formation.