- MakaleAçık Erişim2023Scopus SJRQ3WEAR AND ADHESION PROPERTIES OF MULTILAYER Ti/TiN, (/TiC)/ TiCN/ TaN THIN FILMS DEPOSITED ON Ti13Nb13Zr ALLOY BY CLOSED FIELD UNBALANCED MAGNETRON SPUTTERING
Aslan, Ali Kemal; Bahçe, Erkan
Ti13Nb13Zr alloy stands out as an alternative to Ti6Al4V alloy for orthopaedic joint implant applications due to its low modulus of elasticity, high mechanical properties, high corrosion resistance, high biocompatibility and low modulus of elasticity, as well as con-taining no cytotoxic elements. In this study, Ti13Nb13Zr alloy was coated with TiN/TiC/TiCN/TaN multilayer thin films by pulsed-dc CFBUMS method to increase wear resistance and improve surface properties. Characterization of the deposited films were con-ducted by XRD, SEM, AFM, pin-on-disk, progressive scratch experiments. As a result, it is observed that all the coatings enhanced the tribological properties of the Ti13Nb13Zr alloy surface. The 20-layer TiN/TiC/TiCN/TaN multilayer coatings gave the best results for wear resistance and adhesion properties. Enhancing the interlayer number resulted in increased wear and adhesion resistance. In addition, it was determined that using TiC instead of TiN in the interlayers gave higher results regarding adhesion, wear, and mechanical properties.
AtıfScopus1WoS1OpenAlex1
İncele - MakaleYalnız künye2016Scopus SJRQ1Effect of hydroxyapatite/SiO2 hybride coatings on surface morphology and corrosion resistance of REX-734 alloy
Say, Yakup; Aksakal, Bunyamin; Dikici, Burak
REX-734 stainless steel alloy was coated with hydroxyapatite (HA)-silicon dioxide (SiO2) composite (hybride) coatings by using the sol-gel method. Surface morphologies, adhesion resistances and corrosion behaviors of the coatings were examined and the characterization of the coatings was performed by using XRD, SEM, and EDS. It was observed that porous and crack-free surface morphology enhanced adhesion strength of the coatings. Through the shear tests, it was found that the adhesion resistance was 25.14 MPa in HA coatings and 25.47 MPa in HA-SiO2 coatings. Corrosion analyses of the coatings were performed by using potentiodynamic polarization (PDS) tests. It was determined that corrosion dimples formed on the coating surface and the corrosion resistance in HA+SiO2 coatings increased with decreasing porosity; however, in the further steps of corrosion, it reached to the base material by causing a pitting effect on the coated surface. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
AtıfWoS36OpenAlex39İncele