• MakaleAçık Erişim2024Scopus SJRQ2/r/munzur/1830
  The influence of cold rolling and hydroxyapatite coating on the mechanostructure, corrosion resistance, cell viability, and antibacterial activity of ZnCu biodegradable implants

  Aksakal, B.; Karadogan, S.A.; Aslan, N.; Fidan, F.; Yilmazer, Y.; Sezek, S.

  Zinc (Zn) and its alloys exhibit great potential for utilization in biodegradable bone implants. Zn-1Cu biodegradable alloy was produced and were cold rolled at two different deformation rates of 47 and 61%. The samples have been bioceramic coated with the sol–gel method and microstructure-mechanical property changes, corrosion behavior and biocompatibility of the samples were investigated. They were characterized by Optical, SEM, XRD and wettability analysis. The rolled samples showed a significant increase in hardness when compared to the non-rolled samples. The unrolled and 47% rolled samples showed better corrosion resistance compared to 61% rolled samples. Antibacterial effects of the base and sol–gel-coated groups showed higher cell viability ratios than the uncoated groups. Cell viability increased significantly in 47% of the rolled samples after 24, 48, and 72 h, however decreased by up to 70% in 61% of the rolled samples. Graphical abstract: (Figure presented.).

  • 
  AtıfScopus2·WoS2·OpenAlex2

  İncele
• MakaleYalnız künye2021Scopus SJRQ2/r/munzur/3080
  Effect of graphene reinforcement on hybrid bioceramic coating deposited on the produced porous Ti64 alloys

  Aslan, N.; Aksakal, B.

  Porous-Ti64 alloys (P-Ti64), produced at various porosities by hot-pressing technique with the help of Mg spacer, were coated by hybrid-Graphene Oxide (rGO) reinforced-hydroxyapatite (HAp), using the sol–gel method. The synthesized rGO powder was used in reinforcing HAp by the Modified Hummers method having 30 µm particle size and nano (nm) scale layer thickness. Hybrid coatings were executed on Ti64 substrates in four different groups as single-HAp, HAp reinforced with 0.5 wt%, 1.0 wt% and 1.5 wt% rGO for three different porosities (41, 52, and 64%) were characterized by FT-IR, Raman, XRD and SEM. The average 21 µm coating film thicknesses were obtained and desirably, the only superficial pores of the substrates were closed by coating material rather than the inner connected open pores. It was also shown that 0.5 wt% and 1.0 wt% rGO reinforcements into HAp prevented crack formation on the Ti64 surfaces, whereas 1.5 wt% rGo reinforcement and single-HAp coatings caused. The highest adhesion strength values were achieved at low porosities (41–52%) and of 0.5–1.0 wt% rGO reinforcements through the adhesion tests.

  AtıfScopus14·WoS12·OpenAlex20

  İncele