- MakaleAçık Erişim2024Scopus SJRQ1Preparation of carbon dot/polyaniline composites as voltage based dielectric material for capacitor applications
Coğalmış, Fatma Tuba; Demirelli, Kadir; Barım, Esra; Ük, Nida; Ünlü, Caner; Şenkal, Bahire Filiz; Dere, Ayşegül; Tuncer, Hülya; Yakuphanoğlu, Fahrettin
Polyaniline-carbon dot (CD/PANI) composites were prepared via in-situ oxidative polymerization of aniline in the presence of carbon dots, with specific concentrations carefully controlled during synthesis. The composite was characterized using spectroscopic (FT-IR), morphological (TEM, SEM) and electrical methods. Impedance analysis was employed to investigate the transport behavior of charge carriers in the frequency range of 500 Hz to 10 MHz at 25 °C. This study provides a comprehensive analysis of the dielectric properties of the CD/PANI composite, including dielectric constant, dielectric loss, loss factor, AC conductivity, admittance, impedance, and Cole–Cole plots. The dielectric constant of the CD/PANI composite was 6.97 for 1 kHz at 0.5 V and 12.87 for 1 kHz at 5 V. The values indicate that the increase in the dielectric constant of nanocomposite with increasing voltage. This suggests that CD/PANI composite is a dielectric material whose dielectric constants are controlled by applied voltage. Notably, the dielectric constant increased with rising applied voltage and decreased with increasing frequency. Current-voltage (I-V) measurements revealed that the composite's dielectric parameters could be tuned by varying the applied DC voltage, suggesting its potential as a voltage-dependent dielectric (VDD) material for capacitor applications. Furthermore, the enhanced electrical conductivity indicates that the CD/PANI composite is a promising candidate for next-generation dielectric devices.
AtıfScopus7OpenAlex7
İncele - MakaleAçık Erişim2021Scopus SJRQ1Highly Efficient Defluoridation of Water through Reusable poly(aniline-co-o-aminophenol) Copolymer Modified Electrode Using Electrochemical Quartz Crystal Microbalance
Unal, Asuman; Hillman, A. Robert; Ryder, Karl S.; Cihangir, Salih
Although the World Health Organization (WHO) recommends a limit of 1.5 mg l-1 fluoride ions in drinking water, this is not satisfied in many parts of the world. When this limit is exceeded, the electrochemically switched ion-exchange (ESIX) technique (mainly based on conductive polymers) has been identified as a promising method for removing the excess fluoride ions. The present study aimed to develop an efficient method based on the ESIX technique by using poly(aniline-co-o-aminophenol) copolymer to extract fluoride ions. Electrochemical quartz crystal microbalance (EQCM) and acoustic admittance data were utilized to assay the synthetic efficiency of copolymer deposition, and to evaluate the dependence of the defluoridation process on the proportions of the monomers in the copolymer matrix and on film thickness. The resulting films were characterised by Fourier transform infrared spectroscopy (FTIR) and scanning electrochemical microscopy (SEM) techniques. For optimized co-monomer ratio in the feedstock, poly(aniline-co-o-aminophenol) at an applied potential of 0.30 V showed excellent performance for fluoride removal from water at pH 6.6, to the extent of 20 (mg F-) (g polymer)-1. Comparison of the performance of ESIX using poly(aniline-co-o-aminophenol) with that of other techniques and materials reveal that it has significant potential for water defluoridation.
AtıfScopus9WoS8OpenAlex10
İncele - MakaleAçık Erişim2021Scopus SJRQ1Electrogravimetric analysis of poly(aniline-co-o-toluidine) copolymer films in the presence of fluoride ions
Unal, Asuman; Robert Hillman, A.; Ryder, Karl S.; Cihangir, Salih
Polyaniline itself can be converted to its conductive form from its insulating form by applying an oxidising potential in which polyaniline is converted to its positive charge state. Anions in the target solution are driven into the positively charged polymer film by electrostatic force, and this process is reversed when a reduction potential is applied. Consequently, interfacial processes of polyaniline modified electrode make it viable to remove undesirable ions from the target solution. During this process, polyaniline operates as an ion-exchanger by directing specific ions at definite potentials, which is the principle of the electrochemically switched ion-exchange technique. Therefore, polyaniline can be employed as a convenient material to perform as a new ion-exchanger modified film in an acidic environment. On the other hand, an abrupt decrease in the electroactivity of polyaniline at elevated pH values restricts its use in such practical applications. To overcome this problem, copolymerization of aniline and o-toluidine is expedient as it will be able to enhance the electrochemical properties of polyaniline. Hence, several copolymers were synthesised in the presence of different aniline and o-toluidine feedstock ratios. It was found that the surface coverage value of a representative poly(aniline-co-o-toluidine) copolymer film was 139.7 nmol cm−2 compared with 76 nmol cm−2 for pure Pani under identical conditions. In addition, the redox cycling in monomer-free NaF solutions showed that the poly(aniline-co-o-toluidine) film exhibited excellent reversibility between redox reactions at pH 6.60. These outcomes clearly illustrate the contribution of o-toluidine to the electrochemical properties of polyaniline at raised pH medium.
AtıfScopus8WoS8OpenAlex8İncele