- MakaleAçık Erişim2026Scopus SJRQ4Impact of Basalt Powder on the Physical, Fresh, Hardened and Microstructural Characteristics of Granulated Blast Furnace Slag-Based Alkali-Activated Mortars
Yön, Merve Şahin; Cemalgil, Selim
In this study, the workability, mechanical and physical aspects of alkali-activated mortar (AAM) containing basalt powder (BP) and granulated blast furnace slag (GBFS) were investigated. For the experimental study, alkali-activated mortars (AAM) containing BP at 8%, 16%, 24%, 32% and 40% substitution rates for GBFS were developed. Mortars were synthesized with a sodium silicate/sodium hydroxide ratio of 3.0 for the binder materials and a 0.45 alkali activator-to-binder ratio. The flow diameters of the fresh mortars prepared using 40x40x160 mm molds were determined according to the European Federation of Experts in Construction Chemicals and Concrete Systems (EFNARC) standard. The fresh AAMs were wrapped in stretch film to prevent evaporation and then kept in an oven at 60°C for 48 hours. The cured samples were evaluated for their mechanical strengths at 3 and 28 days, freeze-thaw effects after 33 and 100 cycles, and microstructures after 100 cycles. According to the results, using 40% BP instead of GBFS caused a decrease of approximately 15.08% in 28-day compressive strength compared to the reference sample (100% GBFS). G100 showed a minimum porosity of 15.81% and a water absorption rate of approximately 7.3%. The G60B40 mixture had the highest sorptivity capacity with 5.29x10-3 cm/s0.5, while the G100 mixture showed the lowest capacity with 3.88x10-3 cm/s0.5. After 100 freeze-thaw cycles, the G60B40 sample had the largest strength loss of 61.61%, while the G100 sample showed the lowest strength loss of 9.89%.
AtıfScopus1
İncele - MakaleAçık Erişim2024Scopus SJRQ4Experimental Study on Engineering Properties of Recycled Olivine Aggregate Filled CF Reinforced Electrically Conductive Mortars
Dehghanpour, Heydar; Doğan, Fatih; Subaşı, Serkan; Maraşlı, Muhammed
Electrically conductive concretes produced for different purposes were introduced years ago and since then, intensive scientific research has been going on. Studies in the literature have generally been carried out on conventional concretes with electrical conductivity for floor applications. The current study investigates carbon fiber reinforced mortars filled with fine olivine aggregate. Fine aggregate filled mortars are generally produced for building facade applications. Within the scope of the study, the mechanical, electrical, dynamic and microstructural properties of cementitious mortars containing 0.5%, 0.75% and 1.0% carbon fiber and 100% recycled olivine aggregate were investigated. The purpose of performing dynamic resonance tests was to investigate the effect of carbon fiber on damping ratio. 28-Day compressive, flexural, dynamic resonance, ultrasonic pulse velocity (UPV), Leeb hardness and dry density tests of conductive mortar samples obtained from four different mixtures were performed. In addition, 2, 14, 28, 90 and 180 days electrical conductivity tests were carried out to determine their resistivity in different time intervals. The purpose of performing dynamic resonance tests was to investigate the effect of carbon fiber on damping ratio. While a significant positive effect of CF on electrical conductivity and damping ratio was observed, a negligible decrease in mechanical results was observed. Calcium silicate hydrate (C-S-H) structure formed by hydration using olivine filler in the cement mixture confirmed the binding formations.
AtıfOpenAlex1TR Dizin1İncele - MakaleAçık Erişim2021Mineralogical And Gemological Characteristics Of Metaophiolite Hosted Corundum (Malatya-Türkiye)
Kaydu Akbudak, İlkay; Gürbüz, Meltem; Başibüyük, Zeynel; Hatipoğlu, Murat; Öztüfekçi Önal, Ayten; İşler, Fikret
The corundum is found in the rocks of the Berit metaophiolite in Eastern Anatolia, near Doğanşehir a province of Malatya. Metaophiolitic rocks consist mainly of garnet metagabbro, granulite, amphibolite, mylonitic amphibolite, garnet amphibolite, amphibole schist, pyroxenite, mylonitic pyroxenite, orthopyroxenite, harzburgite, serpentinized dunite and diorite units. Corundum occurrences are mostly found in pyroxenites, amphibolites, peridotites and granulites. Their colors change in range between reddish pink, pink and light pink. They are usually in structure of translucent, vitreous and sometimes cracked. They are seen scattered or clustered together inside the rocks in which they are found. The size of their crystals ranges from 0.5 cm to 10 cm and their euhedral crystals are observed in pseudohexagonal form. As a result of the petrographic examinations, it was observed that pyroxene, amphibole, garnet and plagioclase minerals accompanied with the corundum. The samples of the rocks containing the corundum has qualifications which will be as an object of gemstone and ornament by means of cutting and shining. Large specimens of corundum can be processed alone. Samples, being as scattered and small granules inside the rock can be processed together with the host rock. In the processed samples, it was obtained patterns like the samples of corundum with zoisite which were in great demand in the world gemstone market.
AtıfScopus3OpenAlex4TR Dizin2İncele - MakaleAçık Erişim2020Reviewing Phlomis rigida Labill From Turkey as a Antimicrobial Efficacy
Sönmez, Pınar Erecevit; Kirbağ, Sevda; Çakilcioğlu, Uğur
This work researched the inhibitory properties of the extract of Phlomis rigida Labill plant including chloroform on gram-negative and positive bacteria, yeasts and dermatophyta; the related plant is used for therapeutic purpose in public. For the disk diffusion method, this extract is effective on Pseudomonas aeruginosa that is one of the negative bacterias by 11.33 ± 0.57 mm inhibition areas. Regarding other bacterias, the effect of the related extract is so low in avoiding the improvement of Escherichia coli, Staphylococcus aureus and Bacillus megaterium by 8.33 ± 0.57 mm inhibition area. It has highly effective on Trichopyton sp. and Candida albicans that are from dermatophytes fungis and yeast by 16.33 ± 0.57 mm inhibition area. About yeast and dermatophytes fungi it has a remarkable impact on Candida glabrata (14.33 ± 0.57 mm inhibition area), Epidermophyton sp. (12.33 ± 0.57 mm inhibition area). Antimicrobial activity of this natural extract against all the microorganisms that were tested by MIC method by concentrations vary by 100 uL and 6.25 uL. Acording to this; the results showed good inhibitory effect with 6.25 μL for C. albicans, Trichophyton sp. with 12.25 μL for C. glabrata. In the other hand it is effective with 25 μL for P. aeruginosa, Epidermophyton sp. with 50 μL for E. coli, S. aureus, B. megaterium. Being used plants for medical purposes as from since the early ages show that these plants can be used as alternatives of available antibiotics; including important medical components is the other reason for being an alternative at the same time. Concerning results, P. rigida can be utilized as a therapeutic drug for the healing of infections caused by microorganisms. In this study, we believe that the P. rigida is important in the search for new antibiotics and will contribute to the literature and the world of drug as it affects different types of microorganisms at the lowest level for the first time.