Sürdürülebilir Kalkınma Amaçları
Yazarlar
Yayınlar
- MakaleYalnız künye2024Scopus SJRQ2Synthesis and characterization of TiNbZrMo medium-entropy bio-composites: Microstructure, mechanical properties, and in vitro degradation
Say, Yakup
This study reports the synthesis and characterization of hydroxyapatite (HA)-based bio-composites reinforced with varying amounts (by weight, 1–15 wt.%) of bio-medium entropy alloy (BioMEA) for load-bearing implant applications. BioMEA powders consisting of Ti, Nb, Zr, and Mo were mechanically alloyed for 100 h and subsequently added to HA using powder metallurgy techniques. To show the effect of BioMEA, the microstructure, density, and mechanical tests have been conducted and the synthesized BioMEA was characterized by scanning electron microscope (SEM), x-ray diffractometer (XRD), and Fourier-transform infrared spectroscopy (FTIR) analysis. In addition, in vitro degradation behavior and bioactivity analyses of bio-composites have been conducted. XRD analysis revealed the formation of BioMEA after 20 h of mechanical alloying. The highest density value of 2.47 g/cm3 was found in 15 wt.% BioMEA-reinforced bio-composite. The addition of BioMEA reinforcement led to a significant increase in hardness and tensile strength values, with the highest values observed at 15 wt.% reinforcement. Compression tests demonstrated a significant increase in compressive strength and deformation capability of the bio-composites with the highest values observed at 15 wt.% BioMEA addition. The highest toughness of 7.68 kJ/m2 was measured in 10 wt.% MEA-reinforced bio-composites. The produced bio-composite materials have an elastic modulus between 3.5–5.5 GPa, which may provide a solution to the stress shielding problems caused by the high elastic modulus of metallic implant materials. The most severe degradation occurred in 15 wt.% MEA-reinforced bio-composites, and the effect of degradation caused a decrease in Ca and an increase in Ti-Ni-Zr-Mo in all bio-composites. These findings suggest that HA/BioMEA bio-composites have the potential to be developed as advanced biomaterials with moderate mechanical and biological properties for load-bearing implant applications.
AtıfScopus2WoS1OpenAlex3
İncele - MakaleYalnız künye2024Scopus SJRQ2Recycling Ti1.0Nb0.3Ta0.07Zr0.05 Conventional Alloys: Production of Non-equimolar TiZrCrNb0.3Ta0.07 Medium Entropy Alloys with the Addition of Cr for Improved In Vitro Corrosion Resistance
Guler, Omer; Say, Yakup; Dikici, Burak; Ozkul, Iskender; Niinomi, Mitsuo
A non-equimolar TiZrCrNb0.3Ta0.07 medium entropy alloy (MEA) was successfully designed as theoretical and produced by arc-melting method from Ti1.0Nb0.3Ta0.07Zr0.05 (TNTZ) scraps for possible usage in biomedical applications in this study. The main aim of this study is to find an alternative way to recycle with a reduced carbon footprint the available TNTZ conventional alloy and convert it to a value-added product during this recycling such as medium entropy alloys (MEAs) via using less energy. To examine the microstructural changes induced by the annealing process, scanning electron microscopy was employed. The chemical composition of the HEAs was assessed using energy-dispersive spectroscopy and x-ray photoelectron spectroscopy. Additionally, x-ray diffraction analysis was used to determine the crystallographic structure and phase composition of HEAs. Furthermore, in order to evaluate the electrochemical corrosion performance of the alloys, comprehensive in vitro corrosion tests were conducted in a simulated body fluid solution, specifically Hanks's Balanced Salt Solution. Some elemental segregation has been observed after the annealing process. A big migration of Zr and Cr elements was observed in the samples from the interdendritic region to the dendritic area during the annealing process. This segregation resulted in approximately 1.4 times increase in the hardness of the MEA. The electrochemical corrosion results showed that the in vitro resistance of the MEAs was higher than that of its conventional scraps.
AtıfScopus5OpenAlex5İncele