- MakaleYalnız künye2026Scopus SJRQ2Influence of Boron Addition on the Microstructure, Mechanical, and Corrosion Behavior of NiCrBSi Alloys Prepared by Spark Plasma Sintering
Çelik, Ertuğrul
This study investigates the effect of boron addition on the microstructural, mechanical, and corrosion properties of NiCrBSi alloy fabricated by the spark plasma sintering (SPS) method. Boron was added at levels of 1.5, 3, and 4.5 wt.%, and sintering was conducted at 950 °C for 5 min. Microstructural characterization was carried out using SEM–EDS and XRD analyses, hardness was measured by the Vickers method, and densities were determined according to Archimedes’ principle. The transverse rupture strength (TRS) was obtained by three-point bending tests, while wear performance was evaluated in a reciprocating wear mode. Corrosion behavior was examined through potentiodynamic polarization in a 0.1 M HCl solution. Increasing boron content promoted the formation of nickel and chromium boride phases, enhancing hardness (up to 675 HV0.5) and wear resistance but reducing TRS values due to brittle intermetallic formation. Furthermore, corrosion protection efficiency improved, reaching about 65.9% at 4.5 wt.% B addition.
- MakaleYalnız künye2024Scopus SJRQ2Activity of nanosized copper-boron alloys against Phytophthora species
Yiğit, Uğur; Türkkan, Muharrem; İlhan, Hasan; Şimşek, Tuncay; Güler, Ömer; Derviş, Sibel
This study aimed to evaluate the antifungal activity of copper-boron (Cu-B) nanoalloys against a range of Phytophthora species, including P. capsici, P. citrophthora, P. palmivora, P. cinnamomi, P. nicotianae, P. cactorum, P. plurivora, P. inundata, and P. megasperma. The nanoalloys were synthesized via mechanical alloying under an argon atmosphere, resulting in the formation of nanocrystalline Cu-B nanoalloys with irregular morphology and particle sizes ranging from 50 to 240 nm. At a concentration of 250 µg mL−1, the Cu-B nanoalloys demonstrated complete inhibition of mycelial growth, sporangium production, and zoospore germination in all tested Phytophthora species. The EC50 values for mycelial growth ranged from 28.02 to 120.17 µg mL−1, while for sporangium production and zoospore germination, they were below 10 µg mL−1. Furthermore, the nanoalloys exhibited fungicidal activity against specific Phytophthora species, such as P. capsici, P. citrophthora, P. inundata, and P. megasperma, at concentrations of 100, 250, 250, and 250 µg mL−1, respectively. Notably, the Cu-B nanoalloys displayed significant protective and curative effects on tuber rot severity in P. nicotianae-inoculated potatoes, resulting in reductions of 94.13% and 92.61% compared to the control, respectively, at a concentration of 10 µg mL−1 (P < 0.05). These findings highlight the potential of Cu-B nanoalloys as a promising fungicide for the management of plant diseases caused by Phytophthora spp.
AtıfScopus3WoS1OpenAlex2
İncele - MakaleAçık Erişim2023Scopus SJRQ3The effect of different boron compounds on nutrient digestibility, intestinal nutrient transporters, and liver lipid metabolism
Şahin, Emre; Orhan, Cemal; Erten, Füsun; Şahin, Fikrettin; Şahin, Nurhan; Şahin, Kazim
Background/aim: Gastrointestinal health is essential for maintaining a healthy lifestyle. Improving nutrient absorption and energy metabolism are the critical targets for intestinal health. This study aimed to determine the effects of different boron (B) derivatives on nutrient digestibility, intestinal nutrient transporters, and lipid metabolism in rats. Materials and methods: Twenty-one rats were allocated to three groups (n = 7) as follows: (i) Control, (ii) Sodium pentaborate pentahy-drate (SPP), and (iii) boric acid (BA). The rats were fed a chow diet (AIN-93M) and supplemented with 8 mg/kg elemental B from SPP (45.2 mg/kg BW) and BA (42.7 mg/kg BW) via oral gavage every other day for 12 weeks. The nutrient digestibility of rats in each group was measured using the indigestible indicator (chromium oxide, Cr2 O3, 0.20%). At the end of the experiment, animals were decapitated by cervical dislocation and jejunum, and liver samples were taken from each animal. The nutrient transporters and lipid-regulated transcription factors were determined by RT-PCR. Results: The nutrient digestibility (except for ash) was increased by SPP and BA supplementation (p < 0.05). SPP and BA-supplemented rats had higher jejunal glucose transporter 1 (GLUT1), GLUT2, GLUT5, sodium-dependent glucose transporter 1 (SGLT1), fatty acid transport protein-1 (FATP1), and FATP4 mRNA expression levels compared to nonsupplemented rats (p < 0.0001). BA-supplemented rats had remarkably higher peroxisome proliferator-activated receptor gamma (PPARγ) levels than nonsupplemented rats (p < 0.0001). In contrast, sterol regulatory element-binding protein 1c (SREBP-1c), liver X receptor alpha (LxR-α), and fatty acid synthase (FAS) levels decreased by SPP supplementation compared to other groups (p < 0.05). Conclusion: SPP and BA administration enhanced nutrient digestibility, intestinal nutrient transporters, and liver lipid metabolism in rats.
AtıfScopus8WoS7OpenAlex9TR Dizin1
İncele - MakaleYalnız künye2022Scopus SJRQ3Boron-incorporated biocomposite coatings on 316L and NiTi alloys: Enhanced structural, antibacterial activity, and cell viability performances
Aslan, N.; Aksakal, B.; Aksoy, M.E.
Boron doped (5 %, 10%, and 15 wt.%) Hydroxyapatite (B-HA) biocomposites were syntesized and coated on 316L SS and NiTi (Ni-45Ti) metallic substrates by using the electrophoretic deposition process (EPD). The morphological and structural characterization of the coatings was executed using scanning electron microscopy (SEM) and X-ray diffraction devices (XRD). Antibacterial tests were conducted using Escherichia coli (E. coli, JM103) and Staphylococcus aureus (S. aureus, ATCC29293) microorganisms. The mitochondrial activity assay (MTT)-[3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide] was used to examine cell viability and cytotoxicity in Saos-2 osteoblast cells. HA and boron peaks, as well as B-TCP and metallic components, were detected in XRD examinations. Porous morphologies were generated on the surface with boron doped B-HA coatings, as revealed by SEM views. Antibacterial activity studies revealed that both metallic coating groups, notably with boron doping, demonstrated antibacterial activity against gram-negative E. coli and gram-positive S. aureus. The antibacterial activity of the 316L group was shown to be better than that of the NiTi group in comparisonal testing. The syntesized boron-doped biocomposite coatings did not have any detrimental effects on living cells, according to cell viability studies. The cell viability rate was found to be greater in NiTi coatings than in 316 SS coatings, and the impact was amplified by the addition of boron.
AtıfScopus6WoS4OpenAlex7İncele - MakaleYalnız künye2021Scopus SJRQ3Enhanced Adhesion and Corrosion Properties of Boron Doped Bioceramic Coated 316L Implants
Aksoy, M.E.; Aksakal, B.; Aslan, N.; Dikici, B.
Abstract: In order to provide an effective prevention to 316L implants, a synthesized bioceramic was coated by using electrophoretic deposition (EPD). The effect of boron addition into hydroxyapatite (HA) on surface morphology, adhesion and corrosion resistance of the implant has been examined. Boron doped HA (B–HA) was synthesized by a simple chemical acid-base method with 5, 10, and 15 wt % boron additions to coat on 316L implants. The synthesized B-HA was coated on the substrates and the coated surfaces with and without B additions. Sintering took place at different temperatures and sintering rates. The coatings were characterized by X-ray diffractometer (XRD), Fourier transform infrared spectroscopy (FT–IR) and scanning electron microscope (SEM). Furthermore, adhesion and in vitro corrosion tests were conducted. The influence of boron additons on adhesion and corrosion resistance of 316L have been revealed for the coated substrates at different B additions. It was shown that boron addition increased the adhesion and corrosion resistance of the bioceramic coatings. Furthermore, the sintering effect on adhesion was also evaluated and the highest adhesion as 25.8 MPa has been reached at 750°C for 90 s and 5°C min–1 sintering conditions. It was found that using iodine as EPD dispersant has increased the charging ability of the B–HA powders in the suspension and hence eased deposition rate. The study revealed that boron-containing hydroxyapatite coatings can provide crack-free surfaces that providing high adhesion and hence increase the corrosion resistance of metallic implants. Through the results, it was also shown that the network between powders was improved and hence adhesion was increased with increasing B addition.
AtıfScopus10WoS9OpenAlex12İncele - MakaleYalnız künye2021Scopus SJRQ2Boron-Doped Hydroxyapatite Coatings on NiTi Alloys Using the Electrophoretic Deposition Method: Enhanced Corrosion and Adhesion Performances
Aksoy, M.E.; Aksakal, B.; Aslan, N.; Dikici, B.
Metallic implants are functionalized with coatings due to the need to protect against biological corrosion in the body. Hydroxyapatite (HAp) has desirable biocompatibility and structural properties, but poor mechanical properties limit its use as a standalone coating. In this study, boron-doped hydroxyapatite (B-HAp) biocomposites containing 5, 10, and 15% boron by weight were synthesized by the sol-gel method and applied as a coating to NiTi using electrophoretic deposition (EPD). The deposition was carried out for 60, 90, and 120 s, and sintering at 750 °C for 75 minutes under vacuum. The coated substrates were then characterized by XRD, SEM, and FT-IR, and their adhesion strengths and in-vitro corrosion behaviors in simulated body fluid were compared with uncoated samples. The results showed that the microporous powders formed well-bonded structures, which positively affect adhesion strength. The highest adhesion strength (30 MPa) and corrosion resistance were achieved with 15 wt.% B-HAP coating at 120 s deposition time and 76.5 μm coating thickness.
AtıfScopus18WoS16OpenAlex19İncele - MakaleYalnız künye2020Scopus SJRQ2The Effects of Boron Minerals on the Microstructure and Abrasion Resistance of Babbitt Metal (Sn–Sb–Cu) Used as Coating Materials in Hydroelectric Power Plants
Tasgin, Yahya
In this study, the microstructure of a new alloy is examined which is created by adding boron oxide (B2O3), boric acid (H3BO3) and kolamanit (Ca2B6O11·5H2O) in certain proportions to the white metals (Sn–Sb–Cu) used in the carrier bearing dies of vertical Francis turbines in hydroelectric power plants. The Babbitt materials were coated with electric arc spray coating method before. Also it is examined that whether the coating material produced as a new alloy is appropriate for applying to die surface. Utility of the new white metal material in carrier bearing dies in hydroelectric power plants has been investigated based on the metallographic structure and wear of the new alloy. While some of the boron elements added to the Babbitt metal have positive results in terms of metallographic and abrasion values, some of the boron elements have negative effects.
AtıfScopus13OpenAlex14İncele